A kind of resin and preparation method thereof

A resin and epoxy resin technology, applied in the field of synthetic resin and resin, can solve the problems of low adhesion, low alcohol resistance, poor effect, etc., and achieve obvious adhesion, high alcohol resistance, and improved adhesion. Effect

Inactive Publication Date: 2016-11-23
JIANGMEN SANMU CHEM
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Resin is very common in daily life and production. It has excellent performance and is widely used. Acrylic resin is a very mature resin, such as for adhesion on substrates, or floors, etc., but conventional Acrylic resin usually has low adhesion and low alcohol resistance after forming a film on a metal substrate. In order to improve the characteristics of these two aspects, some manufacturers have adjusted and changed the synthesis or components, but the effect is still not good.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] A resin, which is formed by copolymerization of common bisphenol A epoxy resin and acrylic resin prepolymer at a ratio of 55:100 at 220-240g / eq, wherein the acrylic resin prepolymer includes the following groups Minute:

[0031] Methyl methacrylate: 55wt%,

[0032] Butyl methacrylate: 5wt%,

[0033] Ethyl acrylate: 10wt%,

[0034] Butyl acrylate: 5wt%,

[0035] Acrylic acid: 8wt%,

[0036] Benzoyl peroxide: 2wt%.

[0037] Its concrete preparation process is as follows:

[0038] 1, synthetic acrylic resin prepolymer according to the ratio;

[0039] II. Add xylene and the above-mentioned acrylic resin prepolymer dropwise (2 hours) at the reflux temperature in a ratio of 0.9:1 to make it undergo free radical polymerization;

[0040] III. After the dropwise addition, keep warm for 2 hours, add xylene accounting for 5wt% of the acrylic resin prepolymer, and 0.1wt% TBPB accounting for the acrylic resin prepolymer, and keep warm for 1 hour at reflux temperature;

[004...

Embodiment 2

[0045] A resin, which is formed by copolymerization of common bisphenol A epoxy resin and acrylic resin prepolymer at a ratio of 60:100 at 220-240g / eq, wherein the acrylic resin prepolymer includes the following groups Minute:

[0046] Methyl methacrylate: 60wt%,

[0047] Butyl methacrylate: 7.5 wt%,

[0048] Ethyl acrylate: 15wt%,

[0049] Butyl acrylate: 7.5wt%,

[0050] Acrylic acid: 9wt%,

[0051] Benzoyl peroxide: 2.5 wt%.

[0052] Its concrete preparation process is as follows:

[0053] 1, synthetic acrylic resin prepolymer according to the ratio;

[0054] II. Add xylene and the above-mentioned acrylic resin prepolymer dropwise (2.5 hours) at the reflux temperature in a ratio of 1:1 to make it undergo free radical polymerization;

[0055] III. After the dropwise addition, keep warm for 2 hours, add xylene accounting for 5wt% of the acrylic resin prepolymer, and 0.1-0.3wt% TBPB accounting for the acrylic resin prepolymer, and keep warm at reflux temperature for 1 h...

Embodiment 3

[0060] A resin, which is formed by copolymerization of common bisphenol A epoxy resin and acrylic resin prepolymer at a ratio of 65:100 at 220-240g / eq, wherein the acrylic resin prepolymer includes the following groups Minute:

[0061] Methyl methacrylate: 65wt%,

[0062] Butyl methacrylate: 10wt%,

[0063] Ethyl acrylate: 20wt%,

[0064] Butyl acrylate: 10wt%,

[0065] Acrylic acid: 10wt%,

[0066] Benzoyl peroxide: 3wt%.

[0067] Its concrete preparation process is as follows:

[0068] 1, synthetic acrylic resin prepolymer according to the ratio;

[0069] II, xylene is added dropwise (3 hours) to the above-mentioned acrylic resin prepolymer in a ratio of 1.1:1 at reflux temperature to make it undergo free radical polymerization;

[0070] III. After the dropwise addition, keep warm for 2 hours, add xylene accounting for 5wt% of the acrylic resin prepolymer, and 0.3wt% TBPB accounting for the acrylic resin prepolymer, and keep warm for 1 hour at reflux temperature;

[00...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
epoxy equivalentaaaaaaaaaa
Login to view more

Abstract

The invention proposes novel resin, which is prepared from epoxy resin and an acrylic resin prepolymer through copolymerization according to the ratio of (55-65):100, wherein the acrylic resin prepolymer comprises the following components: 55-65wt% of methyl methacrylate, 5-10wt% of butyl methacrylate, 10-20wt% of ethyl acrylate, 5-10wt% of butyl acrylate, 8-10wt% of acrylic acid and 2-3wt% of benzoyl peroxide. The adhesive force of the novel resin on a substrate after a paint film is formed is improved, and can be up to over two grades, and the alcohol resistance is higher. The invention also proposes a preparation method of the novel resin. The method is simple and feasible, and applicable to popularization.

Description

technical field [0001] The invention relates to the field of synthetic resins, in particular to a resin, and also relates to a method for preparing the resin. Background technique [0002] Resin is very common in daily life and production. It has excellent performance and is widely used. Acrylic resin is a very mature resin, such as for adhesion on substrates, or floors, etc., but conventional Acrylic resin usually has low adhesion and low alcohol resistance after forming a film on a metal substrate. In order to improve these two characteristics, some manufacturers have adjusted and changed the synthesis or components, but the effect is still not good. Contents of the invention [0003] One of the objectives of the present invention is to propose a resin, which is mainly used to improve the adhesion and alcohol resistance of acrylic resin on the substrate under the premise of maintaining low cost. [0004] Another object of the present invention is to propose a resin prep...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08F220/14C08F220/18C08F220/06C09D133/12C09D163/00
Inventor 刘霞
Owner JIANGMEN SANMU CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap