The production method of Nixing pottery imitation bronze ware

A production method and technology of bronze ware, which is applied in the field of imitation bronze ware of Nixing pottery, can solve the problems of lack of metal texture, failure to show the historical weight of bronze ware, and mere imitations, so as to achieve great collection value, rich metallic luster, Natural, simple and elegant color effect

Active Publication Date: 2017-03-15
王茁
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, traditional Nixing pottery imitation bronze ware lacks metallic texture and cannot reveal the unique historical sense of bronze ware, making the imitation products only have their shape but lack their spirit.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] 1) Prepare blank: the blank is made of the following raw materials in parts by weight: 40 parts of Dongni, 20 parts of Xini, 1 part of copper oxide, and 0.1 part of cerium oxide;

[0017] 2) Body forming: making the blank into various device-shaped green bodies;

[0018] 3) Blank trimming: trim the blank to meet the design requirements;

[0019] 4) Decorate the body: engrave classical patterns and / or engrave ancient characters on the body;

[0020] 5) Drying of the green body: drying the green body to discharge the water from the green body;

[0021] 6) Firing: The decorated green body is fired in a kiln; when firing, the temperature is gradually increased, first at a rate of 80°C per hour to 550°C, and then at a rate of 140°C per hour. The heating rate of ℃ raises the temperature to 1050 ℃, and at this temperature, the firing continues for 0.5 hours, and after cooling, it comes out of the kiln, and the imitation bronze ware of Nixing pottery is obtained.

Embodiment 2

[0023] 1) Prepare blank: the blank is made of the following raw materials in parts by weight: 60 parts of Dongni, 40 parts of Xini, 2 parts of copper oxide, and 0.5 part of cerium oxide;

[0024] 2) Body forming: making the blank into various device-shaped green bodies;

[0025] 3) Blank trimming: trim the blank to meet the design requirements;

[0026] 4) Decorate the body: engrave classical patterns and / or engrave ancient characters on the body;

[0027] 5) Drying of the green body: drying the green body to discharge the water from the green body;

[0028] 6) Firing: The decorated green body is fired in a kiln; when firing, the temperature is gradually raised, first at a rate of 130°C per hour to 650°C, and then at a rate of 180°C per hour. The heating rate of ℃ raises the temperature to 1080 ℃, and at this temperature, the firing continues for 1 hour, and after cooling, it comes out of the kiln, and the imitation bronze ware of Nixing pottery is obtained.

Embodiment 3

[0030] 1) Preparing a billet: the billet is made of the following raw materials in parts by weight: 50 parts of Dongni, 30 parts of Xini, 1.5 parts of copper oxide, and 0.3 part of cerium oxide;

[0031] 2) Body forming: making the blank into various device-shaped green bodies;

[0032] 3) Blank trimming: trim the blank to meet the design requirements;

[0033] 4) Decorate the body: engrave classical patterns and / or engrave ancient characters on the body;

[0034] 5) Drying of the green body: drying the green body to discharge the water from the green body;

[0035] 6) Firing: The decorated green body is fired in a kiln; when firing, the temperature is gradually increased, first at a rate of 100°C per hour to 600°C, and then at a rate of 160°C per hour. The heating rate of ℃ raises the temperature to 1060 ℃, and at this temperature, the firing continues for 0.8 hours, and after cooling, it comes out of the kiln, and the imitation bronze ware of Nixing pottery is obtained.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a method for manufacturing Nixing pottery imitated bronze wares. The method comprises the following steps: 1) blank preparation: uniformly mixing 40-60 parts of dong mud, 20-40 parts of xi mud, 1-2 parts of copper oxide and 0.1-0.5 part of cerium oxide; 2) forming a green body; 3) fettling; 4) decorating the green body; 5) drying the green body; and 6) firing: putting the decorated green body in a kiln to fire; and in the process of firing, gradually increasing the temperature, firstly, increasing the temperature to 550-650 DEG C at a temperature rise speed of 80-130 DEG C / hour, then increasing the temperature to 1050-1080 DEG C at a temperature rise speed of 140-180 DEG C / hour, and at the temperature, continuously firing the green body for 0.5-1 hour, then cooling the green body, and taking out the obtained product, so that a Nixing pottery imitated bronze ware is obtained. The Nixing pottery imitated bronze ware prepared according to the invention is natural and of primitive simplicity, and has a metal texture, so that the Nixing pottery imitated bronze ware can show an artistic effect of decorousness and classic elegance and a historical decorous feeling better, therefore, the Nixing pottery imitated bronze ware has a rich collection value.

Description

technical field [0001] The invention relates to a method for making pottery, in particular to a method for making Nixing pottery imitating bronze ware. Background technique [0002] The traditional preparation process of Nixing pottery in Qinzhou mainly includes the following steps: (1) Preparation of blank: the blank is made of pottery clay, and the soil from the east of the Qinjiang River across the urban area of ​​Qinzhou (commonly known as Dongni: soft clay with a color of Yellowish-white, containing a small amount of quartz sand) and the soil in the west of the Qinjiang River (commonly known as Xini: it is a purple mudstone with high iron content, the color is purple, and the surface layer is stained with a small amount of iron, which is hard clay. ), mix the two with a certain weight ratio, and make a blank through a series of processes such as grinding and dehydration; (2) green body molding: promptly fabricate various types of green bodies with the blank; (3) trim th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B33/13
Inventor 王茁王兆儒
Owner 王茁