High heat absorption high-brightness bottle-grade polyester chip and preparation method thereof

A technology of polyester chips and high brightness is applied in the field of high-endothermic and high-brightness bottle-grade polyester chips and their preparation. , The effect of good crack resistance and low acetaldehyde content

Inactive Publication Date: 2014-09-03
CHINA RESOURCES PACKAGING MATERIALS CO LTD +1
View PDF2 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] At present, there are far-infrared absorbing polyester chips on the market, but since these products use carbon black materials as far-infrared absorbers, a large amount of addition is required to achieve a satisfactory energy-saving effect, which affects the color of polyester chips. The value has a large influence

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0026] (1), mix titanium nitride with ethylene glycol, and prepare a titanium nitride mixed solution with a titanium nitride concentration of 1% by weight; mix barium sulfate with ethylene glycol, and prepare a mixed solution of barium sulfate with 0.5% by weight ;

[0027] (2), esterification reaction:

[0028] After mixing terephthalic acid (PTA), ethylene glycol (EG), antimony acetate, and toner into slurry, it enters the esterification kettle. The esterification reaction temperature is 270°C, the reaction pressure is 0.3 Mpa, and the reaction time is 2.5 hours; the weight ratio of terephthalic acid and ethylene glycol is 4:1; the amount of antimony acetate added is 550ppm in the weight content of the finished polyester chips; the toner is composed of redness agent and blueness agent, redness The additive amount is that the weight content in the finished polyester is 0.4ppm, and the blueness agent additive amount is that the weight content in the finished polyester is 0.6p...

example 2

[0037] (1), mix titanium nitride with ethylene glycol, and prepare a titanium nitride mixed solution with a titanium nitride concentration of 1% by weight; mix barium sulfate with ethylene glycol, and prepare a mixed solution of barium sulfate with 0.5% by weight ;

[0038] (2), esterification reaction:

[0039] After mixing terephthalic acid (PTA), ethylene glycol (EG), antimony acetate, and toner into slurry, it enters the esterification kettle. The esterification reaction temperature is 270°C, the reaction pressure is 0.3 Mpa, and the reaction time is 2.5 hours; the weight ratio of terephthalic acid and ethylene glycol is 4:1; the amount of antimony acetate added is 550ppm in the weight content of the finished polyester chips; the toner is composed of redness agent and blueness agent, redness The additive amount is that the weight content in the finished polyester is 0.4ppm, and the blueness agent additive amount is that the weight content in the finished polyester is 0.6p...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a high heat absorption high-brightness bottle-grade polyester chip which is characterized by containing titanium nitride and barium sulfate, wherein the weight content of titanium nitride in the polyester chip is 3-30ppm; the weight content of barium sulfate in the polyester chip is 0.1-5ppm. The invention further relates to a preparation method of the high heat absorption high-brightness bottle-grade polyester chip. The bottle-grade polyester chip provided by the invention has the advantages of high heat absorption and high brightness.

Description

technical field [0001] The present invention relates to a bottle-grade polyester chip, in particular to a bottle-grade polyester chip with high heat absorption and brightness and a preparation method thereof. Background technique [0002] Polyester is a general term for thermoplastic linear saturated polyester represented by polyethylene terephthalate (PET). One of its important uses is in the field of food packaging. As a food packaging material, PET can be made into biaxially stretched packaging film, and can also be made into amorphous preforms and then blown to obtain high-strength, high-transparency stretch blow-molded bottles, and can also be directly extruded into sheets The material is then thermoformed to produce a hollow container. PET products are transparent, oil-resistant, fragrant, hygienic and reliable, and have a wide range of operating temperatures, so their usage in the packaging field continues to grow. [0003] Before the preform is blown into a bottle,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L67/02C08K3/28C08K3/30C08G63/183C08G63/80
Inventor 朱振达宗建平陈小雷
Owner CHINA RESOURCES PACKAGING MATERIALS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com