Method for preparing cement admixture by use of electrolytic manganese residue and product and application

A technology of electrolytic manganese slag and mixed materials, applied in the direction of cement production, etc., can solve the problems of increasing the cost of land requisition and site disposal of waste residues piled up by enterprises, increasing production costs, and large land resources.

Inactive Publication Date: 2014-09-10
贵州省工业固体废弃物综合利用(建材)工程技术研究中心
View PDF4 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

On the one hand, these acid leaching waste residues increase the cost of land requisition and site disposal for enterprises to pile up waste residues, increase the production cost of enterprises, and consume a large amount of land

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing cement admixture by use of electrolytic manganese residue and product and application
  • Method for preparing cement admixture by use of electrolytic manganese residue and product and application
  • Method for preparing cement admixture by use of electrolytic manganese residue and product and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] Embodiment 1 of the present invention: A method for preparing cement admixture by using electrolytic manganese slag is as follows: first crush the electrolytic manganese slag to a particle size of 5-15mm; then place the crushed electrolytic manganese slag in a fluidized fluidized furnace The temperature is calcined for 1 to 1.5 hours to obtain the cement mixture.

Embodiment 2

[0022] Embodiment 2 of the present invention: a method for preparing cement mixture by using electrolytic manganese slag is as follows: first crush the electrolytic manganese slag to a particle size of 5-15 mm; The temperature of ℃ is calcined for 1-1.5 hours to obtain the cement mixture.

Embodiment 3

[0023] Embodiment 3 of the present invention: A method for preparing cement mixture by using electrolytic manganese slag is as follows: first crush the electrolytic manganese slag to a particle size of 5-15mm; The temperature of ℃ is calcined for 1-1.5 hours to obtain the cement mixture.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a method for preparing a cement admixture by use of electrolytic manganese residue and a product and an application. The method comprises the following steps: breaking the electrolytic manganese residue into the particle size of 5-15mm; calcining the broken electrolytic manganese residue in a fluidized-bed furnace for 1-1.5 hours at 450-750 DEG C to obtain the cement admixture. The obtained cement admixture can be applied to the preparation of cement, namely that the cement is prepared by grinding 5-50% of cement admixture and 95-50% of Portland cement clinker by weight. Through the invention, waste utilization and comprehensive treatment of the electrolytic manganese residue can be realized.

Description

technical field [0001] The invention relates to a method, product and application for preparing cement admixture by using electrolytic manganese slag, and belongs to the field of comprehensive utilization of industrial waste residue and cement building materials. Background technique [0002] Manganese is one of the dominant mineral resources in Guizhou Province. Songtao County in Guizhou Province, adjacent to Huayuan County in Hunan Province and Xiushan Autonomous County in Chongqing are known as the "Manganese Triangle" of China's manganese mines. Manganese ore resources are valuable resources in this region, and its reserves account for more than 30% of the country's total reserves. 90% to 95% of manganese production is used in the iron and steel industry, and its use is mainly as a deoxidizer and desulfurizer in the process of ironmaking and steelmaking, as well as for the manufacture of alloys. In addition, chemical industry, light industry, building materials and othe...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B7/147C04B7/43
CPCY02P40/10
Inventor 王勇刘恒波甘四洋彭建军贺勇高遇事宋美唐朝军闫亚楠
Owner 贵州省工业固体废弃物综合利用(建材)工程技术研究中心
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap