Antibacterial coating masterbatch, antibacterial coating woven bag and production method of antibacterial coating masterbatch

A woven bag and coating technology, which is applied in the field of antibacterial coating masterbatch and woven bags, can solve the problems of product storage and sales process not functioning, stored grains, grains are easy to deteriorate, and do not have antibacterial function, etc., to achieve superior barrier Functional, high antibacterial rate, excellent effect of precipitation resistance

Active Publication Date: 2015-12-30
山东寿光健元春化工有限公司
View PDF4 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In the process of realizing the present invention, the inventors found that the prior art has at least the following deficiencies: although plastic woven bags bring great convenience to people's lives, the currently produced plastic woven bags do not have an antibacterial function, especially those made with plastic

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Antibacterial coating masterbatch, antibacterial coating woven bag and production method of antibacterial coating masterbatch
  • Antibacterial coating masterbatch, antibacterial coating woven bag and production method of antibacterial coating masterbatch
  • Antibacterial coating masterbatch, antibacterial coating woven bag and production method of antibacterial coating masterbatch

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0040] Example 1, an antibacterial coating film masterbatch, including the following parts by weight of raw materials: coating grade polyethylene pellets

[0041] 56 parts; 33 parts of nano silver antibacterial agent; 3 parts of oxidized polyethylene wax; 5 parts of additives;

[0042] The additives are light stabilizers, antioxidants and coupling agents with a mass ratio of 1:3:2.

[0043] The preparation method of the antibacterial coating film master batch:

[0044] (1) Mix the above-mentioned various raw materials in a mixer at high speed for 5 minutes;

[0045] (2) The raw material mixture obtained in step 1 is introduced into the twin-screw granulator through vacuum suction;

[0046] (3) 210-270℃ melt extrusion, water cooling, air drying, cutting, screening and packaging to obtain the antibacterial coating masterbatch.

[0047] The above coating masterbatch is used to produce antibacterial coating woven bags, and the coating materials for antibacterial coating woven bags include

[0...

Example Embodiment

[0052] Example 2, an antibacterial coating film masterbatch, including the following parts by weight of raw materials: polypropylene powder produced by the company

[0053] 60 parts of material; 30 parts of nano silver antibacterial agent; 4 parts of oxidized polyethylene wax; 6 parts of additives;

[0054] The additives are light stabilizers, antioxidants and coupling agents with a mass ratio of 1:3:2.

[0055] The preparation method of the antibacterial coating film master batch:

[0056] (1) Mix the above-mentioned various raw materials in a mixer at high speed for 5 minutes;

[0057] (2) The raw material mixture obtained in step 1 is introduced into the twin-screw granulator through vacuum suction;

[0058] (3) 210-270℃ melt extrusion, water cooling, air drying, cutting, screening and packaging into finished products.

[0059] The above coating masterbatch is used to produce antibacterial coating woven bags, and the coating materials for antibacterial coating woven bags include

[0060...

Example Embodiment

[0064] Example 3, an antibacterial coating film masterbatch, comprising the following raw materials in parts by weight: 64 parts of film-grade polypropylene; 27 parts of nano-silver antibacterial agent; 5 parts of oxidized polyethylene wax; 7 parts of auxiliary agent;

[0065] The additives are light stabilizers, antioxidants and coupling agents with a mass ratio of 1:3:2.

[0066] The preparation method of the antibacterial coating film master batch:

[0067] (1) Mix the above-mentioned various raw materials in a mixer at high speed for 5 minutes;

[0068] (2) The raw material mixture obtained in step 1 is introduced into the twin-screw granulator through vacuum suction;

[0069] (3) 210-270℃ melt extrusion, water cooling, air drying, cutting, screening and packaging into finished products.

[0070] The above coating masterbatch is used to produce antibacterial coating woven bags, and the coating materials for antibacterial coating woven bags include

[0071] The following parts by weigh...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to antibacterial coating masterbatch which comprises 60+/-4 parts of coating-grade polyethylene aggregates, 30+/-3 parts of a nano antibacterial agent, 4+/-1 parts of oxidized polyethlene wax and 6+/1 parts of an auxiliary. The production method comprises the following steps: mixing the various raw materials in a material mixing machine at a high speed for 5 minutes; introducing a raw material mixture into a double-screw granulator through vacuum suction; performing melt extrusion, water cooling, air drying, cutting and screening under the temperature of 210 to 270 DEG C, thus obtaining a finished product. The antibacterial rate is up to 99.07-99.62 percent; after the antibacterial coating masterbatch is soaked by one month, the antibacterial rate to various germs is still kept at 94.93 to 98.45 percent; the oxygen penetration amount (cm<3>/m<2>.d.0.1MPa) reaches 825 to 1,090; the contact angle is larger than 150 degrees.

Description

technical field [0001] The invention relates to a woven bag, in particular to an antibacterial coating film masterbatch, an antibacterial coating film woven bag and a production method thereof, belonging to the technical field of packaging materials. Background technique [0002] Since the development of flat wire woven bags in my country in 1966, the products have developed rapidly, and a series of products with various designs and colors and complete specifications and sizes have been formed. At present, plastic woven bags have been widely used in sea, transportation, packaging industrial and agricultural products, and in agricultural product packaging. At present, plastic woven bags have been widely used in aquatic product packaging, poultry feed packaging, covering materials for farms, sunshade for crop planting, windproof, hailproof sheds and other materials. Common products: feed woven bags, chemical woven bags, putty powder woven bags, urea woven bags, etc. [0003] I...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D123/12C09D123/06C09D7/12D06M15/227D06M11/83
Inventor 张居正刘忠民
Owner 山东寿光健元春化工有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap