Preparation method for conduction and sustained release type nervous tissue engineering scaffold

A nerve tissue, slow-release technology, applied in non-woven fabrics, filament/thread forming, textiles and papermaking, etc., to achieve simple operation, high economic benefits, and good biocompatibility

Active Publication Date: 2014-12-24
诺一迈尔(山东)医学科技有限公司
View PDF5 Cites 27 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At the same time, nerve growth factor (NGF) can also promote the regeneration of motor nerves. So far, there is no preparation of a conductive nerve growth factor (NGF) loaded nerve growth factor (NGF) based on coaxial electrospinning technology. Reports on Tissue Engineering Scaffolds

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method for conduction and sustained release type nervous tissue engineering scaffold
  • Preparation method for conduction and sustained release type nervous tissue engineering scaffold
  • Preparation method for conduction and sustained release type nervous tissue engineering scaffold

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] Weigh 0.1g of protein silk fibroin, 0.3g of lactic acid-caprolactone copolymer, dissolve in 5ml of hexafluoroisopropanol (HFIP), the molecular weight of lactic acid-caprolactone copolymer is Mw≈300,000, at 200r / min. Stir at a high speed for 5 hours and mix evenly to obtain a solution with a total concentration of 8% (w / v); after mixing evenly, add 60mg of polyaniline (Mn≈15,000) and camphorsulfonic acid, and then magnetically stir at a rate of 300r / min. After 48 hours, the cortex electrospinning solution was prepared by mixing evenly, and 1 ml of 10 μg / ml nerve growth factor (NGF) ultrapure aqueous solution was taken as the core electrospinning solution. The electrospinning solution of the shell layer was loaded into a syringe, and the advancing speed of the micro-injection pump was controlled to be 1ml / h. The electrospinning solution of the core layer was loaded into another syringe, and the advancing speed of the micro-injection pump was controlled to be 0.2ml / h. The ...

Embodiment 2

[0037]Weigh 0.125g of protein silk fibroin, 0.375g of lactic acid-caprolactone copolymer, dissolve in 5ml hexafluoroisopropanol (HFIP), the molecular weight of lactic acid-caprolactone copolymer is Mw≈300,000, at 200r / min. Stir at a high speed for 5 hours and mix evenly to obtain a solution with a total concentration of 10% (w / v); after mixing evenly, add 80 mg of polyaniline (Mn≈15,000) and camphorsulfonic acid, and then magnetically stir at a rate of 300r / min. After 48 hours, the cortex electrospinning solution was prepared by mixing evenly, and 1 ml of 10 μg / ml nerve growth factor (NGF) ultrapure aqueous solution was taken as the core electrospinning solution. The electrospinning solution of the shell layer was loaded into a syringe, and the advancing speed of the micro-injection pump was controlled to be 1ml / h. The electrospinning solution of the core layer was loaded into another syringe, and the advancing speed of the micro-injection pump was controlled to be 0.2ml / h. Th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a preparation method for a conduction and sustained release type nervous tissue engineering scaffold. The method comprises the following steps: silk fibroin Silk and lactic acid-caprolactone copolymer are dissolved in a solvent, dissolved and stirred to obtain a solution, then polyaniline and camphorsulfonic acid are added and stirred and mixed uniformly to obtain a cortex electrospinning solution, and NGF (nerve growth factors) are dissolved in ultrapure water completely to obtain a core electrospinning solution; and the cortex electrospinning solution and the core electrospinning solution are accommodated in an injector respectively for coaxial electrospinning, and then fumigation treatment and vacuum drying are performed to obtain the conduction type nervous tissue engineering scaffold. According to the prepared nanofiber scaffold, the nerve repair speed is increased from ways including external electrical stimulation (conductive polymer), biochemistry (NGFs), a topological structure required by nerve regeneration (orientation guide) and the like. The method is simple to operate, good in repeatability and high in economic benefit, and provides novel experimental thought for nerve defect repair in clinical application.

Description

technical field [0001] The invention belongs to the field of nerve defect repair involving the preparation of biological materials, in particular to a preparation method of a conductive slow-release nerve tissue engineering scaffold. Background technique [0002] Peripheral nerve regeneration and functional recovery have always been a clinical problem. Every year, a large number of patients around the world need nerve repair. By far, the most commonly used method is autologous nerve transplantation to treat nerve rupture or defect. However, the sources of autologous nerves available for transplantation are very limited. In addition, it is difficult to avoid the misalignment of nerve fibers during microsurgery, which will affect the recovery of nerve function. In recent years, with the gradual development of tissue engineering, the use of biomaterials to construct nerve regeneration conduits has brought hope for clinical nerve defect repair. [0003] However, peripheral ne...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): A61L27/54A61L27/50A61L27/22A61L27/18D01D5/00D04H1/728D04H1/541
Inventor 莫秀梅张建光孙彬彬宋炜
Owner 诺一迈尔(山东)医学科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com