Rubber hammer iron plating technology

A technology of rubber hammer and process, which is applied in the direction of metal material coating process, liquid chemical plating, coating, etc., can solve the problems affecting the service life of rubber hammer, rubber fatigue, corrosion, etc., and achieve long service life, strong resistance Wear and corrosion resistance, simple operation effect

Inactive Publication Date: 2014-12-24
WUXI DONGBEITANG YONGFENG RUBBER FACTORY
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Existing rubber hammers use rubber that will cause problems such as rubber fatigue, damage, and corrosion after long-term use, which will affect the service life of the rubber hammer

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] Rubber hammer iron plating process, including the following steps:

[0022] 1) Soak the rubber hammer in a solution made of sodium hydroxide and sodium carbonate for 20 minutes;

[0023] 2) Put the rubber hammer into the hydrochloric acid solution with a concentration of 0.3% to roughen it, and then soak the rubber hammer in a solution made of silver nitrate and ammonia water for 20 minutes;

[0024] 3) Soak the rubber hammer in a solution prepared from stannous chloride and hydrochloric acid solution for 30 minutes;

[0025] 4) Put it into copper sulfate solution for electroless iron plating;

[0026] 5) Spray the repair agent on the damaged part of the rubber hammer to form a surface repair agent layer on the outer surface of the rubber hammer;

[0027] 6) Using the preset powder feeding method, laser cladding is carried out layer by layer on the repair agent layer, and the laser cladding starts from the lowest point on the repair agent layer surface;

[0028] 7) R...

Embodiment 2

[0030] Rubber hammer iron plating process, including the following steps:

[0031] 1) Soak the rubber hammer in a solution made of sodium hydroxide and sodium carbonate for 30 minutes;

[0032] 2) Put the rubber hammer into a 0.3% hydrochloric acid solution to roughen it, and then soak the rubber hammer in a solution made of silver nitrate and ammonia water for 30 minutes;

[0033] 3) Soak the rubber hammer in a solution prepared from stannous chloride and hydrochloric acid solution for 40 minutes;

[0034] 4) Put it into copper sulfate solution for electroless iron plating;

[0035] 5) Spray the repair agent on the damaged part of the rubber hammer to form a surface repair agent layer on the outer surface of the rubber hammer;

[0036] 6) Using the preset powder feeding method, laser cladding is carried out layer by layer on the repair agent layer, and the laser cladding starts from the lowest point on the repair agent layer surface;

[0037] 7) Rinse with tap water, then ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a rubber hammer iron plating technology. The rubber hammer iron plating technology comprises the following steps: 1), putting a rubber hammer in a solution prepared from sodium hydroxide and sodium carbonate and soaking for 20-30 minutes; 2), putting the rubber hammer in a 0.3% hydrochloric acid solution to be coarsened and then soaking the rubber hammer with a solution prepared from silver nitrate and ammonia water for 20-30 minutes; 3), soaking the rubber hammer with a solution prepared from stannous chloride and a hydrochloric acid solution for 30-40 minutes; 4), putting the mixture in a copper sulfate solution to carry out chemical iron plating; 5), spraying a restoration agent at the damaged part of the rubber hammer so as to form a surface restoration agent layer on the outer surface of the rubber hammer; 6), carrying out layer-by-layer laser cladding on the restoration agent layer in a preset powder conveying mode, and beginning laser cladding from the surface lowest point of the restoration agent layer; 7), bleaching with running water, and then blowing dry by a draft fan. Rubber processed by the invention has stronger wear-resistant and corrosion-resistant performance and long service life.

Description

technical field [0001] The invention relates to the field of rubber, in particular to a rubber hammer iron plating process. [0002] Background technique [0003] When installing the floor in the decoration industry, in order to make the cement under the floor tiles evenly distributed and no voids appear, a rubber hammer is often used to hit the floor tiles. The existing rubber hammer includes a hammer body and a handle, an inner core is arranged in the hammer body, and the hammer body and the handle are integrated. The rubber used in the existing rubber hammers will have problems such as rubber fatigue, damage, and corrosion after long-term use, which will affect the service life of the rubber hammers. Contents of the invention [0004] The purpose of the present invention is to provide a rubber hammer iron plating process to solve the above problems. [0005] The technical problem solved by the present invention can adopt following technical scheme to realize: [000...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C23C18/30C23C18/24C23C18/32C23C24/10
Inventor 马聚龙
Owner WUXI DONGBEITANG YONGFENG RUBBER FACTORY