Method for manufacturing bottle piece spinning return material recycled polyester moisture-absorbing sweat-releasing POY filament

A technology of regenerated polyester and moisture absorption and perspiration, which is applied in the melting of filament raw materials, the complete set of equipment for the production of artificial threads, and the melt spinning method. Excellent sweat function

Inactive Publication Date: 2014-03-26
仪征市仲兴环保科技有限公司
View PDF0 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In the prior art, there is no report on the regenerated polyester moistur

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0021] Example 1

[0022] A method for preparing recycled polyester moisture wicking polyester POY filaments spun from a piece of cardboard, comprising the following steps:

[0023] Step 1. Pre-crystallize the material, the material is a PET bottle sheet; specifically, dry hot air is used for pre-crystallization; when the material is pre-crystallized, the pre-crystallization temperature is 168°C, and the temperature of the dry hot air is 172°C , The air dew point is -60℃, the material moisture content is 50ppm, and the drying time is 8 hours.

[0024] Step 2. Screw feeding of the material: First, feed the dried PET bottle back into the screw extruder; when feeding the material by screw, the material is PET (polyethylene terephthalate) 甁片回料.

[0025] Step 3. Filter, homopolymerize, pressurize, filter, homopolymerize, and pressurize the melt extruded by the extruder to ensure the continuous production of spinning and the constant melt pressure; the pre-filter pressure during filtration ...

Example Embodiment

[0027] Example 2

[0028] A method for preparing recycled polyester moisture wicking polyester POY filaments spun from a piece of cardboard, comprising the following steps:

[0029] Step 1. Pre-crystallize the material, the material is PET bottle sheet; specifically, dry hot air is used for pre-crystallization; when the material is pre-crystallized, the pre-crystallization temperature is 172°C, and the temperature of dry hot air is 174°C , The air dew point is -59℃, the material moisture content is 50ppm, and the drying time is 6 hours.

[0030] Step 2. Screw feeding of the material: the hot-air dried PET bottle is fed back into the screw extruder; when the material is fed by screw, the material is PET (polyethylene terephthalate) bottle Piece back material.

[0031] Step 3. Filter, homopolymerize, pressurize, filter, homopolymerize, and pressurize the melt extruded by the extruder to ensure continuous spinning production and constant melt pressure; the front pressure during filt...

Example Embodiment

[0033] Example 3

[0034] A method for preparing recycled polyester moisture wicking polyester POY filaments spun from a piece of cardboard, comprising the following steps:

[0035] Step 1. Pre-crystallize the material, the material is PET bottle sheet; specifically, dry hot air is used for pre-crystallization; when the material is pre-crystallized, the pre-crystallization temperature is 176°C, and the temperature of the dry hot air is 176°C , The air dew point is -55℃, the material moisture content is 50ppm, and the drying time is 9 hours.

[0036] Step 2. Feed the hot-air-dried PET bottle return material into the screw extruder; when the material is fed in the screw type, the material is PET (polyethylene terephthalate) bottle return material.

[0037] Step 3. Filter, homopolymerize, pressurize, filter, homopolymerize, and pressurize the mixture extruded by the extruder to ensure continuous spinning production and constant melt pressure; the pre-filtration pressure during filtration...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a method for manufacturing a bottle piece spinning return material recycled polyester moisture-absorbing sweat-releasing POY filament. The method includes the following steps that (1) pre-crystallization is carried out on materials, wherein the materials are PET bottle piece return materials, and dried hot air is adopted for pre-crystallization; (2) the materials are fed in a screw mode, the PET bottle piece return materials are dried through hot air, and then the dried PET bottle piece return materials are fed into a screw extruding machine; (3) filtering, homopolymerization and pressurizing are carried out, wherein filtering, homopolymerization and pressurizing are carried out on melts generated through extruding of the extruding machine so as to guarantee continuous production of spun yarn and stability of melt pressure; (4) spinning is carried out, wherein the melts output from a pressurizing pump enter a spinning assembly, and are ejected from a spinneret plate through the spinning assembly and coiled and formed. The bottle piece spinning return material recycled polyester moisture-absorbing sweat-releasing POY filament manufactured in the method is good in moisture-absorbing and sweat-releasing characteristic, size stability and air permeability, and stability of fabrics is not influenced by any environment.

Description

technical field [0001] The invention belongs to the technical field of fiber preparation, in particular to a preparation method of regenerated polyester moisture-absorbing and sweat-wicking polyester POY filaments. Background technique [0002] Products made of recycled polyester moisture-absorbing and sweat-wicking polyester POY filaments are ideal materials for high-end clothing. Specifically: [0003] Moisture absorption and perspiration function: moisture absorption and perspiration requirements and other characteristics, we have made a special design for the key technology and process of this product, first of all, the design of the shape of the spinneret hole, the ratio of the length of the spinneret hole to the width of the blade requires 3: 1. The angle between the three lobes is 120 degrees, and the central part of the arc R=0.20mm. This special design and the adjustment of the size of the side blowing cooling air process make the cross-sectional shape of th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D01D13/00D01D1/04D01D5/08
Inventor 窦宝盛陈士胜
Owner 仪征市仲兴环保科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap