Nano-titanium dioxide automobile topcoat coating

A technology of nano-titanium dioxide and automotive topcoat, applied in coatings and other directions, can solve the problems of easy agglomeration and dispersion instability of nano-materials, and achieve the effects of reducing agglomeration, improving gloss, and increasing compactness

Inactive Publication Date: 2014-05-14
CHONGQING UNIVERSITY OF SCIENCE AND TECHNOLOGY
View PDF6 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Since nanomaterials are fine particles that cannot be seen by ordinary microscopes, and their surface activity is quite high, after the current nanomaterials are added to the base material to prepare a coating, the nanomaterials are prone to further agglomeration, flocculation, and dispersion instability.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] Embodiment 1, the preparation of nano-titanium white slurry

[0022] Add 88% hydroxy acrylic resin, 7% nano-titanium dioxide, 2% xylene, 2.6% butanol, and 0.4% butyl acetate into the mixer, stir at a high speed to make the mixture even, and the stirring speed is 1200~ 1300r / min. Then grind for 5-6 hours to obtain nano-titanium white slurry;

Embodiment 2

[0023] The preparation of embodiment 2 titanium white slurry

[0024] Add hydroxyacrylic resin with a mass fraction of 88%, 7% titanium dioxide, 2% xylene, 2.6% butanol, and 0.4% butyl acetate into the mixer, stir at a high speed to make the mixture even, and the stirring speed is 1200-1300r / min, then grind for 5-6 hours to obtain titanium white slurry;

Embodiment 3

[0026] Mix 60 parts of titanium white paste, 14 parts of nano-titanium white paste, 7 parts of 1158 amino resin, 0.3 part of leveling agent, 8.7 parts of butanol, and 10 parts of butyl acetate in a mixer to obtain the product. The content of nano titanium dioxide is 0.98%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a nano-titanium dioxide automobile topcoat coating. The nano-titanium dioxide automobile topcoat coating is characterized by being prepared from the following raw materials in parts by weight: 55-70 parts of titanium dioxide slurry, 8.5-21.4 parts of nano-titanium dioxide slurry, 6-8 parts of polar resin, 0.2-0.4 part of a flatting agent and 15-20 parts of a dispersing agent, wherein the nano-titanium dioxide slurry comprises the following components in percentage by mass: 88 percent of hydroxy acrylic resin, 7 percent of nano-titanium dioxide, 2 percent of dimethylbenzene, 2.6 percent of butyl alcohol and 0.4 percent of butyl acetate; the particle diameter of the nano-titanium dioxide is 65-130 nanometers; the dispersing agent is the combination of butyl alcohol, butyl acetate and dimethylbenzene. By adopting the coating, the agglomeration, flocculation and dispersion of titanium dioxide are avoided, and stable ultraviolet resistance, high hardness and high compactness are realized.

Description

technical field [0001] The invention relates to an automobile coating, in particular to a nano-titanium dioxide automobile topcoat. Background technique [0002] Paint coating is one of the main processes in the manufacture of automobiles and motorcycles. It plays a decorative and protective role and can improve the grade of products. With the rapid development of automobiles and motorcycles at home and abroad and the entry of WTO, product competition is increasingly intensified. All manufacturers are improving and innovating in quality, variety, shape, and appearance. The innovation and paint film of the overall appearance and decoration of automobiles and motorcycles The improvement of service life is particularly important to increase the competitiveness of products. [0003] At present, the appearance of the existing automobile paint film is exposed to sunlight and ultraviolet rays. After a period of use, the appearance of the paint film will produce aging phenomena suc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/00C09D161/20C09D7/12
Inventor 曹鹏军兰伟仵海东范培耕周安若刘筱薇
Owner CHONGQING UNIVERSITY OF SCIENCE AND TECHNOLOGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com