6082 aluminium alloy spectral standard sample and 6082 aluminium alloy composition detection method
A spectral standard sample and standard sample technology, applied in the field of 6082 aluminum alloy spectral standard sample and 6082 aluminum alloy composition detection, to achieve the effect of improving production efficiency and product quality
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0075] Example 1
[0076] According to the composition percentage of Table 1, pure aluminum, Al-20wt% Si master alloy, Al-15wt% Fe master alloy, Al-40wt% Cu master alloy, Al-15wt% Mn master alloy, Al-4wt% Cr master alloy, The Al-20wt% Ni master alloy and the Al-20wt% Ti master alloy are added into the furnace and melted and blended at 760°C to obtain the first alloy melt. Add pure zinc to the first alloy melt according to the composition percentage in Table 1, and stir to obtain the second alloy melt. Add pure magnesium to the second alloy solution according to the composition ratio in Table 1, and stir to obtain an aluminum alloy melt. Under stirring conditions, hot-top casting is used to cast the aluminum alloy melt. The casting temperature is 735°C, the casting speed is 78mm / min, and the cooling water pressure is 0.06MPa. After casting, an aluminum with a diameter of 162mm is obtained. Alloy ingot bar.
[0077] Table 1 The mass percentage of the chemical composition of the 60...
Example Embodiment
[0092] Example 2
[0093] According to the composition percentage of Table 2, pure aluminum, Al-20wt% Si master alloy, Al-15wt% Fe master alloy, Al-40wt% Cu master alloy, Al-15wt% Mn master alloy, Al-4wt% Cr master alloy, The Al-20wt% Ni master alloy and the Al-20wt% Ti master alloy are added into the furnace and melted and blended at 760°C to obtain the first alloy melt. Add pure zinc to the first alloy melt according to the composition percentage in Table 2, and stir to obtain the second alloy melt. Add pure magnesium to the second alloy solution according to the composition ratio in Table 2, and stir to obtain an aluminum alloy melt. Under stirring conditions, hot-top casting was used to cast the aluminum alloy melt. The casting temperature was 745°C, the casting speed was 72mm / min, and the cooling water pressure was 0.08MPa. After the casting, aluminum with a diameter of 162mm was obtained. Alloy ingot bar.
[0094] Table 2 The mass percentage of the chemical composition of ...
Example Embodiment
[0111] Example 3
[0112] According to the composition percentages in Table 3, pure aluminum, Al-20wt% Si master alloy, Al-15wt% Fe master alloy, Al-40wt% Cu master alloy, Al-15wt% Mn master alloy, Al-4wt% Cr master alloy, The Al-20wt% Ni master alloy and the Al-20wt% Ti master alloy are added into the furnace and melted and blended at 760°C to obtain the first alloy melt. Add pure zinc to the first alloy melt according to the composition percentage in Table 3, and stir to obtain the second alloy melt. Add pure magnesium to the second alloy solution according to the composition ratio in Table 3 and stir to obtain an aluminum alloy melt. Under stirring conditions, hot-top casting was used to cast the aluminum alloy melt. The casting temperature was 740°C, the casting speed was 76mm / min, and the cooling water pressure was 0.07MPa. After casting, an aluminum with a diameter of 162mm was obtained. Alloy ingot bar.
[0113] Table 3 The mass percentage of the chemical composition of t...
PUM
Property | Measurement | Unit |
---|---|---|
Diameter | aaaaa | aaaaa |
Diameter | aaaaa | aaaaa |
Thickness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap