Thermal-insulation waterproof building material

A waterproof material and construction technology, which is applied in the field of building heat insulation and waterproof materials, can solve the problems of low strength and weak self-protection, and achieve the effects of good anti-aging performance, good waterproof effect, and strong tensile strength

Inactive Publication Date: 2014-03-26
QINGDAO UWELL INFORMATION TECH
View PDF0 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Its disadvantage is that its strength is not

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0014] Below in conjunction with specific embodiment the present invention is described in further detail;

[0015] A building heat insulation and waterproof material, which consists of the following components by weight:

[0016] Triethanolamine 5-10;

[0017] Scaly aluminum flakes 4~8;

[0018] Talc powder 10-12;

[0019] Expanded perlite 20-30;

[0020] Tourmaline powder 10~15;

[0021] Sodium silicate 3~5;

[0022] Titanium dioxide 5~10;

[0023] Deionized water 10-15.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a thermal-insulation waterproof building material which comprises the following components in parts by weight: 5-10 parts of triethavolamine, 4-8 parts of scaly sheet aluminum, 10-12 parts of talcum powder, 20-30 parts of expanded pearlite, 10-15 parts of tourmaline powder, 3-5 parts of sodium silicate, 5-10 parts of titanium dioxide and 10-15 parts of deionized water. The material provided by the invention is easy to buy and prepare, low in cost, energy-saving and environment-friendly. The finished product is convenient for construction, achieves high adhesive strength, tensile resistance and good aging resistance, and has the characteristics of no cracking at low temperature and no bulking at high temperature. The material is mainly applied to waterproof construction of outdoor and indoor pools and washrooms as well as underground engineering, waterproof and damp-proof construction of maintenance engineering, and the like. The waterproof paint provided by the invention completely abandons the defects of the conventional waterproof coiled material and the traditional waterproof paint, is easy for construction, has a good waterproof effect, higher waterproof strength and self-protection force and is easy to use.

Description

technical field [0001] The invention relates to a building heat insulation and waterproof material. Background technique [0002] At present, the waterproofing of various buildings is a key issue. Commonly used waterproof materials are various types of waterproof membranes, waterproof coatings, waterproof cement, etc. Waterproof membranes are generally hot construction, mostly baked by fire, the main disadvantage is that the bonding is not comprehensive, there are seams, and some special parts, such as corners, nozzles, etc. Not easy to repair. Waterproof coatings are usually applied cold. After the waterproof coating is mixed well, it can be painted at one time. There is no joint construction and strong adhesion. Its shortcoming is that strength is not high, and self-protection is not strong. Contents of the invention [0003] Aiming at the deficiencies in the prior art, the technical problem to be solved by the present invention is to provide a building heat insu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B24/12C04B22/04C04B14/18
Inventor 张涛
Owner QINGDAO UWELL INFORMATION TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap