Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

A kind of coal tar hydrogenation method

A technology for coal tar and hydrogenation upgrading, which is applied in hydrotreating process, petroleum industry, treatment of hydrocarbon oil, etc., can solve the problems of great influence of catalyst activity, high impurity content of coal tar, and reduced catalyst activity, etc. Product distribution and product properties, extended operating cycles, effects of improved properties

Active Publication Date: 2016-03-30
CHINA PETROLEUM & CHEM CORP +1
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This method is actually switching the fixed bed process to carry out hydrofining of coal tar raw materials. However, due to the high impurity content in coal tar, and the reaction is easy to coke under high temperature conditions, resulting in serious blockage of the catalyst bed, it is necessary to maintain long-term operation. The catalyst needs to be replaced frequently, the amount of catalyst is large, the cost is increased, and the process is complicated
In addition, the product from the switching reactor contains a considerable amount of water, which directly enters the hydrogenation reactor without treatment, which has a great impact on the activity of the catalyst (especially the catalyst containing molecular sieves), which will greatly reduce the activity of the catalyst

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of coal tar hydrogenation method
  • A kind of coal tar hydrogenation method
  • A kind of coal tar hydrogenation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0052] Catalyst preparation

[0053] 1. Preparation of a reverse hydrogenation catalyst I-1

[0054] Weigh 1000g of ferric oxyhydroxide filter cake prepared by wet air oxidation method, which contains 400g of ferric oxyhydroxide, add 80g of citric acid dissolved in 1L of water to it and stir to make it evenly mixed, the modification treatment time is 1h, and the treated slurry is use.

[0055] Preparation of sodium metaaluminate solution concentration is 50gAl 2 o 3 / L, a total of 1L, heated to 75°C for use, the concentration of aluminum sulfate solution is 20gAl 2 o 3 / L for a total of 2L, heated to 75°C for use.

[0056] Add 1.0L of distilled water into the gel tank and heat to 75°C. Weigh 500g (the specific surface area of ​​macroporous alumina is 220m 2 / g, pore volume 0.92mL / g, average pore diameter 17nm) and 100g Y-type molecular sieve (SiO 2 / Al 2 o 3 =11.5), add it into the gelling tank and stir evenly, and then add sodium metaaluminate solution and aluminum ...

Embodiment 2

[0078] Catalysts I-1, I-2, I-3 and II-1 were evaluated on the activity of continuous stirring autoclaves (CSTR) in series, each reactor was loaded with 100mL of catalyst, and medium and low temperature coal tar was selected as the raw material oil for evaluation , its properties are shown in Table 2, the process conditions are shown in Table 3, and the evaluation results are shown in Table 4, Table 5 and Table 6.

[0079] Table 2 Raw Oil Properties

[0080]

[0081] Table 3 Evaluation Process Conditions

[0082]

[0083] Table 3 continued

[0084]

[0085] Table 4 gasoline fraction properties (C 5 -180°C)

[0086]

[0087] Table 4 continued

[0088]

[0089] Table 5 Properties of diesel fractions (180-350°C)

[0090]

[0091] Table 5 continued

[0092]

[0093] Table 6 Hydrogenation Tail Oil Properties (>350℃)

[0094]

[0095] Table 6 continued

[0096]

[0097] From the above evaluation results, it can be seen that after coal tar is hydrotr...

Embodiment 3

[0099] Select catalyst I-1 / II-1 in series, at a reaction temperature of 370°C, a reaction pressure of 15MPa and a space velocity of 0.5h -1 Under the condition of normal operation for 1000h, the S in the hydrogenation tail oil was sampled and analyzed at different times, and the hydrogenation activity of the catalyst at different times was obtained. figure 2 .

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
diameteraaaaaaaaaa
specific surface areaaaaaaaaaaa
Login to View More

Abstract

The invention discloses a coal tar hydrogenation method. In the method, the raw material of coal tar is hydrogenated and upgraded firstly, and then water is separated and removed, and then hydrogenated and refined, and fractionated to obtain gasoline fraction, diesel fraction and hydrogenated tail oil. The composition of the hydrogenation modification catalyst used here includes ferric oxyhydroxide, organic polycarboxylic acid, macroporous alumina, molecular sieve and pseudo-boehmite. The hydrogenation upgrading catalyst adopted in the present invention uses cheap iron oxyhydroxide as the active metal component, which has low cost, and can realize moderate cracking of coal tar before refining, effectively remove impurities in coal tar, and adjust product distribution And product properties, and can extend the operating cycle of the device.

Description

technical field [0001] The invention relates to a coal tar hydrogenation catalyst and a preparation method thereof, which is particularly suitable for the fluidized bed hydrocracking process of coal tar. Background technique [0002] Coal tar is an important by-product of coal pyrolysis and carbonization process. It is a complex mixture of various substances. According to the temperature and process method of coal pyrolysis and carbonization, coal tar can be divided into low-temperature coal tar and high-temperature coal tar. [0003] Compared with petroleum heavy fractions, coal tar raw materials have the characteristics of high content of heteroatoms such as sulfur and nitrogen, high ash content, high content of polycyclic aromatic hydrocarbons, and high content of colloids and asphaltenes. Therefore, direct combustion will produce a large amount of sulfide and nitride, causing serious environmental pollution. Clean processing and effective utilization of coal tar become ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C10G65/02
CPCC10G65/02C10G2300/202C10G2300/70
Inventor 朱慧红孙素华刘杰金浩杨光彭绍忠蒋立敬
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com