A kind of preparation method of composite foam building wall insulation material

A technology for building walls and thermal insulation materials, applied in ceramic products, applications, household appliances, etc., can solve the problems of affecting the foaming effect and foaming material performance, loss of thermal insulation ability, increase of bulk density, etc., and achieve significant sound insulation and production costs. Low, high porosity effect

Active Publication Date: 2017-03-01
刘方成
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But its biggest disadvantage is its strong water absorption, which can reach 2 to 3 times its own volume, thus completely losing its heat preservation ability.
Not only that, its porous structure and strong water absorption will absorb a large amount of wood liquefiable expandable resin when it is combined with wood liquefiable expandable resin to increase the bulk density, which not only increases the cost, but also seriously affects the foaming effect and foam properties

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] A method for manufacturing a composite foamed building wall insulation material is carried out in the following steps:

[0029] 1) Preparation of hydrophobic expanded perlite:

[0030] Select perlite ore with a particle size of 0.05-0.1mm, preheat it to make its combined water content (water content) reach 2-3%, and then roast it in a furnace at 1200-1230°C to make it expand to 20% of its original volume. After doubling, it becomes expanded perlite and is exported with a negative pressure output pipeline; and then sprays the expanded perlite in the negative pressure output pipeline with hydroxyl hydrogen-containing silicone oil (consumption is 0.5% of the expanded perlite weight), and the sprayed hydrophobic agent formed is sticky Attached to the surface of expanded perlite at a temperature of 600-630°C, a film is formed on the surface of expanded perlite in 2-5 seconds, and the output is cooled for use;

[0031] 2) Preparation of wood liquefaction expandable resin:

...

Embodiment 2

[0036] A method for manufacturing a composite foamed building wall insulation material is carried out in the following steps:

[0037] 1) Preparation of hydrophobic expanded perlite:

[0038] Select perlite ore with a particle size of 0.05-0.1mm, preheat it to make the combined water content reach 2-3%, and then roast it in a furnace at 1230-1260°C to make it expand to 25 times its original volume and become expanded The perlite is also exported with a negative pressure output pipeline; then sprayed to the expanded perlite in the negative pressure output pipeline with methyl hydrogen-containing silicone oil (consumption is 0.6% of the expanded perlite weight), and the mist hydrophobic agent formed adheres to the On the surface of expanded perlite at around 600-800°C, a film is formed on the surface of expanded perlite for 2-5 seconds, and the output is cooled for use;

[0039] 2) Preparation of wood liquefaction expandable resin:

[0040]Add wood flour with a moisture conten...

Embodiment 3

[0044] A method for manufacturing a composite foamed building wall insulation material is carried out in the following steps:

[0045] 1) Preparation of hydrophobic expanded perlite:

[0046] Select perlite ore with a particle size of 0.05-0.1mm, preheat it to make the combined water content reach 2-3%, and then roast it in a furnace at 1260-1300°C to make it expand to 30 times the original volume and become expanded Perlite is also exported with a negative pressure output pipeline; then spray to the expanded perlite in the negative pressure output pipeline with sodium hydroxysiliconate (consumption is 0.8% of the expanded perlite weight), and the mist hydrophobic agent formed adheres to the temperature still On the surface of expanded perlite at around 600-800°C, a film with a certain strength is formed on the surface of expanded perlite in 2-5 seconds, and the output is cooled for use; the test data of the expanded perlite is: the obtained bulk density is 70-150kg / m 3 , the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
water contentaaaaaaaaaa
densityaaaaaaaaaa
Login to View More

Abstract

The invention relates to a preparation method of a composite foamed building wall thermal-insulation material. The invention aims to provide a thermal-insulation material which has the advantages of excellent thermal-insulation property, favorable heat-insulating property (low heat conductivity coefficient) and favorable noise absorption and reduction properties. The method provided by the invention has the advantages of simple technical process and low manufacturing cost. The technical scheme is as follows: the manufacturing method comprises the following steps: 1) preparing hydrophobic expanded perlite; 2) preparing a wood liquefied expandable resin; and 3) preparing the composite foamed building wall thermal-insulation material.

Description

technical field [0001] The invention relates to a preparation method of a building wall thermal insulation material, in particular to a preparation method of a building wall thermal insulation material made by composite foaming of wood chip liquefaction product resin and expanded perlite. Background technique [0002] The development of building insulation materials is an important guarantee for the country to develop energy-saving buildings and promote green buildings in new rural areas. However, the development of wall insulation materials is not satisfactory. It has light weight and excellent thermal insulation performance, and there are too few biomass lightweight insulation products that can be directly used and assembled on the construction site. The construction site is wet and the construction efficiency is low. situation will continue to exist for a long time. [0003] On the other hand, with the rapid reduction of global timber resources and the strengthening of f...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L61/10C04B20/06C04B14/18C04B26/10C04B38/02
Inventor 刘方成
Owner 刘方成
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com