Steel plate paint remover and preparation method thereof

A paint remover and steel plate technology, applied in the field of cleaning agents, can solve the problems of low removal efficiency, damage to the steel plate, leaving traces, etc., and achieve the effect of not corroding the substrate and high removal efficiency

Inactive Publication Date: 2015-02-18
WUXI EPIC TECH
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, the paint strippers currently on the market still have certain deficiencies. They will leave traces on the steel plate when the paint is stripped, and the stripping efficiency is low
For example, the Chinese invention patent (patent number 201210315222.3, application date 2012-08-30) discloses a paint remover, which has an excellent removal effect on acrylic paint, but it will damage the steel plate itself during the paint removal process ; Chinese invention patent (patent number 201110153160.6, application date 2011-06-09) discloses a paint remover, which can effectively and quickly remove the paint film on the surface of the workpiece, thereby effectively removing the paint film without damaging the workpiece. However, the scope of application of the paint remover is narrow, and it will still damage the steel plate if it stays on the surface of the steel plate for a long time

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] A steel plate paint remover, comprising the following raw materials in parts by mass: 55 parts of sodium gluconate, 12 parts of benzoic acid, 4 parts of diacetone alcohol, 4 parts of amyl acetate, 0.8 part of hydroxypropyl cellulose, castor oil 1 part, 0.7 part of dimethyl cellosolve, 1.5 parts of banana water, 0.6 part of sodium dodecylbenzenesulfonate, 0.6 part of dimethyl adipate, 1 part of polyethylene glycol.

[0018] A preparation method for steel plate paint stripper, comprising the steps of:

[0019] (1) Stir and mix sodium gluconate, hydroxypropyl cellulose and dimethyl cellosolve evenly, then add polyethylene glycol, benzoic acid, diacetone alcohol, amyl acetate, sodium dodecylbenzenesulfonate and dimethyl adipate, at a temperature of 20 ° C for 1 h;

[0020] (2) Then add castor oil, cool down to 80°C, then add banana water, stir and mix well to remember the finished product.

Embodiment 2

[0022] A steel plate paint remover, comprising the following raw materials in parts by mass: 75 parts of sodium gluconate, 22 parts of benzoic acid, 12 parts of diacetone alcohol, 12 parts of amyl acetate, 2.5 parts of hydroxypropyl cellulose, castor oil 3 parts, 2 parts of dimethyl cellosolve, 7 parts of banana water, 1.5 parts of sodium dodecylbenzenesulfonate, 1.5 parts of dimethyl adipate, 3 parts of polyethylene glycol.

[0023] A preparation method for steel plate paint stripper, comprising the steps of:

[0024] (1) Stir and mix sodium gluconate, hydroxypropyl cellulose and dimethyl cellosolve evenly, then add polyethylene glycol, benzoic acid, diacetone alcohol, amyl acetate, sodium dodecylbenzenesulfonate and dimethyl adipate, at a temperature of 40 ° C for 2 hours;

[0025] (2) Then add castor oil, cool down to 90°C, then add banana water, stir and mix evenly to remember the finished product.

Embodiment 3

[0027] A steel plate paint remover, comprising the following raw materials in parts by mass: 58 parts of sodium gluconate, 14 parts of benzoic acid, 5 parts of diacetone alcohol, 5 parts of amyl acetate, 1 part of hydroxypropyl cellulose, castor oil 1.3 parts, 0.9 parts of dimethyl cellosolve, 2 parts of banana water, 0.8 parts of sodium dodecylbenzenesulfonate, 0.8 parts of dimethyl adipate, 1.3 parts of polyethylene glycol.

[0028] A preparation method for steel plate paint stripper, comprising the steps of:

[0029] (1) Stir and mix sodium gluconate, hydroxypropyl cellulose and dimethyl cellosolve evenly, then add polyethylene glycol, benzoic acid, diacetone alcohol, amyl acetate, sodium dodecylbenzenesulfonate and dimethyl adipate, at a temperature of 20 ° C for 1 h;

[0030] (2) Then add castor oil, cool down to 80°C, then add banana water, stir and mix well to remember the finished product.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a steel plate paint remover and a preparation method thereof. The paint remover comprises the following raw materials in parts by mass: 55-75 parts of sodium gluconate, 12-22 parts of benzoic acid, 4-12 parts of diacetone alcohol, 4-12 parts of amyl acetate, 0.8-2.5 parts of hydroxypropyl cellulose, 1-3 parts of castor oil, 0.7-2 parts of dimethyl cellosolve, 1.5-7 parts of banana oil, 0.6-1.5 parts of sodium dodecylbenzenesulfonate, 0.6-1.5 parts of dimethyl adipate and 1-3 parts of polyethylene glycol. By the paint remover provided by the invention, various paints on the surface of the steel plate can be removed, no traces or residue is caused, the matrix cannot be corroded and the removal efficiency is high.

Description

technical field [0001] The invention relates to a cleaning agent, in particular to a steel plate paint remover and a preparation method thereof. Background technique [0002] The paint remover is a liquid composed of aromatic compounds and high-solvent solvents. It has a strong ability to dissolve paint films. The paint remover is fast and efficient. It can remove a wide range of coatings and is suitable for alcohol Acid, nitro, polyurea rubber type vinyl, epoxy, polyester, polyurethane and other paints. [0003] But, the paint stripper still exists certain deficiency in the market at present, can leave mark on steel plate when stripping, and stripping efficiency is low. For example, the Chinese invention patent (patent number 201210315222.3, application date 2012-08-30) discloses a paint remover, which has an excellent removal effect on acrylic paint, but it will damage the steel plate itself during the paint removal process ; Chinese invention patent (patent number 20111...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D9/04
CPCC09D9/04
Inventor 尤为
Owner WUXI EPIC TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap