Preparation method of composite fiber for wig

A technology of composite fibers and wigs, which is applied in the chemical characteristics of fibers, cellulose/protein conjugated rayon, and rayon manufacturing, etc., can solve the problems of secondary burns, unsatisfactory flame retardant performance, and high energy consumption. Achieve the effect of preventing shrinkage, improving mechanical strength, and improving strength and modulus
CN104674375AActive Publication Date: 2015-06-03DALIAN POLYTECHNIC UNIVERSITY
8 Cites 5 Cited by

Patent Information

Authority / Receiving Office
CN · China
Current Assignee / Owner
DALIAN POLYTECHNIC UNIVERSITY
Publication Date
2015-06-03

Smart Images

  • Figure 1
    Figure 1
  • Figure 2
    Figure 2
Patent Text Reader

Abstract

The invention relates to a preparation method of a composite fiber for a wig, and particularly relates to a preparation method of a composite fiber for a high-intensity seaweed / euphausiid protein simulation wig. The preparation method comprises the following step: adding a composite enhancer in the preparation process of a spinning solution, wherein the composite enhancer comprises the following components in percentage by weight: 70-90% of micromolecule dialdehyde and 10-30% of a hydrochloric acid and acetic acid mixture, wherein the volume ratio of hydrochloric acid to acetic acid in the mixture is (1 to 1) to (1 to 3). According to the method, natural environment-friendly degradable sodium alga acid and euphausia superb protein are compounded organically so as to prepare the simulation wig similar to real hairs in performance; the enhancer is added into the raw materials for improving the mechanical intensity of composite fibers; according to different thresholds of the added enhancer, the mechanical intensity can be improved by 1-7%.
Need to check novelty before this filing date? Find Prior Art

Description

technical field

[0001] The invention belongs to the technical field of composite fiber preparation, and relates to a method for preparing composite fibers for wigs, in particular to the organic compounding of two marine biomass materials, sodium alginate and Antarctic krill protein, and proposes to combine reinforcing agents with wet spinning technology Production and preparation of a high-strength seaweed / krill protein synthetic wig composite fiber. Background technique

[0002] Wigs are known as "fashion on the head". As a high value-added product, it has broad market development space at home and abroad. However, the current wig products on the market have performance defects, such as flame retardancy that cannot meet the requirements. , It is easy to cause secondary burns, and consumers prefer wigs with real hair simulation properties, such as skin-friendly, hot dyeing, curling, etc. Due to the disadvantages of high energy consumption and high pollution in the productio...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine