Preparation method of optical composite nano-fiber material

A composite nanofiber and optical technology, applied in luminescent materials, chemical instruments and methods, fiber treatment, etc., can solve problems such as poor electrical conductivity and unsatisfactory immobilization capacity

Active Publication Date: 2015-05-06
SOUTHEAST UNIV
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the conductivity of Nafion nanofibers is poor
The above two methods for Ru(bpy) 3 2+ The loading capacity is not ideal

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of optical composite nano-fiber material
  • Preparation method of optical composite nano-fiber material
  • Preparation method of optical composite nano-fiber material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0039] Transmission electron microscopy (TEM) of Au-MCNTs ( figure 1 ), it can be seen that the gold nanoparticles are uniformly arranged along the outer wall of the MCNT, and the diameter of the gold nanoparticles is about 12 nm, spherical and very uniform. Au-MCNTs do not agglomerate or change color even when placed in the dark for several months.

[0040] By PA6-Au-MCNT-Ru(bpy) 3 2+ Field emission scanning electron microscopy (FESEM) patterns of optical composite nanofibers ( figure 2 ), it can be seen that PA6-Au-MCNT-Ru(bpy) 3 2+ The optical composite nanofibers are randomly oriented to form a nanofiber membrane with a porous 3D structure. The nanofiber surface is smooth and non-obtrusive, and the diameter ranges from 50nm to 300nm.

[0041] image 3 Cyclic voltammetry (CV) and electrochemiluminescence (ECL) scanning were applied to PA6-Au-MCNT-Ru(bpy) 3 2+ Optical composite nanofibers were characterized. In the CV curve, there is an obvious oxidation peak at +1...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a preparation method of an optical composite nano-fiber material. The method comprises the steps of 1) preparing a nano gold-multi-wall carbon nano tube compound Au-MCNT; 2) preparing a spinning solution; 3) preparing the optical composite nano-fiber material in an electrostatic spinning way. In the electrostatic spinning, the prepared uniform and transparent precursor electrostatic spinning solution is arranged in an injector, a positive electrode of a high-voltage electrostatic generator is connected with a needle, a negative electrode is connected onto a clean bare electrode, the liquid is supplied by adopting a trace injection pump and directly applied to the injector needle through the high-voltage electrostatic power generated by the high-voltage electrostatic generator, and the optical composite nano-fiber is collected onto the bare electrode. The nano gold-multi-wall carbon nano tube compound with good conductivity and large specific surface area and capable of stably and firmly loading a great amount of trisruthenium Ru(bpy)3<2+> is doped with the spinnable macromolecular nylon 6 with good stability to obtain the precursor electrostatic spinning solution, and the optical composite nano fiber is obtained through the one-step electrostatic spinning method.

Description

technical field [0001] The invention discloses an optical composite nanofiber material and a preparation method thereof. The optical composite nanofiber material has simple process, convenient operation, wide source of raw materials, low cost and high yield; the superior optoelectronic properties of ruthenium bipyridine are maintained, and at the same time, it has high luminous efficiency, fast electron transfer rate, good stability, Ruthenium bipyridine does not leak and other characteristics. It is a new optoelectronic material and also provides an effective method for immobilizing electrochemiluminescent actives. It belongs to the field of photoelectric material manufacturing. Background technique [0002] With the need for device miniaturization and the development of molecular devices, molecular materials based on nanometer and submicrometer scales have attracted much attention in the past decade. One-dimensional nanostructures have intrinsic anisotropy, which is ben...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D01F6/90D01F1/09D01F1/10C09K11/06D01D5/00
Inventor 王晓英
Owner SOUTHEAST UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com