Reducing slag in the early stage of converter tapping and mud for blocking the tapping hole and its use

A technology for tapping and mud, which is applied in the direction of manufacturing converters, etc., can solve problems such as easy falling, and achieve the effects of simple operation, improved slag blocking effect in the early stage, and strong applicability

Active Publication Date: 2017-03-22
SHIJIAZHUANG IRON & STEEL
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In order to solve the problem that the slag blocking cap and lightweight slag blocking plug can only be blocked outside the tapping hole, and at the same time, they are easy to fall during the process of tapping the furnace downwards, the present invention proposes a method to reduce the slag and sealing Mud for plugging the steel hole and its application method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Reducing slag in the early stage of converter tapping and mud for blocking the tapping hole and its use
  • Reducing slag in the early stage of converter tapping and mud for blocking the tapping hole and its use

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] A mud material for reducing slag in the early stage of converter tapping and blocking the tapping hole. The mass fraction of chemical components is as follows: CaO: 75 parts, C: 7 parts, SiO 2 : 10 parts, MgO: 7 parts, FeO: 0.5 parts, water: 0.5 parts.

[0015] How to use: After tapping, clean the remaining steel slag in the tapping hole, block the mud material inside the tapping hole, the mud material will be heated and bonded with the tapping hole to block the tapping hole, and at the same time It can reduce the erosion of the taphole by the high temperature flame and high temperature steel slag in the blowing process, and improve the service life of the taphole.

[0016] When the mud is tapped, it is necessary to use an iron pipe to open a small hole in the center of the mud in advance, so as to ensure that the mud will not fall off when the furnace is shaken at -70 degrees, and there will be no slag gushing out, and it can be guaranteed at -85 Due to the pressure o...

Embodiment 2

[0019] Reduce the slag in the early stage of converter tapping and the mud that blocks the tapping hole. The chemical composition mass fraction is as follows: CaO: 80 parts, C: 5 parts, SiO 2 : 7 parts, MgO: 7 parts, FeO: 0.5 parts, water: 0.5 parts.

[0020] How to use: After tapping, clean the remaining steel slag in the tapping hole, block the mud material inside the tapping hole, the mud material will be heated and bonded with the tapping hole to block the tapping hole, and at the same time It can reduce the erosion of the taphole by the high temperature flame and high temperature steel slag in the blowing process, and improve the service life of the taphole.

[0021] When the mud is tapped, it is necessary to use an iron pipe to open a small hole in the center of the mud in advance, so as to ensure that the mud will not fall off when the furnace is shaken at -70 degrees, and there will be no slag gushing out, and it can be guaranteed at -85 Due to the pressure of the mol...

Embodiment 3

[0024] Reduce the slag in the early stage of converter tapping and the mud that blocks the tapping hole. The chemical composition mass fraction is as follows: CaO: 85 parts, C: 3 parts, SiO 2 : 5 parts, MgO: 6 parts, FeO: 0.5 parts, water: 0.5 parts.

[0025] Using method: with embodiment 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a new type of mud material for reducing slag in the early stage of converter tapping and blocking the tapping hole. The mass fraction of chemical components is as follows: CaO: 75-85 parts, C: 3-7 parts, SiO2: 5-10 parts, MgO: 3-7 parts, FeO: 0.1-0.5 parts, water: 0.2-1.0 parts. How to use: After tapping, clean the remaining steel slag in the tapping hole, block the mud material inside the tapping hole, the mud material will be heated and bonded to the tapping hole to block the tapping hole, and at the same time It can reduce the erosion of the taphole by the high temperature flame and high temperature steel slag in the blowing process, and improve the service life of the taphole. The invention can completely prevent converter slag from entering the ladle in the early stage of tapping, improve the effect of slag blocking in the early stage, and has simple operation and strong applicability; the composition of the new mud material is better than that of refining slag, and falling into the steel ladle during tapping will not damage the molten steel create pollution.

Description

technical field [0001] The invention belongs to the technical field of iron and steel industry production, and in particular relates to reducing slag in the early stage of converter tapping, and mud material for blocking the tapping hole and its use method. Background technique [0002] As users have higher and higher requirements for steel quality, in the actual production on site, the converter is required to minimize the amount of slag during the tapping process, reduce the oxidation of molten steel and improve the refining effect. The research on slag blocking technology in the middle and later stages (slag blocking plug, sliding plate slag blocking, etc.) is relatively mature and practical, but for the early stage slag (that is, from the beginning of tapping the furnace to seeing the steel flow into the ladle), the blocking technology at this stage There are generally two ways of slag blocking caps and lightweight slag blocking plugs. The molten steel can only be seen ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C21C5/28
Inventor 杨锋功容晨光李建业刘勇胡云生王恭亮刘泳华祺年
Owner SHIJIAZHUANG IRON & STEEL