Attapulgite-containing refining agent for melting of magnesium alloy

A technology of attapulgite and magnesium alloy, which is applied in the field of metal material processing, can solve the problems of reducing the mechanical properties, corrosion resistance and poor corrosion resistance of magnesium alloys, so as to improve the removal rate of inclusions, improve the ability of slagging, reduce the The effect of content

Active Publication Date: 2014-07-30
江苏古沙农业科技发展有限公司
View PDF3 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Magnesium alloy is the lightest metal structure material in practical application. It has the advantages of high specific strength and specific stiffness, thermal and electrical conductivity, electromagnetic shielding and environmental compatibility, but it has the

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] A refining agent for magnesium alloy smelting containing attapulgite, made of the following raw materials in parts by weight: 10 parts of attapulgite, 3 parts of quartz sand nano powder, 13 parts of tool steel powder, 3 parts of barium oxide, and 3 parts of boron oxide 3 parts of calcium fluoride, 1 part of manganese chloride, 2 parts of magnesium sulfate, 0.5 parts of titanium sponge, 2 parts of nano silicon dioxide, 2 parts of straw ash, 10 parts of sodium nitrate, 2 parts of vermiculite powder, 3.5 parts of cryolite , 6 parts of wood carbon powder, 15 parts of hexachloroethane, 8 parts of rare earth chloride, 5 parts of zirconium tetrachloride, and 5 parts of GaSi.

[0013] The preparation method of the magnesium alloy smelting refining agent containing attapulgite comprises the following preparation steps: mixing raw materials except sponge titanium and boron oxide, heating to a molten state, and then pouring into pure water to quench, Then crush it into 200 mesh po...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

A disclosed attapulgite-containing refining agent for melting of magnesium alloy is prepared from the following raw materials in parts by weight: 8-10 parts of attapulgite, 2-4 parts of quartz sand nanometer powder, 12-15 parts of tool steel powder, 3-4 parts of barium oxide, 2-3 parts of boron oxide, 3-4 parts of calcium fluoride, 1-2 parts of manganese chloride, 2-3 parts of magnesium sulfate, 0.3-0.5 part of titanium sponge, 2-3 parts of nanometer silica, 1-2 parts of straw ash, 10-12 parts of sodium nitrate, 1-2 parts of vermiculite powder, 3-4 parts of cryolite, 5-7 parts of charcoal powder, 13-15 parts of hexachloroethane, 7-9 parts of chlorinated rare earth, 5-6 parts of zirconium tetrachloride and 4-6 parts of GaSi. According to the refining agent, titanium sponge, manganese chloride and boron oxide are capable of chemically reacting with element iron in melt for forming compounds, slagging and discharging, so that the content of iron element in magnesium alloy is substantially reduced; cryolite is beneficial for improving the slagging capability of a solvent; zirconium tetrachloride is beneficial for improving inclusion removing rate of alloy and improving the mechanical properties and the corrosion resistance of alloy; and CaSi helps to improve the capability of forming composite inclusions.

Description

technical field [0001] The invention relates to the technical field of metal material processing, in particular to a refining agent for smelting magnesium alloys containing attapulgite. Background technique [0002] Magnesium alloy is the lightest metal structure material in practical application. It has the advantages of high specific strength and specific stiffness, thermal and electrical conductivity, electromagnetic shielding and environmental compatibility, but it has the problem of poor corrosion resistance. Magnesium chemical properties Lively, magnesium alloys often contain a large amount of impurities such as oxides, carbides and sulfides, which significantly reduce the mechanical properties and corrosion resistance of magnesium alloys. Therefore, during the smelting process of magnesium alloys, solvents are used to refine them. The purpose of the refining treatment is to reduce the impurity elements such as iron and non-metallic impurities such as magnesium oxide m...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C23/00C22C1/06C22B9/10
Inventor 倪菲菲
Owner 江苏古沙农业科技发展有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap