A composite material and non-woven technology, which is applied in non-woven fabrics, textiles and papermaking, chemical instruments and methods, etc., can solve the problems of unfavorable wide-scale application and low strength of sound-absorbing materials, and achieve light and thin strength and low production cost. , good sound absorption effect

Active Publication Date: 2014-05-28
DANYANG YUSHENG TEXTILE NEW MATERIAL
View PDF4 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the strength of kapok fiber is about one-third of that of polyester fiber, and the price of kapok f

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Sound-absorption needled non-woven composite and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0025] Example 1

[0026] The preparation method of the sound-absorbing needle punched non-woven composite material of this embodiment includes the following specific steps:

[0027] A. Using the existing opening, carding, and netting process disclosed in the 2010 master's thesis of Donghua University "Research on the Sound Absorption Properties of Composite Needle Punched Nonwovens", the porous polyester fiber is opened, carded and formed into a net. The porous polyester fiber uses 8.33dtex×64mm seven-hole polyester staple fiber produced by Sinopec Yizheng Chemical Fiber Co., Ltd.

[0028] B. The fiber web is fed into the needle punching machine for needling reinforcement, winding, and cutting to make two fabric samples. One fabric sample has a thickness of 10mm and an areal density of 55g / m 2 , The thickness of another cloth sample is 10mm and the areal density is 70g / m 2 . The total number of needles of the needle punching machine: 4800 needles, area 1.2m×0.3m, needle punching ...

Example Embodiment

[0031] Example 2

[0032] The preparation method of the sound-absorbing needle punched non-woven composite material of this embodiment includes the following specific steps:

[0033] A. Using the existing opening, carding, and netting process disclosed in the 2010 master's thesis of Donghua University "Research on the Sound Absorption Properties of Composite Needle Punched Nonwovens", the porous polyester fiber is opened, carded and formed into a net. The porous polyester fiber uses 8.33dtex×64mm seven-hole polyester staple fiber produced by Sinopec Yizheng Chemical Fiber Co., Ltd.

[0034] B. The fiber web is fed into the needle punching machine for needling reinforcement, winding, and cutting to make two fabric samples. One fabric sample has a thickness of 10mm and an areal density of 65g / m 2 , The thickness of another cloth sample is 10mm and the areal density is 50g / m 2 . The total number of needles of the needle punching machine: 4800 needles, area 1.2m×0.3m, needle punching ...

Example Embodiment

[0037] Example 3

[0038] The preparation method of the sound-absorbing needle-punched nonwoven composite material of this example is the same as in Example 1, except for the difference: the porous polyester fiber is made of 10.00dtex×60mm seven-hole polyester staple produced by Sinopec Yizheng Chemical Fiber Co., Ltd. fiber.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Areal densityaaaaaaaaaa
Lengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparation method for a sound-absorption needled non-woven composite. The preparation method comprises the following steps: A, opening porous polyester fibers, carding and netting; B, inputting the fiber net into a needling machine for reinforcing by needling, winding, cutting, and preparing fabric, wherein the thickness of the fabric is 4-40 mm and the surface density of the fabric is 40-500 g/m<2>; C, laminating 2-6 layers of the fabric, conducing hot pressing for combining, and then cooling, wherein the temperature for the hot pressing is 100-120 DEG C. The invention further discloses the sound-absorption needled non-woven composite. After hot pressing for combining, the sound-absorption performance of the sound-absorption needled non-woven composite is significantly improved; besides, the sound-absorption needled non-woven composite is light, thin, high in strength and low in production cost.

Description

technical field [0001] The invention relates to a sound-absorbing material and a preparation method thereof, in particular to a needle-punched non-woven sound-absorbing material and a preparation method thereof, belonging to the technical field of sound-absorbing materials. Background technique [0002] With the advancement of science and technology, people have brought more social problems to themselves while enjoying high-efficiency social activities, among which environmental pollution has become one of the main bottlenecks restricting the development of human society. At the same time, noise pollution has seriously affected people's living standards along with modern high-speed transportation and enterprise production. Noise reduction has become an important issue related to people's living standards and coordinated development. There are two main development directions for noise reduction: one is sound insulation technology, and the other is sound absorption technology...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B32B27/36B32B3/26B32B37/06D04H1/435D04H1/46
CPCB32B3/26B32B3/266B32B5/02B32B5/022B32B5/26B32B27/08B32B27/12B32B27/36B32B37/00B32B37/02B32B37/06B32B37/10B32B2250/05B32B2250/20B32B2262/0276B32B2262/0284B32B2307/102B32B2457/00B32B2605/08B32B2605/10D04H1/435D04H1/46
Inventor 晏雄陈夕方杨旭东张慧萍陈静
Owner DANYANG YUSHENG TEXTILE NEW MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap