Lumining rattan making method

A production method and rattan technology are applied in the field of light-emitting rattan production, which can solve the problems that the rattan does not have a luminous effect, is difficult to find, and dries out, and achieves the effect of facilitating nighttime lighting.

Inactive Publication Date: 2015-05-13
慈溪市光明灯具有限公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the influence of the climate after the rattan is used for a long time, it will become dry and weak, and it is easy to lose color
In order to solve these problems, there are existing plastic rattans processed by plastics. Plastic rattans are processed by molds and have the advantages of wear resistance, low temperature resistance, energy saving and environmental protection. However, the plastic rattans in the prior art Since the rattan does not have a luminous effect, it is not easy to be found at night without lighting, and it cannot embellish the space where it is located.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] A method for making luminous rattan, comprising the following steps:

[0016] a. Ingredients: Mix transparent PE material and fluorescent powder. The fluorescent powder accounts for 5%-60%, and the transparent PE material accounts for 40%-95%. The fluorescent powder can make the rattan glow. The transparent PE material referred to here The ratio to the phosphor is the physical ratio, and the transparent PE material needs to be granular.

[0017] b. Mold processing: mix PE material and fluorescent powder into the hopper of the extruder, extrude through the mold after melting, and carry out water-cooling through the water flow channel opened in the mold to form semi-finished luminescent rattan, PE After the PE material and phosphor powder are mixed and put into the hopper of the extruder, a little water can be added to accelerate the dissolution of PE material and phosphor powder.

[0018] c. Embossing: Emboss the semi-finished luminous rattan extruded from the mold. The...

Embodiment 2

[0022] The difference between this embodiment and the first embodiment is that in the step a, a color PE material is also added to mix with the masterbatch, the color PE material accounts for 70%-95%, and the masterbatch accounts for 5%-30%. , first mix the transparent PE material and phosphor powder through the main machine and then extrude, then mix the color PE material and masterbatch through the auxiliary machine and then extrude. When the extrusion strip of transparent PE material and phosphor powder is not completely cooled, the color The extruded strips of PE material and masterbatch are bonded into a whole strip, and extruded after cooling. The masterbatch is gray or white. The combination of masterbatch and colored PE material can enhance the luminous effect of rattan and change different colors. The extruded strips of transparent PE material and fluorescent powder are bonded with the extruded strips of colored PE material and masterbatch to form a whole finished prod...

Embodiment 3

[0024] The difference between this embodiment and Embodiment 1 is that a colored PE material is also added in the step a, wherein the fluorescent powder accounts for 5%-15%, and the transparent transparent PE material accounts for 85%-95%; At the same time, the transparent PE material and the fluorescent powder are first mixed and extruded through the host machine, and then the colored PE material is extruded through the auxiliary machine. The beading is pasted into a whole strip, and it is extruded after cooling. The ratio of the excess fluorescent powder in the transparent PE material is to save costs. Of course, the specific ratio can be determined according to the actual luminous effect required.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of rattan, and in particular relates to a lumining rattan making method which is as follows: a PE (poly ethylene) material and fluorescent powder are mixed, the mixture material is processed by a mold, cooled by water and molded into a semi manufactured lumining rattan, embossing processing is performed before the lumining rattan completely cooled, finally the cooled molded lumining rattan finished product is rolled up and bundled by a traction machine, the lumining rattan prepared by the method is mixed with the fluorescent powder, so that the lumining rattan has glowing effect, is easy to light at night, and plays the space decorative effect.

Description

technical field [0001] The invention relates to the technical field of rattan, in particular to a method for making luminous rattan. Background technique [0002] Rattan is a plant with tough texture, glossy appearance, smooth handle and excellent elasticity. It is often used to weave daily necessities such as rattan chairs and rattan boxes. However, due to the influence of the climate after long-term use, the rattan will become dry, weakened, and easy to lose color. In order to solve these problems, there are existing plastic rattans processed by plastics. Plastic rattans are processed by molds and have the advantages of wear resistance, low temperature resistance, energy saving and environmental protection. However, the plastic rattans in the prior art Since the rattan does not have a luminous effect, it is not easy to be found at night without lighting, and it cannot embellish the space where it is located. Contents of the invention [0003] The object of the present ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B29C69/00B29C47/00B29C47/04B29K23/00
Inventor 沈锡明
Owner 慈溪市光明灯具有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com