Refining technology for molten medium-high carbon steel

A medium-high carbon and molten steel technology, applied in the field of steel smelting, can solve problems such as difficulty in cleaning, increased viscosity of slag, inclusions, etc.

Active Publication Date: 2013-12-25
PANGANG GRP PANZHIHUA STEEL & VANADIUM
View PDF3 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Deoxidation of molten steel by aluminum deoxidizer leads to Al in steel slag 2 o 3 With the increase of the content, the viscosity of the slag increases, which makes the slag stick to the insertion pipe of the RH cycle vacuum degassing equipment and is difficult to clean, which seriously affects the operation rate of the RH cycle vacuum degassing equipment
[0004] In addition, the deoxidized product Al 2 o 3 Easy to be included in molten steel, reducing the quality of steel
[0005] In addition, the molten steel is deoxidized and alloyed before RH cycle vacuum degassing, alloying and deoxidation may be carried out at the same time, so that part of the alloy is oxidized into oxides, thereby reducing the yield of the alloy
In addition, the amount of oxide inclusions that are excluded in subsequent treatments such as RH cycle vacuum degassing is limited, which reduces the quality of the steel

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0021] The refining process of medium-high carbon molten steel according to the present invention comprises the following steps: during the process of tapping molten steel from a converter to a ladle, adding the first batch of recarburizers to the molten steel so that the carbon content of the molten steel is 0.20% to 0.30%; and In the process of circular vacuum degassing treatment (RH treatment) of molten steel, the second batch of recarburizer is added to molten steel for deoxidation, and then the molten steel is alloyed so that the oxygen content, carbon content and alloy content of molten steel all reach the target value. In this specification, the percentage content mentioned may refer to the mass percentage content.

[0022] The first batch of carburizers and the second batch of carburizers may be at least one of carbon particles and pitch coke. The first batch of carburizers and the second batch of carburizers can be the same or different.

[0023] The refining proces...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A provided refining technology for molten medium-high carbon steel comprises: during the process that molten steel is subjected to tapping from a converter to a steel ladle, adding the first batch of a carburant into the molten steel to enable the carbon content of the molten steel to be 0.20%-0.30%; during cyclic vacuum degassing treatment of the molten steel, adding the second batch of the carburant into the molten steel for deoxidation; and then alloying the molten steel to enable the oxygen content, the carbon content and the alloy content of the molten steel to reach target values. The refining technology is capable of reducing viscosity of steel slag, avoiding or reducing generation of Al2O3 to improve molten steel cleanliness, improving the yielding rate of alloy elements as well as reducing metal oxide inclusions in the molten steel, and / or reducing treatment cost.

Description

technical field [0001] The invention relates to steel smelting, in particular to a refining process for medium-high carbon molten steel. Background technique [0002] Medium and high carbon steel such as rail steel is usually smelted by killed steel treatment process, specifically, carburization, deoxidation, alloying in the process of converter tapping, and then vacuum treatment, degassing, removal of some inclusions, and fine-tuning of the alloy. In the killed steel treatment process, aluminum deoxidizer is used to deoxidize molten steel, and the deoxidized product is Al 2 o 3 . For example, aluminum alloy is added to the molten steel during the tapping process of the converter to partially deoxidize the molten steel. Aluminum shot or aluminum wire may be added at the LF station, and then a certain amount of aluminum shot will be added after the molten steel enters the RH cycle vacuum degassing equipment. Final deoxidation of molten steel. [0003] Deoxidation of molte...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C21C7/00
Inventor 刘荣蒂李清春解明科
Owner PANGANG GRP PANZHIHUA STEEL & VANADIUM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com