Leaching process of vanadium-containing tailings clinker

A technology for vanadium tailings and clinker, which is applied in the field of leaching of vanadium-containing tailings and clinker, can solve the problems of increased production cost, long water soaking time, high water content and soluble vanadium content, and achieves improved leaching efficiency and improved recovery. Effectiveness of utilization efficiency, reduced particle size requirements

Active Publication Date: 2016-07-06
PANZHIHUA ZHUYU VANADIUM TITANIUM
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This results in that part of the tailings clinker that has been roasted into balls needs to be screened out, returned to the ball mill for crushing, and then roasted again, which increases production costs to a certain extent. The screened tailings clinker accounts for about 10% of
The clinker leaching process in the prior art has the following disadvantages: intermittent operation, long soaking time in water, high residual moisture and soluble vanadium content in the spoil (tailing residue after vacuum filtration)

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Leaching process of vanadium-containing tailings clinker
  • Leaching process of vanadium-containing tailings clinker

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1 5

[0024] Embodiments one to five are specifically implemented in the following manner:

[0025] a. Ball milling: the vanadium-containing tailings clinker after sodium roasting is subjected to wet ball milling to obtain a mixture of vanadium-containing tailings clinker and water, and the wet ball mill controls 70% to 90% of the vanadium-containing tailings clinker particle size to pass through a 120 mesh sieve;

[0026] b. The mixture obtained in step a is vacuum filtered to obtain a solution and a waste residue.

[0027] The data obtained in the above manner are shown in Table 1.

[0028] Table 1

[0029]

[0030] According to the prior art, the comparative data obtained by washing and soaking the vanadium-containing tailings clinker with tank trucks and vacuum filtration are shown in Table 2.

[0031] Table 2

[0032]

[0033] Contrast table 1 and table 2 data and can find that the present invention compares the soluble vanadium content in moisture in the obtained spoi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a leaching technology for tailings clinker containing vanadium and belongs to the technical field of extraction of vanadium from vanadium slag. The invention aims to provide a vanadium-extraction leaching technology for tailings clinker containing vanadium, which can achieve continuous production and has high leaching efficiency. The invention adopts the technical scheme as follows: a, ball milling is performed, that is, after being subjected to sodium salt roasting, the tailings clinker containing vanadium is subjected to wet ball milling to obtain a mixture of the tailings clinker containing vanadium and water, wherein the wet ball milling controls the particle size to achieve the effect that 70%-90% of the tailings clinker containing vanadium can pass through a 120-mesh sieve; b, the mixture is filtered in vacuum to obtain a solution and waste slag. The leaching technology provided by the invention can replace a tank car leaching technology in the original extraction technology of vanadium from tailings, achieve continuous production operation, shorten the leaching time of the tailings clinker and reduce the production cost.

Description

technical field [0001] The invention belongs to the technical field of vanadium extraction from vanadium slag, and in particular relates to a process for leaching vanadium-containing tailing slag clinker. Background technique [0002] Iron and steel plants will get a lot of high V 2 o 5 content of vanadium slag. Vanadium slag will be V 2 o 5 The vanadium-containing tailings with relatively low content are directly called tailings. Tailings usually contain 1.6-2.5% V 2 o 5 , 0.8-2.5% MFe, 15.0-20.0% H 2 O, the rest is SiO 2 , CaO, MgO, MnO, Cr 2 o 3 and other impurities, its particle size is usually 45-60% under the 120 mesh sieve. Tailings are mainly used for roasting to extract vanadium, and the remaining vanadium is recycled to produce vanadium pentoxide. [0003] In the prior art, the process of extracting vanadium from tailings mainly includes 5 processes of raw material pretreatment, sodium roasting, clinker leaching, vanadium precipitation and melting, and ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C22B1/02C22B7/00C22B34/22
CPCY02P10/20
Inventor 庞泽光谢德富刘东鸣饶文冬
Owner PANZHIHUA ZHUYU VANADIUM TITANIUM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products