A kind of method for preparing ammonium sulfate from phosphogypsum and increasing the granularity of ammonium sulfate

A technology for making gypsum and phosphogypsum, which is applied in chemical instruments and methods, ammonium salt fertilizers, nitrogen fertilizers, etc., can solve the problems of easy agglomeration, influence on chroma and purity, etc. dust effect

Active Publication Date: 2015-09-09
WENGFU (GRP) CO LTD
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

And the particle size of ammonium sulfate made from phosphogypsum, ammonia and carbon dioxide is 0.1-0.2mm, it is easy to agglomerate after long storage, and it also contains a small amount of impurities, which affects the color and purity

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] Take 400g of crystalline ammonium sulfate produced by a phosphate fertilizer factory, add 1000g of water, dissolve at a temperature of 70°C and a stirring speed of 200r / min, add 7g of fly ash and white carbon black, filter after 30min, and let the filtrate stand for 20min. Concentrate by heating until the density of the concentrated liquid is 1.20g / cm 3 , put the concentrated solution into a crystallization tank with a temperature of 80°C, stir at a speed of 300r / min, add 2.8g of crystal modifier magnesium sulfate, keep the temperature constant for 20min, add 18g of seed crystals, when the seeds are not completely dissolved, start Use program cooling, the cooling rate is 18°C / h, when it drops to 76°C, the cooling rate is reduced to 10°C / h, from the beginning of cooling and crystallization, the stirring speed is reduced by 20r / min per hour, when the temperature is lowered to 30°C, stop cooling and filter , drying, the purity of the obtained ammonium sulfate product is 99...

Embodiment 2

[0017] Take 650g of crystalline ammonium sulfate produced by a phosphate fertilizer factory, add 1000g of water, dissolve at a temperature of 50°C and a stirring speed of 600r / min, add 1.7g of white carbon black, filter after 40min, and then heat and concentrate the filtrate after standing for 30min. Concentrate density is 1.36g / cm 3 , Put the concentrated solution into a crystallization tank with a temperature of 96°C, stir at a speed of 400r / min, add 4g of zinc sulfate as a crystal modifier, keep the temperature constant for 30min, add 7g of seed crystals, and start using Programmed cooling, the cooling rate is 22°C / h. When it drops to 76°C, the cooling rate is reduced to 12°C / h. From the beginning of cooling and crystallization, the stirring speed is reduced by 20r / min per hour. When the temperature drops to 42°C, stop cooling and filter. Drying, the ammonium sulfate product purity that obtains is 99.32%, and ammonium sulfate particle size is 3-4mm.

Embodiment 3

[0019] Take 500g of crystalline ammonium sulfate produced by a phosphate fertilizer factory, add 1000g of water, dissolve at a temperature of 60°C and a stirring speed of 400r / min, add 5g of fly ash, filter after 60min, and heat the filtrate to concentrate after standing for 40min. The liquid density is 1.28g / cm 3 , Put the concentrated solution into a crystallization tank with a temperature of 88°C, stir at a speed of 350r / min, add 4g of crystal modifier urea and 1g of magnesium sulfate, keep the temperature constant for 40min, add 9g of seed crystals, when the seeds are not completely dissolved , start to use program cooling, the cooling rate is 20°C / h, when it drops to 76°C, the cooling rate is reduced to 10°C / h, from the beginning of cooling and crystallization, the stirring speed is reduced by 20r / min per hour, and the cooling is stopped when the temperature drops to 40°C , filtered, dried, the obtained ammonium sulfate product has a purity of 99.15%, and the particle siz...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for preparing large particle ammonium sulfate from ardealite. The method comprises the steps of firstly adding water into ammonium sulfate generated by conversion of ardealite, ammonia gas and carbon dioxide according to certain proportion and mixing, after heating and dissolving through stirring, adding coal ash and white carbon black for purifying the ammonium sulfate solution, filtering the solution, standing the filtrate for a while, then evaporating and concentrating the filtrate, stopping heating when the density of the concentrated solution is 1.20-1.36g / cm<3>, transferring the concentrated solution to a 80-96 DEG C crystallizing tank, beginning stirring, after the temperature is constant, adding a crystallizing modifier, preserving heat for 20-40 minutes, then adding ammonium sulfate seed crystal, beginning programmed freezing when the seed crystal is not dissolved completely, stopping cooling when cooling to be 30-42 DEG C, filtering, and stoving so as to obtain large particle ammonium sulfate crystal product. The ammonium sulfate product prepared by the method has high purity, good chroma, and large particle, and is not easy to cake; in addition, the preparation method is simple in technological processes, low in production cost, and easy to realize industrialization.

Description

technical field [0001] The invention relates to ammonium sulfate, in particular to a method for increasing the particle size and purity of the product ammonium sulfate in the process of preparing ammonium sulfate from phosphogypsum. Background technique [0002] Ammonium sulfate is abbreviated as ammonium sulfate. It is a commonly used chemical fertilizer. Its solubility in water at 20°C is 75.4. It is acidic after being dissolved in water. It is easily absorbed by crops after being applied to the soil. It is especially suitable for alkaline soils. Ammonium sulfate can be used as In base fertilizer, topdressing fertilizer and compound fertilizer, when used as base fertilizer and topdressing fertilizer, cover soil and water after application, and use in compound fertilizer can improve the utilization rate of other elements in compound fertilizer and reduce fertilizer loss. [0003] At present, the common ammonium sulfate in the market is mostly powdery or small granular ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C01C1/248C05C3/00
Inventor 刘飞李天祥史连军
Owner WENGFU (GRP) CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com