Aluminum alloy, preparation method thereof, aluminum alloy moulded body, and aluminium alloy surface coloring method
A technology of aluminum alloy surface and aluminum alloy, applied in the field of aluminum alloy surface coloring and aluminum alloy forming body, to achieve the effect of good anodic oxidation characteristics, coloring characteristics, and high comprehensive mechanical properties
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0062] (1) Prepare aluminum alloy raw materials, wherein, based on the total amount of aluminum alloy raw materials, the content of Mn is 1%, the content of Mg is 1%, the content of La is 0.2%, and the balance is Al , where Mn is provided in the form of a master alloy of Mn and Al, La is provided in the form of a master alloy of La and Al, and the rest are provided in the form of pure metals.
[0063] Aluminum alloy raw materials were smelted and cast into ingots, and the obtained ingots were mold-cast on a 160T cold die-casting machine to obtain the aluminum alloy die-cast body of the present invention (referred to as A1). Among them, the melting temperature is 750°C, the injection speed is 2m / s, the mold temperature is 200°C, and the casting size is 200mm×30mm×3mm.
[0064] The surface hardness and tensile strength of the prepared aluminum alloys were measured, and the results are listed in Table 1.
[0065] (2) After degreasing and pickling the aluminum alloy die-casting b...
Embodiment 2
[0068] (1) The aluminum alloy die-casting body is prepared by the same method as in Example 1, wherein the composition of the aluminum alloy raw material is: based on the total amount of the aluminum alloy raw material, in terms of weight percentage, the content of Mn is 2.5%, the content of Mg The content is 1%, the content of La is 0.2%, and the balance is Al, so as to obtain an aluminum alloy die-casting body, and its surface hardness and tensile strength are listed in Table 1.
[0069] (2) The aluminum alloy molded body was prepared by the same method as in step (2) of Example 1.
[0070] The effects of anodizing and coloring are listed in Table 1.
Embodiment 3
[0072] (1) The aluminum alloy die-casting body is prepared by the same method as in Example 1, wherein the composition of the aluminum alloy raw material is: based on the total amount of the aluminum alloy raw material, in terms of weight percentage, the content of Mn is 4%, the content of Mg The content is 1%, the content of La is 0.2%, and the balance is Al, so as to obtain an aluminum alloy die-casting body, and its surface hardness and tensile strength are listed in Table 1.
[0073] (2) The aluminum alloy molded body was prepared by the same method as in step (2) of Example 1.
[0074] The effects of anodizing and coloring are listed in Table 1.
PUM
Property | Measurement | Unit |
---|---|---|
Thickness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap