Preparation method of plating layer protective agent, plating layer protective agent prepared by method and use of plating layer protective agent, and hot-dip plated metal material

A hot-dip metal and protective agent technology, applied in the direction of metal layered products, chemical instruments and methods, coatings, etc., can solve the problems of poor corrosion resistance of the protective film, and achieve excellent storage resistance and excellent corrosion resistance.

Inactive Publication Date: 2014-09-24
PANZHIHUA IRON & STEEL RES INST OF PANGANG GROUP
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the invention is to overcome the relatively poor corrosion resistance defect of the protective film formed by the existing coating protective agent, and provide a coating protective agent capable of forming a better protective film with corrosion resistance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of plating layer protective agent, plating layer protective agent prepared by method and use of plating layer protective agent, and hot-dip plated metal material

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0013] The invention provides a method for preparing a plating protective agent, which comprises mixing water, a silane coupling agent, a water-soluble silicate, a silicon oxide filler, and a water-soluble film-forming resin in sequence; the silane coupling agent comprises The first silane coupling agent and the second silane coupling agent, the first silane coupling agent is HS (CH 2 ) 3 Si(OCH 3 ) 3 、HS(CH 2 ) 3 Si(OC 2 h 5 ) 3 、HS(CH 2 ) 3 SiCH 3 (OCH 3 ) 2 and HS(CH 2 ) 3 SiCH 3 (OC 2 h 5 ) 2 at least one of; the second silane coupling agent is CH 2 =C(CH 3 )COO(CH 2 ) 3 Si(OCH 3 ) 3 、CH 2 =C(CH 3 )COO(CH 2 ) 3 Si(OC 2 h 5 ) 3 、CH 2 =C(CH 3 )COO(CH 2 ) 3 SiCH 3 (OCH 3 ) 2 and CH 2 =C(CH 3 )COO(CH 2 ) 3 SiCH 3 (OC 2 h 5 ) 2 at least one of the

[0014] Wherein, in detail, the method includes: (1) uniformly mixing water and the silane coupling agent to obtain a uniform liquid A; (2) uniformly mixing the uniform liquid A and a wat...

Embodiment 1

[0051] Mix 28 parts by weight of water and 1.6 parts by weight of silane coupling agent (composed of the first silane coupling agent and the second silane coupling agent) at a stirring speed of 1500 rpm to obtain uniform liquid A, Among them, the first silane coupling agent is HS(CH 2 ) 3 Si(OCH 3 ) 3 , purchased from Hubei Debang Chemical New Material Co., Ltd., brand DB-590, the second silane coupling agent CH 2 =C(CH 3 )COO(CH 2 ) 3 Si(OCH 3 ) 3 , purchased from Hubei Debang Chemical New Material Co., Ltd., brand DB-570, the weight ratio of the first silane coupling agent and the second silane coupling agent is 4:1.

[0052] Mix all the uniform liquid A and 1 part by weight of water-soluble silicate (sodium metasilicate pentahydrate, purchased from Qingdao Darun Chemical Co., Ltd.) at a stirring speed of 1500 rpm until uniform to obtain uniform liquid B .

[0053] All the uniform liquid B and 0.72 parts by weight of silica filler (nano-silica sol, purchased from S...

Embodiment 2

[0066] Mix 25 parts by weight of water and 1.4 parts by weight of silane coupling agent (composed of the first silane coupling agent and the second silane coupling agent) at a stirring speed of 1500 rpm to obtain a homogeneous liquid A, Among them, the first silane coupling agent is HS(CH 2 ) 3 Si(OC 2 h 5 ) 3 , purchased from Hubei Debang Chemical New Material Co., Ltd., brand DB-580, the second silane coupling agent is CH 2 =C(CH 3 )COO(CH 2 ) 3 Si(OCH 3 ) 3 , purchased from Hubei Debang Chemical New Material Co., Ltd., brand DB-570, the weight ratio of the first silane coupling agent and the second silane coupling agent is 3.7:1.

[0067] All of the uniform liquid A and 1 part by weight of water-soluble silicate (potassium silicate, purchased from Baoding Runfeng Industrial Co., Ltd.) were mixed until uniform at a stirring speed of 1500 rpm to obtain a uniform liquid B.

[0068] Mix all the homogeneous liquid B and 0.6 parts by weight of silica filler (nano-silica...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
viscosityaaaaaaaaaa
viscosityaaaaaaaaaa
Login to View More

Abstract

The invention provides a preparation method of a plating layer protective agent. The method comprises successively mixing evenly water, silane coupling agents, water-soluble silicate, a silica filler and water-soluble film-forming resin. The invention also provides the plating layer protective agent prepared according to the preparation method and a use thereof in preparation of metal materials. The invention further provides a hot-dip plated metal material which comprises a hot-dip plated metal substrate and a coating layer adhering onto the hot-dip plated metal substrate, wherein the coating layer is a cured product of the plating layer protective agent. A protective film formed by the plating layer protective agent provided by the invention is quite excellent in corrosion resistance. In addition, the plating layer protective agent provided by the invention is quite excellent in storage resistance, and can be stored for 180 days at room temperature after completion of preparation but does not generate obvious character changes and performance reduction.

Description

technical field [0001] The invention relates to the field of metal protection, in particular to a preparation method of a plating protection agent, a plating protection agent obtained by the preparation method, uses of the plating protection agent and hot-dip metal materials. Background technique [0002] Hot-dip metal materials, including hot-dip galvanized metal materials and hot-dip galvanized metal materials, in order to prevent corrosion, a layer of coating protection agent will be coated on the surface of the hot-dip metal materials to form a protective film. Therefore, the performance of coating protective agent is very important for the anti-corrosion of hot-dip metal materials. [0003] For example, CN101608306A discloses a passivation solution, which also belongs to a coating protection agent, and is characterized in that the passivation solution is an aqueous solution containing a water-soluble molybdenum compound, boric acid, water-soluble organic matter and sili...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D4/06C09D5/08B32B15/08
Inventor 许哲锋李纪仁李南黄平生李光跃
Owner PANZHIHUA IRON & STEEL RES INST OF PANGANG GROUP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com