Processing method of polyester superfine denier plush composite fabric

A technology of composite fabrics and processing methods, applied in the processing of textile materials, chemical instruments and methods, and trimming of fabric surfaces, etc., can solve the problems of human skin irritation, ineffective effect, soft suede fabric and so on, so as to avoid itching Feel, good skin-friendly, excellent softness effect

Active Publication Date: 2015-04-01
SUZHOU YIBEI TEXTILE CO LTD
View PDF15 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The suede fabrics processed from this raw material are generally not soft, feel stiff, have poor fit, and are accompanied by a lack of itching that is irritating to human skin.
In order to eliminate such defects and make plush fabrics have good silk-like softness, good slippery effect, ideal warmth retention and excellent skin-fitting feeling, the industry usually focuses on the after-treatment process of fabrics. , but practice has shown that the effect is not obvious

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028]A) Select the raw material of the inner layer cloth and the raw material of the outer layer cloth, select 150D / 288F superfine DTY polyester filament of S+Z double twist direction and 100D / 48F DTY polyester filament as the raw material of the inner layer cloth, among which : 150D / 288F ultra-fine denier DTY polyester yarn accounts for 75% by mass in the inner layer cloth, and 100D / 48F DTY polyester yarn accounts for 25% by mass in the inner layer cloth, choose 100D / 144F ultra-fine denier polyester yarn and 50D / 24F FDY polyester yarn are used as raw materials for the outer layer cloth, among which: 100D / 144F ultra-fine denier polyester yarn accounts for 80% of the mass percentage in the outer layer cloth, while 50D / 24F The mass percent that the FDY polyester yarn in the outer layer cloth accounts for is 20%, and the inner layer cloth raw material and the outer layer cloth raw material are obtained;

[0029] B) Weaving, put the raw material of the inner layer cloth obtained...

Embodiment 2

[0040] A) Select the raw material of the inner layer cloth and the raw material of the outer layer cloth, select 150D / 288F superfine DTY polyester filament of S+Z double twist direction and 100D / 48F DTY polyester filament as the raw material of the inner layer cloth, among which : 150D / 288F ultra-fine denier DTY polyester yarn accounts for 85% by mass in the inner layer cloth, and 100D / 48F DTY polyester yarn accounts for 15% by mass in the inner layer cloth, choose 100D / 144F ultra-fine denier polyester yarn and 50D / 24F FDY polyester yarn are used as raw materials for the outer layer cloth, among which: 100D / 144F ultra-fine denier polyester yarn accounts for 70% of the mass percentage in the outer layer cloth, while 50D / 24F The mass percentage that the FDY polyester yarn accounts for in the outer layer cloth is 30%, obtain inner layer cloth raw material and outer layer cloth raw material;

[0041] B) Weaving, put the raw material of the inner layer cloth obtained in step A) in...

Embodiment 3

[0052] A) Select the raw material of the inner layer cloth and the raw material of the outer layer cloth, select 150D / 288F superfine DTY polyester filament of S+Z double twist direction and 100D / 48F DTY polyester filament as the raw material of the inner layer cloth, among which : 150D / 288F ultra-fine denier DTY polyester yarn accounts for 80% by mass in the inner layer cloth, and 100D / 48F DTY polyester yarn accounts for 20% by mass in the inner layer cloth, choose 100D / 144F ultra-fine denier polyester yarn and 50D / 24F FDY polyester yarn are used as raw materials for the outer layer cloth, among which: 100D / 144F ultra-fine denier polyester yarn accounts for 75% of the mass percentage in the outer layer cloth, while 50D / 24F The mass percent that the FDY polyester yarn in the outer layer cloth accounts for is 25%, and the inner layer cloth raw material and the outer layer cloth raw material are obtained;

[0053] B) Weaving, put the raw material of the inner layer cloth obtaine...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a processing method of a polyester superfine denier plush composite fabric and belongs to the technical field of fleece-faced fabric processing. The processing method comprises the following steps: selecting superfine denier DTY polyester yarns and DTY polyester yarns as the raw materials of inner-layer cloth, selecting superfine denier polyester yarns and FDY polyester yarns as the raw materials of outer-layer cloth, thereby obtaining the raw materials of the inner-layer cloth and the outer-layer cloth; weaving; carding the inner-layer grey cloth by use of a carding machine, next, guiding into a natural luster finishing machine for natural luster finishing to obtain the natural luster finished cloth, and then guiding the natural luster finished cloth into a pre-setting machine for pre-setting, thereby obtaining the pretreated inner-layer grey cloth; dyeing the inner-layer grey cloth; fleecing; pretreating the outer-layer grey cloth; dyeing the outer-layer grey cloth; raising; and ageing; combining the inner-layer grey cloth with the outer-layer grey cloth, thereby obtaining the polyester superfine denier plush composite fabric. The polyester superfine denier plush composite fabric is soft and smooth, and shows the texture exactly like silk; besides, the composite fabric has excellent skin affinity and an ideal wind-proof effect; the fabric is non-irritating to the skin of a human body and itchy feeling can be avoided; and furthermore, the fabric has excellent heat retention property.

Description

technical field [0001] The invention belongs to the technical field of suede fabric processing, and in particular relates to a processing method of polyester superfine denier plush composite fabric. Background technique [0002] The technical information of all suede fabrics can be seen in the published Chinese patent documents, such as CN1266307C (a kind of polyester superfine denier coral fleece blanket and its production method), CN101016675A (processing technology of full polyester superfine denier coral fleece blanket), CN101407972A (A polyester velvet blanket and its preparation method), CN101380179A (polyester super soft velvet blanket), CN101397719A (preparation method of polyester velvet blanket), CN101564256A (double-sided lambskin blanket and its processing method), CN101113547A (supersoft Raschel plush fabric and its manufacturing method), etc. In addition, the technical information of various polyester plush fabrics can also be seen in the published Chinese pat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B32B27/02B32B7/12A41D31/02D04B1/04D06B3/10D06C11/00D06C15/08D06C7/02
CPCA41D31/02B32B27/12B32B2262/0276B32B2307/304B32B2307/7242B32B2437/00D04B1/04D06B3/10D06C7/02D06C11/00D06C15/08D10B2331/04
Inventor 方靓
Owner SUZHOU YIBEI TEXTILE CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.