Surfactant-assisted in-situ co-precipitation method for preparing nano-powder with core-shell structure

A surfactant and in-situ co-precipitation technology, applied in the chemical industry, can solve the problems of low interface bonding strength, large extrinsic loss, and uneven distribution, and achieve the effects of low cost, uniform particle size, and simple preparation process

Inactive Publication Date: 2017-07-07
CHINA JILIANG UNIV
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there is a large extrinsic loss in the two-phase kneading and sintering composite ceramics, which greatly limits its wide application.
In order to overcome the shortcomings of coarse particles, low interfacial bonding strength, uneven distribution, and poor density of composite materials prepared by two-phase kneading and sintering, it is urgent to develop composite materials with good dispersion, uniform particle size, high crystallinity, and coating structure. phase powder preparation technology

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Surfactant-assisted in-situ co-precipitation method for preparing nano-powder with core-shell structure
  • Surfactant-assisted in-situ co-precipitation method for preparing nano-powder with core-shell structure
  • Surfactant-assisted in-situ co-precipitation method for preparing nano-powder with core-shell structure

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] 1) Dissolve a portion of 0.05mol of barium nitrate, 0.05mol of strontium nitrate and 0.1mol of magnesium nitrate in 200ml of deionized water, stir well to obtain a solution containing Ba, Sr and Mg;

[0026] 2) Dissolve 0.2mol oxalic acid in 200ml ethanol and stir evenly to obtain an oxalic acid-ethanol solution;

[0027] 3) Dissolve a portion of 0.1mol butyl titanate in the above oxalic acid-ethanol solution and stir evenly to obtain a titanium oxalate solution;

[0028] 4) Dissolve a portion of 0.0263mol (10ml) oleic acid in 50ml ethanol solution, and stir evenly at a temperature of 60°C to obtain a surfactant solution;

[0029] 5) Mix and stir the solution containing Ba, Sr, Mg obtained above, the solution containing Ti, and the surfactant solution, and then slowly add ammonia water to adjust its pH=2 to obtain oleic acid-modified Ba 0.5 Sr 0.5 TiO 3 @MgO precursor solution;

[0030] 6) Add the above Ba 0.5 Sr 0.5 TiO 3 The @MgO precursor solution was subjecte...

Embodiment 2

[0034] 1) Dissolve a portion of 0.05mol of barium nitrate, 0.05mol of strontium nitrate and 0.1mol of magnesium nitrate in 200ml of deionized water, stir well to obtain a solution containing Ba, Sr and Mg;

[0035] 2) Dissolve 0.2mol oxalic acid in 200ml ethanol and stir evenly to obtain an oxalic acid-ethanol solution;

[0036] 3) Dissolve a portion of 0.1mol butyl titanate in the above oxalic acid-ethanol solution and stir evenly to obtain a titanium oxalate solution;

[0037] 4) Dissolve a portion of 0.0367mol (10g) sodium dodecylsulfonate in 50ml of deionized water, and stir evenly at a temperature of 60°C to obtain a surfactant solution;

[0038] 5) Mix and stir the solution containing Ba, Sr, Mg obtained above, the solution containing Ti, and the surfactant solution, and then slowly add ammonia water to adjust its pH=2 to obtain oleic acid-modified Ba 0.5 Sr 0.5 TiO 3 @MgO precursor solution;

[0039] 6) Add the above Ba 0.5 Sr0.5 TiO 3 The @MgO precursor solution ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for preparing nano-powder with a core-shell structure assisted by in-situ co-precipitation with surfactants. The preparation process is as follows: Weigh the nitrates of barium, strontium and magnesium according to the precise stoichiometric ratio and dissolve them in water to prepare A solution, and press Accurate stoichiometric ratio Weigh butyl titanate and dissolve in ethanol-oxalic acid solution to prepare B solution, weigh a certain amount of surfactant and dissolve in hot water-alcohol to prepare C solution, slowly drop ammonia into A, B and The co-precipitation reaction was carried out in the mixed solution of C, and the pH of the reaction system was controlled to be 2. After the precipitate was filtered, washed, heat-treated and ground, Ba1-nSrnTiO3@MgO core-shell nanopowder with high crystallinity was obtained. The preparation process of the invention is simple, the cycle is short, and the cost is low, and the obtained nano-composite powder has good dispersibility, uniform particle size, high crystallinity and coating structure, which can achieve the purpose of practical application.

Description

technical field [0001] The invention belongs to the technical field of chemical industry, and in particular relates to a method for preparing nano-powder with core-shell structure by in-situ co-precipitation assisted by surfactant. Background technique [0002] barium strontium titanate ferroelectric material (Ba 1-n Sr n TiO 3 , BST) because its Curie temperature is adjustable with the ratio of Ba / Sr and has strong dielectric nonlinearity and low dielectric loss in the paraelectric state, so it is used in tuners, filters, phase shifters, etc. Microwave devices have broad application prospects and have become one of the research hotspots at home and abroad in recent years. However, the dielectric constant of BST ferroelectric materials in the microwave frequency range is relatively high, and it is difficult to meet the requirements for matching the internal impedance of the excitation source and high-power devices. The use of low dielectric constant microwave medium MgO ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B35/468C04B35/628
Inventor 张景基王疆瑛姬卢东高亚锋陈航宇李翰奇黄智源
Owner CHINA JILIANG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com