Flavored cellulose and method for preparing multicolor cellulose sheet using the same

A scented cellulose and cellulose technology, applied in the field of cellulose plates, can solve the problems of poor cellulose compatibility, short fragrance persistence, and single color of cellulose plates, and achieve good compatibility, strong fragrance persistence, Good air permeability

Active Publication Date: 2015-12-23
东莞冠狄塑胶有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] But the compatibility of flavoring agent and cellulose of existing cellulose board material is relatively poor, after using for a period of time, fragrance is completely dissipated, causes the persistence of fragrance to be shorter, and existing cellulose board material color is single in addition, can't satisfy people. requirements

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] A method for preparing multi-colored cellulose plates using scented cellulose, comprising the steps of:

[0045] a. Put 60 parts of cellulose acetate and 20 parts of diethyl phthalate into a high-speed mixer and mix for 20 hours to prepare mixture I;

[0046] b. Add 0.01 part of lily flavoring agent to mixture I, mix and stir evenly, and let it stand for 20 hours to prepare mixture II;

[0047] c. Put part of the mixture II into a twin-screw extruder for melt extrusion, the extrusion temperature is 165°C, the extrusion speed is 20r / min, cool to 30°C and then pelletize to obtain colorless flavor cellulose;

[0048] d. Put part of the mixture II into a twin-screw extruder for melt extrusion, and add 1 part of Lithor red pigment powder during the melt extrusion process, cool to 30~40°C and cut into pellets to obtain colored and fragrant fibers white;

[0049] e. Mix the obtained colorless and flavored cellulose with colored and flavored cellulose and put them into a hot ...

Embodiment 2

[0052] A method for preparing multi-colored cellulose plates using scented cellulose, comprising the steps of:

[0053] a. Put 70 parts of cellulose acetate propionate and 25 parts of glyceryl diacetate into a high-speed mixer and mix for 21 hours to prepare mixture I;

[0054] b. Add 0.03 parts of rose flavoring agent to mixture I, mix and stir evenly, and let it stand for 21 hours to prepare mixture II;

[0055]c. Put part of the mixture II into a twin-screw extruder for melt extrusion, the extrusion temperature is 170°C, the extrusion speed is 22r / min, and after cooling to 35°C, it is pelletized to obtain colorless and flavorful cellulose;

[0056] d. Put part of the mixture II into a twin-screw extruder for melt extrusion, and add 1.5 parts of permanent orange pigment powder during the melt extrusion process, cool to 30~40°C and cut into pellets to obtain colored and fragrant cellulose ;

[0057] e. Mix the obtained colorless and flavored cellulose with colored and flavo...

Embodiment 3

[0060] A method for preparing multi-colored cellulose plates using scented cellulose, comprising the steps of:

[0061] a. Put 75 parts of cellulose acetate butyrate and 30 parts of glyceryl triacetate into a high-speed mixer and mix for 22 hours to prepare mixture I;

[0062] b. Add 0.04 parts of lavender flavoring agent to mixture I, mix and stir evenly, and let it stand for 22 hours to prepare mixture II;

[0063] c. Put part of the mixture II into a twin-screw extruder for melt extrusion, the extrusion temperature is 175°C, the extrusion speed is 24r / min, cool to 40°C and then pelletize to obtain colorless flavor cellulose;

[0064] d. Put part of the mixture II into a twin-screw extruder for melt extrusion, and add 2 parts of benzidine yellow pigment powder during the melt extrusion process, cool to 30~40°C and cut into pellets to obtain colored and fragrant cellulose ;

[0065] e. Mix the obtained colorless and flavored cellulose with colored and flavored cellulose and...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
densityaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to a scented cellulose and a method for preparing multi-colored cellulose plates using the scented cellulose. The scented cellulose is composed of the following raw materials: 60-100 parts of cellulose, 20-50 parts of plasticizer, 0-3 parts of pigment powder, Fragrance agent 0.01~0.1 part, the plasticizer that the present invention adds in cellulose helps flavor agent migrate in cellulose, does not need to add other compatibilizer and can significantly strengthen the persistence of fragrance, the fiber that makes The plain fragrance has high strength and strong fragrance persistence, which solves the problem of short duration of the existing cellulose fragrance. The multi-color cellulose sheet has high elasticity, good air permeability, no electrostatic adsorption, non-toxic, long-term and It is not allergic to skin contact, has good liquid penetration and excellent adsorption, can be dry-cleaned or washed, and can be used to make tool handles, hair clips and other products, with a wide range of applications. The multi-color cellulose prepared by the present invention The plate method has simple process and low production cost.

Description

technical field [0001] The invention relates to the technical field of cellulose plates, in particular to a scented cellulose and a method for preparing multi-color plates using the same. Background technique [0002] Cellulose is the oldest and most abundant natural polymer on the earth. It is inexhaustible and the most precious natural renewable resource for human beings. The cellulose sheet made of it has low thermal conductivity and can be produced flexibly. , a variety of visual effects, excellent fluidity, good surface gloss, good electrical insulation, anti-static, self-brightness, high transparency, strong pressure resistance, unique surface vision, has been widely used in tool handles, hair clips, Toys, goggles, helmets, glasses frames, toothbrushes, tableware handles, combs and photo negatives, etc., as people's requirements for cellulose products continue to increase, people add flavoring agents to them, so that the prepared cellulose can Exudes a pleasant or app...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L1/12C08L1/14C08K5/12C08K5/103C08K5/11B29C47/92B29C48/92
CPCB29C48/0022B29C48/07B29C48/40
Inventor 黄炳坚
Owner 东莞冠狄塑胶有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com