Co-free composite reinforced secondary hardening ultrahigh-strength steel and preparing method

An ultra-high-strength steel and secondary hardening technology, applied in the field of alloy steel, can solve the problems of poor economy, vulnerability to the impact of the international situation, and reduce Co content, etc., to achieve high economy, save Co element content, and high tempering The effect of stability

Active Publication Date: 2015-11-11
CENT IRON & STEEL RES INST
View PDF5 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0012] Although the AerMet series materials have excellent performance, due to the large amount of precious alloy elements such as cobalt and nickel, there are problems such as poor economy. Although M54 tries to solve the economic problems of the AerMet series materials, it relies on relatively high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Co-free composite reinforced secondary hardening ultrahigh-strength steel and preparing method
  • Co-free composite reinforced secondary hardening ultrahigh-strength steel and preparing method

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0040] According to the chemical composition range of the steel of the present invention, a 25 kg vacuum induction furnace is used to prepare a 21 kg alloy ingot 10 furnace. The specific chemical composition is shown in Table 3, and the furnace number is 1 # ~15 # .

[0041] After 15 furnaces are smelted and cast into steel ingots, the first high-temperature homogenization treatment system before forging is: After holding at 1200°C for 10 hours, the temperature is lowered for forging, and the forging heating temperature is 1150°C. The dimensions of forged test bars are: φ15×2000mm, 15×15×2000mm and 25×45×L.

[0042] After forging, the test bar is first subjected to normalizing and annealing heat treatment: normalizing treatment 1050℃×1h, air cooling, annealing treatment 680℃×6h, air cooling. Then send the sample section to process tensile, impact and fracture toughness sample blanks. The final heat treatment is quenching, cryogenic and tempering heat treatment: quenching at 900-10...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses Co-free composite reinforced secondary hardening ultrahigh-strength steel and a preparing method and belongs to the technical field of alloy steel. The Co-free composite reinforced secondary hardening ultrahigh-strength steel comprises, by weight, 0.20-0.50% of C, 1.0-5.0% of Cr, 10.0-30.0% of Ni, 0.50-3.0% of Al, 1.0-5.0% of Mo, 2.0% of W or less, 0.30% of V or less, 0.20% of Nb or less, and the balance Fe and unavoidable impurities. The vacuum induction technology, the vacuum arc remelting or vacuum induction technology and the electroslag remelting technology can be adopted in the alloy. Compared with the prior art, the Co-free composite reinforced secondary hardening ultrahigh-strength steel has the beneficial effects that the comprehensive performance is good, ultrahigh strength and good ductility and toughness are achieved, the heat treatment technology is superior in performance, high temper resistance and overaging resisting capability are achieved, the content of the strategic resource of the Co element is saved, and the economical efficiency is improved.

Description

technical field [0001] The invention belongs to the technical field of alloy steel, in particular to an economical Co-free compound strengthened secondary hardening ultra-high strength steel Air360 and its preparation method, which has good comprehensive performance, high tensile strength and good plastic toughness, and excellent heat treatment process performance , has high tempering stability and anti-aging ability, saves the strategic element Co, and is economical. Background technique [0002] With the development of the aviation and aerospace industry, especially after the durability / damage tolerance design criteria are adopted for aerospace components, higher requirements are put forward for materials, which require materials to have higher strength, toughness and reasonable yield / strength ratio. Especially for the development of new aircraft, there is an increasingly urgent demand for ultra-high-strength steels of 2000 MPa and above that can be used for durability dam...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C38/48C22C38/46C22C38/44C22C33/04C21D1/18C21D6/04
Inventor 王春旭厉勇赵博赵志国黄顺喆韩顺刘少尊邢峰刘宪民许广兴景绿露赵世春楼瑞祥李建新庞学东
Owner CENT IRON & STEEL RES INST
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap