High-brightness polishing paste and preparation method and application thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A polishing paste and brightness technology, applied in polishing compositions, chemical instruments and methods, polishing compositions containing abrasives, etc., can solve the problems of general surface brightness of metal materials, etc.
Inactive Publication Date: 2015-05-06
WUHU HANGTIAN SPECIAL CABLE FACTORY
View PDF1 Cites 4 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0004] In view of the above-mentioned prior art, the purpose of the present invention is to overcome the general problem of the surface brightness of polished metal materials in the prior art, thereby providing a high-brightness polishing paste capable of making the polished conductor have high gloss and a preparation method thereof
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
preparation example Construction
[0014] The present invention provides a kind of preparation method of high gloss polishing paste, wherein, described preparation method comprises:
[0015] (1) heating stearic acid, paraffin wax, palm wax, beeswax and ethanol in a water bath to obtain a mixture M1;
[0016] (2) Calcium carbonate and calcium oxide are added to the mixture M1 to obtain a high-gloss polishing paste; wherein,
[0017] With respect to 100 parts by weight of the stearic acid, the amount of paraffin wax is 5-50 parts by weight, the amount of palm wax is 5-50 parts by weight, and the amount of ethanol is 1-30 parts by weight, so The consumption of the calcium carbonate is 50-150 parts by weight, the consumption of the calcium oxide is 50-150 parts by weight, and the consumption of the beeswax is 1-30 parts by weight.
[0018] The above design mixes stearic acid, paraffin wax, carnauba wax, ethanol, calcium carbonate, calcium oxide and beeswax in a certain ratio, so that the polishing paste prepared b...
Embodiment 1
[0030] Put 100g of stearic acid, 10g of paraffin wax, 10g of palm wax, 5g of beeswax and 5g of ethanol in a water bath at a temperature of 60°C and heat for 1 hour to obtain a mixture M1; add 1g of graphite, 80g of calcium carbonate and 80g of calcium oxide to the mixture M1 , to obtain high gloss polishing paste A1.
Embodiment 2
[0032] Put 100g of stearic acid, 30g of paraffin wax, 30g of palm wax, 20g of beeswax and 20g of ethanol in a water bath at a temperature of 100°C and heat for 5 hours to obtain a mixture M1; add 10g of graphite, 120g of calcium carbonate and 120g of calcium oxide to the mixture M1 , to obtain high gloss polishing paste A2.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Property
Measurement
Unit
particle size (mesh)
aaaaa
aaaaa
Login to view more
Abstract
The invention discloses a high-brightness polishing paste and preparation method and application thereof. The preparation method comprises the following steps: heating stearic acid, paraffin wax, palm wax, bee wax and ethanol in a water bath to obtain a mixture M1; adding calcium carbonate and calcium oxide in the mixture M1 to obtain the high-brightness polishing paste; with respect to 100 parts of stearic acid by weight, the use amount of the paraffin wax is 5-50 parts, the use amount of the palm wax 5-50 parts by weight, the use amount of ethanol is 1-30 parts by weight, the use amount of calcium carbonate is 50-150 parts by weight, the use amount of calcium oxide is 50-150 parts by weight, and the use amount of bee wax is 1-30 parts by weight. After stearic acid, paraffin wax, palm wax, ethanol, calcium carbonate, calcium oxide and bee wax are mixed, the polishing paste prepared from above materials in proportion is capable of effectively promoting the surface gloss of the metal in actual use, and further the metal polishing effect can be effectively guaranteed.
Description
technical field [0001] The invention relates to the field of production and preparation of polishing paste, in particular to a high-brightness polishing paste and its preparation method and application. Background technique [0002] In the production process of cables, etc., because metal materials are involved, it is necessary to apply polishing in many cases, and polishing paste, as a more commonly used polishing material with better practical effects, is widely used in production, and The brightness after polishing also greatly determines the performance of the polishing paste. [0003] Therefore, it is an urgent problem to be solved in the present invention to provide a high-brightness polishing paste capable of making the polished conductor have high gloss and a preparation method thereof. Contents of the invention [0004] In view of the above-mentioned prior art, the purpose of the present invention is to overcome the general problem of the surface brightness of po...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more