Fragrance cellulose and method for preparing multi-colour cellulose plate by applying fragrance cellulose

A scented cellulose and cellulose technology, which is applied in the field of cellulose boards, can solve the problems of single color of cellulose boards, short fragrance persistence, and poor compatibility of cellulose, and achieve good air permeability, strong fragrance persistence, and relatively good capacitive effect

Active Publication Date: 2013-12-11
东莞冠狄塑胶有限公司
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] But the compatibility of flavoring agent and cellulose of existing cellulose board material is relatively poor, after using for a period of time, fragrance is completely dissipated, causes the persistence of fragrance to be shorter, and existing cellulose board material color is single in addition, can't satisfy people. requirements

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] A method for preparing multi-colored cellulose plates using scented cellulose, comprising the steps of:

[0045] a. Put 60 parts of cellulose acetate and 20 parts of diethyl phthalate into a high-speed mixer and mix for 20 hours to prepare mixture I;

[0046] b. Add 0.01 part of lily flavoring agent to mixture I, mix and stir evenly, and let it stand for 20 hours to prepare mixture II;

[0047] c. Put part of the mixture II into a twin-screw extruder for melt extrusion, the extrusion temperature is 165°C, the extrusion speed is 20r / min, cool to 30°C and then pelletize to obtain colorless and flavorful cellulose;

[0048] d. Put part of the mixture II into a twin-screw extruder for melt extrusion, and add 1 part of Lithor red pigment powder during the melt extrusion process, cool to 30~40°C and then cut into pellets to obtain colored and fragrant fibers white;

[0049] e. Mix the prepared colorless flavor cellulose and colored flavor cellulose into a hot press, and put...

Embodiment 2

[0052] A method for preparing multi-colored cellulose plates using scented cellulose, comprising the steps of:

[0053] a. Put 70 parts of cellulose acetate propionate and 25 parts of glyceryl diacetate into a high-speed mixer and mix for 21 hours to prepare mixture I;

[0054]b. Add 0.03 parts of rose flavoring agent to mixture I, mix and stir evenly, and let it stand for 21 hours to prepare mixture II;

[0055] c. Put part of the mixture II into a twin-screw extruder to melt and extrude, the extrusion temperature is 170°C, the extrusion speed is 22r / min, cool to 35°C and then pelletize to obtain colorless and flavorful cellulose;

[0056] d. Put part of the mixture II into a twin-screw extruder for melt extrusion, and add 1.5 parts of permanent orange pigment powder during the melt extrusion process, cool to 30~40°C and cut into pellets to obtain colored and fragrant cellulose ;

[0057] e. Mix the prepared colorless flavor cellulose and colored flavor cellulose into a hot...

Embodiment 3

[0060] A method for preparing multi-colored cellulose plates using scented cellulose, comprising the steps of:

[0061] a. Put 75 parts of cellulose acetate butyrate and 30 parts of glyceryl triacetate into a high-speed mixer and mix for 22 hours to prepare mixture I;

[0062] b. Add 0.04 parts of lavender flavoring agent to mixture I, mix and stir evenly, and let it stand for 22 hours to prepare mixture II;

[0063] c. Put part of the mixture II into a twin-screw extruder for melt extrusion, the extrusion temperature is 175°C, the extrusion speed is 24r / min, cool to 40°C and then pelletize to obtain colorless flavor cellulose;

[0064] d. Put part of the mixture II into a twin-screw extruder for melt extrusion, and add 2 parts of benzidine yellow pigment powder during the melt extrusion process, cool to 30~40°C and cut into pellets to obtain colored and fragrant cellulose ;

[0065] e. Mix the prepared colorless flavor cellulose and colored flavor cellulose into a hot press...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
densityaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to view more

Abstract

The invention relates to the technical field of cellulose plates, and in particular to a fragrance cellulose and a method for preparing a multi-colour cellulose plate by applying the fragrance cellulose. The fragrance cellulose is composed of the following raw materials in the following parts by weight: 60-100 parts of cellulose, 20-50 parts of a plasticizer, 0-3 parts of pigment powder and 0.01-0.1 parts of a flavouring agent. According to the method disclosed by the invention, the plasticizer added in cellulose is conducive to migratinge the flavouring agent in cellulose, the persistence of fragrance can be remarkably enhanced without the need of adding other compatilizerscompatilizers, the prepared cellulose is high in fragrance intensity and strong in fragrance persistence, and the problem of short fragrance persistence time of the existing cellulose is solved; the prepared multi-colour cellulose plate is high in elasticity, good in air permeability, without free from electrostatic adsorption, non-toxic, non-allergic in case of being contacted with the skin for a long time, great in liquid transmission property, excellent in adsorbability, capable of being dry-cleaned or water-washed, capable of being applied to preparinge various products such as tool handles, hairpins and the like, and wide in application range; and the method for preparing the multi-colour cellulose plate disclosed by the invention is simple in process and low in production cost.

Description

technical field [0001] The invention relates to the technical field of cellulose plates, in particular to a scented cellulose and a method for preparing multi-color plates using the same. Background technique [0002] Cellulose is the oldest and most abundant natural polymer on the earth. It is inexhaustible and the most precious natural renewable resource for human beings. The cellulose sheet made of it has low thermal conductivity and can be produced flexibly. , a variety of visual effects, excellent fluidity, good surface gloss, good electrical insulation, anti-static, self-brightness, high transparency, strong pressure resistance, unique surface vision, has been widely used in tool handles, hair clips, Toys, goggles, helmets, glasses frames, toothbrushes, tableware handles, combs and photo negatives, etc., as people's requirements for cellulose products continue to increase, people add flavoring agents to them, so that the prepared cellulose can Exudes a pleasant or app...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L1/12C08L1/14C08K5/12C08K5/103C08K5/11B29C47/92B29C48/92
CPCB29C48/0022B29C48/07B29C48/40
Inventor 黄炳坚
Owner 东莞冠狄塑胶有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap