Concrete pavior brick facing material with water permeability

A technology of concrete pavement and water permeability, applied in the municipal field, can solve problems such as uneven thickness, easy fading, impermeability, etc., and achieve the effect of reducing cement

Active Publication Date: 2015-02-11
内江市恒世达建材有限公司
View PDF8 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The existing pavement bricks for sidewalks are hand-made water-milled bricks produced by using mold boxes, which have low strength, uneven thickness, large color difference, non-slip, impermeable, and water-grinding will cause water pollution.
[0003] Ordinary permeable bricks have low strength and are easy to fade

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Concrete pavior brick facing material with water permeability
  • Concrete pavior brick facing material with water permeability
  • Concrete pavior brick facing material with water permeability

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] Example 1 Preparation of hemp surface fabric

[0018] Weigh 100 parts by weight of No. 42.5 cement, 300 parts by weight of quartz sand, 4 parts by weight of pigments and 25 parts by weight of water and mix them together to form a hemp surface fabric.

Embodiment 2

[0019] Example 2 Preparation of imitation granite fabric

[0020] Weigh 100 parts by weight of No. 42.5 cement, 210 parts by weight of quartz sand, 90 parts by weight of granite, parts by weight of pigments, and 25 parts by weight of water, and mix them together to form an imitation granite fabric.

Embodiment 3

[0021] Example 3 Preparation of Tiansha fabric

[0022] Weigh 100 parts by weight of No. 42.5 cement, 300 parts by weight of river sand, 4 parts by weight of pigments, and 25 parts by weight of water, and mix them together to form a Tiansha fabric.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a concrete pavior brick facing material with water permeability. The concrete pavior brick facing material contains 42.5# cement, pigments and water. Compared with the existing materials, the concrete pavior brick facing material with water permeability, disclosed by the invention, has the advantage that a brick prepared from the concrete pavior brick facing material with water permeability is high in compressive strength, good in bending resistance and standard in geometric dimensions, is antiskid, has a water-permeable function and does not have radioactivity.

Description

Technical field [0001] The field of municipal administration of the present invention particularly relates to a concrete pavement brick fabric with water permeability. Background technique [0002] The existing sidewalk pavement tiles are hand-made terrazzo tiles produced by hand using mold boxes, which have low strength, uneven thickness, large color difference, non-slip, impermeable, and water-grinding can cause water pollution. [0003] Ordinary permeable bricks have low strength and are easy to fade. Natural granite cut by infrared or semi-automatic equipment is strong, impermeable, but generally radioactive. [0004] The sintered bricks made by press molding and high-temperature roasting are impervious to water, and the demand for clay is relatively large, which can damage soil, mountains, forests and cultivated land. Summary of the invention [0005] One of the objectives of the present invention is to provide a water-permeable concrete pavement tile fabric. The bricks prepare...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/04E01C5/06C04B14/06
Inventor 张洪春李世清
Owner 内江市恒世达建材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com