Water-absorbing side and waterproof water-locking microbubble mask non-woven fabric and manufacturing method

A technology of waterproof lock and non-woven fabrics, which is applied in the direction of textiles, papermaking, and non-woven fabrics. It can solve the problems that the mask material has no water-locking function and cannot prevent the volatilization of liquid skin care products, and achieves high softness and comfort. Moisture volatilization, The effect of preventing moisture volatilization and reducing fiber loss rate

Active Publication Date: 2017-08-01
HANGZHOU NBOND NONWOVENS
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The disadvantages of the above background technology are: the above-mentioned mask materials are all water-absorbing and breathable materials, and the mask materials have no water-locking function and cannot prevent the volatilization of liquid skin care products.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Water-absorbing side and waterproof water-locking microbubble mask non-woven fabric and manufacturing method
  • Water-absorbing side and waterproof water-locking microbubble mask non-woven fabric and manufacturing method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0012] Embodiment 1: with reference to attached figure 1 . A non-woven fabric for water-absorbing and water-repelling water-locking micro-bubble mask on one side, made of 5-15 mm cellulose fiber with a fineness of less than or equal to 0.9 decitex and spunlace composited with PP hydrophobic layer; the PP hydrophobic layer is PP spunbonded fabric , The weight per square meter is 5-15 grams. The surface layer of the cellulose fiber after the cellulose fiber is combined with the PP spunbonded cloth and dried has a wrinkled microbubble structure.

Embodiment 1-1

[0013] Embodiment 1-1: On the basis of embodiment 1, a kind of water-absorbing side water-repellent water-locking microbubble mask non-woven fabric, the fineness is less than 0.9 decitex or is equal to 5 millimeters of cellulose fibers of 0.9 decitex and 5 grams of PP It is made of spunbond fabric and spunlace composite.

Embodiment 1-2

[0014] Embodiment 1-2: On the basis of embodiment 1, a kind of water-absorbing side water-repellent water-locking microbubble facial mask non-woven fabric, the fineness is less than 0.9 decitex or is equal to 5 millimeters of cellulose fibers of 0.9 decitex and 10 grams of PP It is made of spunbond fabric and spunlace composite.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to a micro-bubble face mask non-woven fabric with one water absorbing side and one water-proof and water locking side, which is comfortable to skin, highly soft and fine and can effectively lock water and prevent a skin-friendly side from drying during use in a wet state, and a manufacturing method. The non-woven fabric is formed by compounding 5-15 millimeter cellulose fibers with fineness of being smaller than or equal to 0.9 dtex and a PP (Propene Polymer) hydrophobic layer spunlace. The non-woven fabric and the manufacturing method have the advantages that firstly the fine-denier short cellulose fibers and the PP spun-bonded nonwoven to spunlace, so the face mask material has the characteristic of softness and comfort to skin and the characteristic of preventing moisture from volatizing, secondly the fiber wastage rate is greatly reduced, and thirdly the using amount of a liquid skin care product by the face mask is reduced, the absorption rate of the skin to the liquid skin care product of the face mask is improved, and a precedent that liquid volatilization of the face mask is avoided is established.

Description

technical field [0001] The invention relates to a non-woven fabric for a water-absorbing, water-repelling and water-locking micro-bubble mask, which is softer, more delicate and close to the skin, and can effectively lock water and prevent drying of the skin-friendly surface when used in a wet state, and its manufacturing method , belonging to the field of non-woven fabric manufacturing. Background technique [0002] 1. Because the traditional spunlace mask material is combed into a net, the fibers used are thicker and longer, and the mask product is thicker, which has poor affinity to the skin and poor skin comfort. The spunlace mask material is used as a liquid skin care product during use. It is extremely volatile, and the skin’s poor absorption of liquid skin care products is the fatal flaw of traditional spunlace breathable masks. It not only affects the skin’s absorption of liquid skin care products, but also has to greatly increase the amount of liquid skin care produ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D04H1/4382D04H1/492D04H1/4374
Inventor 张国炎
Owner HANGZHOU NBOND NONWOVENS