A kind of easy processing silicon brass alloy and preparation method thereof

A silicon brass, easy-to-process technology, applied in the field of alloys, can solve the problems of cracking, poor processing performance, easy shrinkage of castings, etc., and achieves the effect of simple process, strong dezincification resistance, and not easy to produce shrinkage porosity.

Active Publication Date: 2017-10-13
JOMOO KITCHEN & BATHROOM
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The existing silicon brass alloy has high hardness, the castings are easy to shrink and crack, and the processing performance is poor, which limits its application

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of easy processing silicon brass alloy and preparation method thereof
  • A kind of easy processing silicon brass alloy and preparation method thereof
  • A kind of easy processing silicon brass alloy and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0016] An easy-to-process silicon brass alloy is composed of the following components: 60-63wt% copper (Cu), 0.50-0.90wt% silicon (Si), 0.50-0.80wt% aluminum (Al), 0.10-0.20wt% lead (Pb), other elements are less than 0.3%, the rest is zinc (Zn) and unavoidable impurities, of which (copper+silicon+aluminum+zinc)>99.60%, the other elements are tin (Sn), manganese (Mn) , a combination of iron (Fe) and nickel (Ni).

[0017] As a preferred embodiment, the alloy is composed of the following components: 61-62.5wt% copper (Cu), 0.60-0.80wt% silicon (Si), 0.60-0.80wt% aluminum (Al), 0.10- 0.15wt% lead (Pb), 0.20~0.25wt% other elements, the rest is zinc (Zn) and unavoidable impurities, wherein (copper+silicon+aluminum+zinc)>99.70%, said other elements are tin (Sn ), manganese (Mn), iron (Fe) and nickel (Ni) combination, specifically including 0.06-0.1wt% tin (Sn), 0.002-0.007wt% manganese (Mn), 0.07-0.09wt% iron (Fe) , 0.04 to 0.09% nickel (Ni).

[0018] The method of preparing easy-...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
melting pointaaaaaaaaaa
lengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses an easily processed silicon brass alloy. The alloy comprises the following components in percentage by weight: 60-63% of copper (Cu), 0.50-0.90% of silicon (Si), 0.50-0.80% of aluminum (Al), 0.10-0.20% of lead (Pb), less than 0.3% of other elements, and the balance of zinc (Zn) and inevitable impurities, wherein the sum of copper, silicon, aluminum and zinc is more than 99.60%, and other elements are a combination of tin (Sn), manganese (Mn), ferrum (Fe) and nickel (Ni). The invention further comprises a preparation method of the silicon brass alloy. The prepared silicon brass alloy is obviously higher than common lead brass in the performances of tensile strength, elongation rate, hardness and anti-zinc removal, the casting processability is good, practical production and application demands can be met, the precipitation of metals can meet the standard requirements, and the easily processed silicon brass alloy can be widely applied to water heating, valves and other various industries having limit on the precipitation of metal pollutants.

Description

technical field [0001] The invention relates to the field of alloys, in particular to an easy-to-process silicon brass alloy and a preparation method thereof. Background technique [0002] Lead brass is widely used in daily hardware and drinking water systems because of its good mechanical and physical properties, as well as good processing performance. However, the lead content in lead brass is high, which is easy to precipitate and pollute the environment. Especially when used in drinking water systems, it will cause serious harm to the human body, so all countries have put forward corresponding restrictions on the lead content of these products. The development of new brass alloys to reduce the content of lead while maintaining good processing performance has become an inevitable trend in the development of the industry. Among them, silicon brass replaces lead with silicon, and has attracted attention for its environmental protection and health. The existing silicon bras...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C9/04C22C1/02
CPCC22C1/02C22C9/04
Inventor 林孝发林孝山巴寿宁黄志钱陈国煌
Owner JOMOO KITCHEN & BATHROOM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com