Tempering process of medium-carbon steel large diesel engine output shaft hardening and

A diesel engine and output shaft technology, applied in the direction of manufacturing tools, furnace types, heat treatment equipment, etc., to achieve the effect of increasing safety factor, improving surface quenching hardness, and reducing quenching stress

Active Publication Date: 2015-07-08
CSSC MARINE POWER
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The conventional quenching and tempering process is not suitable for quenching and tempering heat treatment of large shaft forgings, and a new quenching and tempering process needs to be redesigned

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Tempering process of medium-carbon steel large diesel engine output shaft hardening and
  • Tempering process of medium-carbon steel large diesel engine output shaft hardening and
  • Tempering process of medium-carbon steel large diesel engine output shaft hardening and

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0018] The present invention will be further described below in conjunction with drawings and embodiments.

[0019] The cross-sectional size of the output shaft of the large diesel engine in this embodiment is about 220mm, its mass is about 1000Kg, and its material is #45 forging. like figure 1 As shown, this embodiment includes the following steps:

[0020] (1) normalizing

[0021] Put the rough-processed large diesel engine output shaft into the trolley furnace at room temperature, raise the temperature in stages, keep it at 350±20°C and 600±20°C for 1 hour, and then raise the temperature to 870±20°C for 4-4.5 hours; After the heat preservation is completed, the output shaft of the large diesel engine is hoisted out, and cooled to room temperature with a fan.

[0022] (2) three quenching

[0023] The output shaft of the large diesel engine is put into the trolley furnace again at room temperature, and the temperature is raised in stages, and the temperature is kept at 35...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a medium-carbon steel large diesel engine output shaft hardening and tempering process. The process comprises the following steps: (1) normalizing: filling an output shaft in a furnace, heating to the temperature of 350 + / -20 DEG C and 600+ / -20 DEG C in a staged way, preserving the heat, hanging out the output shaft, blowing cold air to cool the output shaft to room temperature by using a fan; (2) quenching for three times: filling the output shaft into the furnace again, heating to the temperature of 350 + / -20 DEG C, 600+ / -20 DEG C and 850+ / - 10 DEG C in a staged way; cooling by air and then cooling in a water tank, cooling by the air again and cooling by water again, and then cooling in an oil tank; (3) high-temperature tempering: tempering at the temperature of 565+ / - 10 DEG C, preserving the temperature and cooling by the air out of the furnace. By the process, the surface martensite transformation speed at the first stage of a large shaft forging is improved, and the surface quenching hardness of the large shaft forging is improved by adopting the reasonable quenching cooling mode of air cooling-water cooling-air cooling-water cooling-oil cooling. The difference between the inside temperature and the outside temperature of the large shaft forging is reduced by the air cooling adopted by the process, and the cracking tendency of the large shaft forging is effectively reduced.

Description

technical field [0001] The invention relates to a heat treatment process for a large shaft forging after rough machining, in particular to a quenching and tempering process for a large diesel engine output shaft made of medium carbon steel, and belongs to the technical field of metal heat treatment. Background technique [0002] Large-scale diesel engine output shafts generally use forged blanks. This large-scale shaft forging needs quenching and tempering treatment after rough machining to improve its comprehensive mechanical properties and meet the requirements of diesel engine output shafts under alternating stress conditions. [0003] Due to the large cross-sectional effective size and mass of such large shaft forgings, according to the "size effect" and "mass effect" of the heat treatment process, the conventional quenching and tempering process is prone to the relatively large surface hardening depth of such large shaft forgings. Shallow, large residual tensile stress ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C21D1/25C21D9/28
Inventor 朱松东徐飞庄振武连兴旺
Owner CSSC MARINE POWER
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com