Glass bonding agent, standard hardness blocks and manufacturing method thereof

A technology of standard hardness block and manufacturing method, which is applied in the direction of manufacturing tools, abrasives, grinding devices, etc., can solve the problems of unstable composition, unstable bonding performance of bonding agent, large difference in hardness value of standard grinding wheel hardness blocks, etc., and achieve stability binding effect

Inactive Publication Date: 2015-12-23
ZHENGZHOU RES INST FOR ABRASIVES & GRINDING CO LTD
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The invention provides a vitreous bonding agent to solve the problem of unstable bonding performance of the existing ceramic bonding agents such as clay and feldspar due to unstable components
[0008] The second object of the present invention is to provide a standard hardness block using the above-mentioned vitreous bond to solve the technical problem of large differences in the hardness value of the standard grinding wheel hardness block in the prior art, so that it can be used to calibrate the sandblasting hardness machine throughout the Accuracy over measuring range

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Glass bonding agent, standard hardness blocks and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] 1. Vitreous binder

[0033] The vitreous bond in this embodiment is composed of the following components by mass: 87.5 parts of glass powder, 7.5 parts of borax, and 5 parts of zinc oxide. Put the above components into the mixer and mix well to form the glassy binder.

[0034] 2. Standard hardness block

[0035] The standard hardness block using the vitreous bond of this embodiment is composed of the following components in mass percentage: 40% vitreous bond and 60% abrasive. The abrasive is hollow spherical corundum with a particle size of F36.

[0036] 3. Manufacturing method of standard hardness block

[0037] The manufacturing method of the standard hardness block of this embodiment, the manufacturing process is as follows figure 1 As shown, it is manufactured by the following steps:

[0038] 1) When the vitreous binder is heated to 800°C, it will completely melt into a liquid;

[0039] 2) Add hollow spherical corundum to the above liquid, stir for 5 minutes u...

Embodiment 2

[0043] 1. Vitreous binder

[0044] The vitreous bond in this embodiment is composed of the following components by mass: 17 parts of glass powder, 1 part of borax, and 2 parts of zinc oxide. The preparation method is the same as in Example 1.

[0045] 2. Standard hardness block

[0046] The standard hardness block using the vitreous bond of this embodiment is composed of the following components in mass percentage: 20% vitreous bond and 80% abrasive. The abrasive is hollow spherical corundum with a particle size of F30.

[0047] 3. Manufacturing method of standard hardness block

[0048] The manufacturing method of the standard hardness block of this embodiment is manufactured by the following steps:

[0049] 1) When the vitreous binder is heated to 1000°C, it will completely melt into a liquid;

[0050] 2) Add hollow spherical corundum to the above liquid, stir for 10 minutes until completely dispersed and evenly, and obtain a mixed liquid;

[0051] 3) adding the mixed ...

Embodiment 3

[0054] 1. Vitreous binder

[0055] The vitreous bond in this embodiment is composed of the following components by mass: 88 parts of glass powder, 8 parts of borax, and 4 parts of zinc oxide. The preparation method is the same as in Example 1.

[0056] 2. Standard hardness block

[0057] The standard hardness block using the vitreous bond of this embodiment is composed of the following components in mass percentage: 25% vitreous bond and 75% abrasive. The abrasive is hollow spherical corundum with a particle size of F10.

[0058] 3. Manufacturing method of standard hardness block

[0059] The manufacturing method of the standard hardness block of this embodiment is manufactured by the following steps:

[0060] 1) When the vitreous binder is heated to 900°C, it will completely melt into a liquid;

[0061] 2) Add hollow spherical corundum to the above liquid, stir for 12 minutes until completely dispersed and uniform, and obtain a mixed liquid;

[0062] 3) adding the mixed s...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a glass bonding agent, standard hardness blocks and a manufacturing method thereof and relates to the technical field of detection and calibration of grinding wheels. The glass bonding agent comprises 10-40 parts of glass powder, 1-20 parts of borax and 1-3 parts of zinc oxide. According to the glass bonding agent, the stable bonding force can be provided; the change of the property of the bonding agent caused by unstable components of the conventional ceramic bonding agents such as clay and feldspar can be avoided; the standard hardness blocks are manufactured by using the glass bonding agent through a liquid stirring process; the standard hardness blocks are uniform in distribution of grinding materials; the same batch of hardness block products are small in hardness uniformity difference; and the accuracy of the whole detection range of a sand-blasting hardness machine can be accurately calibrated.

Description

technical field [0001] The invention belongs to the technical field of grinding wheel detection and calibration, and in particular relates to a vitreous bond, a standard hardness block and a manufacturing method thereof. Background technique [0002] Ordinary grinding wheels are composed of abrasives and bonds, and hardness is an important parameter when selecting and using grinding wheels. If the hardness of the grinding wheel is harder than the workpiece, it will lead to poor self-sharpening of the grinding wheel, lower grinding efficiency, lower grinding quality and even burn the workpiece; if the hardness of the grinding wheel is softer than the workpiece, the grinding wheel will be consumed Fast, affecting the machining accuracy. It is very important to choose a grinding wheel with the appropriate hardness according to the workpiece. [0003] The sandblasting hardness machine is a special equipment for testing the hardness of the grinding wheel. Its working principle ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B24D3/04B24D3/34B24D18/00C03C8/24
Inventor 吕申峰赵鹏高艳兵张克选包华
Owner ZHENGZHOU RES INST FOR ABRASIVES & GRINDING CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap