A preparation process and packaging technology, which is applied in the field of preparation process of packaging straps, can solve problems such as unstable mechanical properties, uneven surface color, and easy occurrence of overburning, and achieve good film-forming effect, high efficiency, and avoid The effect of wastewater

Inactive Publication Date: 2014-12-24
WUXI FANGZHENG METAL LIGATURE
View PDF1 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The disadvantages of high-strength packaging steel strips produced by electric heating furnaces

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A preparation process for strapping for packaging, the chemical composition of the steel is: C: 0.18%, Si: 0.3%, Mn: 1.5%, P≤0.012%, S≤0.008%, Als: 0.020% , Nb: 0.010%, Cr: 0.50%, and the balance is Fe and unavoidable impurities. The cold-rolled coil of the steel is used as the raw material. The preparation process includes the following steps: decoiling, welding, strip slitting and slitting, Deburring and leveling, surface bluing, cooling, cleaning, surface zinc coating, coating drying, waxing, coiling, the surface bluing step is to use electromagnetic induction coil intermediate frequency heating to carry out surface bluing, and the bluing temperature The temperature is controlled at 360°C, and the holding time is 35 seconds; the mass ratio of original paint and water in the zinc coating step is 1:2.5, the coating temperature is 40°C, and the zinc coating speed on the surface is 16m / min.

Embodiment 2

[0025] A preparation process for strapping for packaging, the chemical composition of the steel is: C: 0.20%, Si: 0.2%, Mn: 1.7%, P≤0.012%, S≤0.008%, Als: 0.010% , Nb: 0.012%, Cr: 0.30%, and the balance is Fe and unavoidable impurities. The cold-rolled coil of the steel is used as the raw material. The preparation process includes the following steps: decoiling, welding, strip slitting and slitting, Deburring and leveling, surface bluing, cooling, cleaning, surface zinc coating, coating drying, waxing, coiling, the surface bluing step is to use electromagnetic induction coil intermediate frequency heating to carry out surface bluing, and the bluing temperature The temperature is controlled at 370°C, and the holding time is 25 seconds; the mass ratio of original paint and water in the zinc coating step is 1:2.5, the coating temperature is 45°C, and the zinc coating speed on the surface is 14m / min.

Embodiment 3

[0027] A preparation process for strapping for packaging, the chemical composition of the steel is: C: 0.19%, Si: 0.25%, Mn: 1.6%, P≤0.012%, S≤0.008%, Als: 0.015% , Nb: 0.011%, Cr: 0.40%, the balance is Fe and unavoidable impurities, and the cold-rolled coil of the steel is used as a raw material. The preparation process includes the following steps: decoiling, welding, strip slitting and slitting, Deburring and leveling, surface bluing, cooling, cleaning, surface zinc coating, coating drying, waxing, coiling, the surface bluing step is to use electromagnetic induction coil intermediate frequency heating to carry out surface bluing, and the bluing temperature The temperature is controlled at 35°C, and the holding time is 30 seconds; the mass ratio of original paint and water in the zinc coating step is 1:2.5, the coating temperature is 42°C, and the zinc coating speed on the surface is 15m / min.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a preparation process of a bundling strip for packaging. A cold-rolled steel coil is used as a raw material. The preparation process comprises the following steps of uncoiling, welding, stripping by longitudinally shearing a steel belt, deburring and leveling, surface bluing, cooling, cleaning, surface zinc coating, coating drying, waxing and rolling, wherein the surface bluing step is realized in a way of heating at intermediate frequency by using an electromagnetic induction coil, the bluing temperature is controlled at 360-370 DEG C, and the heat preservation time is controlled within 25-35s; and in the surface zinc coating step, the mass ratio of an original paint to water is 1:2.5, the coating temperature ranges from 40 DEG C to 45 DEG C, and the surface zinc coating speed is controlled at 14-16m/min.

Description

technical field [0001] The invention relates to the technical field of packaging, in particular to a preparation process of a strap for packaging. Background technique [0002] Packaging steel strips are divided into three categories according to their mechanical properties: low-strength steel strips, medium-strength steel strips and high-strength steel strips. Medium and low-strength steel strips are generally made of carbon structural steel. The high-strength steel strip needs to be manufactured with low-alloy steel, alloy structural steel or high-quality carbon structural steel. [0003] Steel belts are usually used as the binding belt, and the items are firmly bundled into a bundle on an automatic or manually operated coil binding machine, stacked on a shelf or placed in a crate for transportation, storage and sales. In some applications, especially those in which strapping bundles of considerable weight, such as a stack of bricks, require the use of steel strapping, th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C38/38C21D1/10B65D63/02
CPCY02P10/25
Inventor 宋志方
Owner WUXI FANGZHENG METAL LIGATURE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap