Inorganic capillary waterproofing agent
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A waterproofing agent, inorganic technology, applied in the field of inorganic penetrating waterproofing agent, can solve the problems of insufficient waterproof layer thickness and affecting the durability of concrete, and achieve the effect of improving durability, good durability, and increasing penetration depth
Inactive Publication Date: 2016-01-13
GUILIN HEXIN WATERPROOF DECORATION MATERIAL
View PDF6 Cites 1 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
Although it adopts the inorganic silicate primer method and the organic silicon topcoat method to make it have a certain degree of waterproof and maintenance functions, but because its main component is silicate with relatively high viscosity, during the infiltration process, silicon
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0026] This embodiment discloses an inorganic penetrating waterproofing agent, which is made of the following components in proportion by weight: 500 parts of sodium silicate, 5 parts of aluminum potassium sulfate, 4 parts of copper sulfate, 5 parts of zinc stearate, hard 5 parts of calcium fatty acid, 28 parts of diatomaceous earth, 5 parts of aluminum powder, 3 parts of polyaluminum ferric chloride, 3 parts of talcum powder, 3 parts of triisopropanolamine, 3 parts of sodium lignosulfonate, and 375 parts of water.
Embodiment 2
[0028] This embodiment discloses an inorganic penetrating waterproofing agent, which is made of the following components in proportion by weight: 450 parts of sodium silicate, 3 parts of aluminum potassium sulfate, 2 parts of copper sulfate, 2 parts of zinc stearate, hard 2 parts of calcium fatty acid, 30 parts of diatomaceous earth, 7 parts of aluminum powder, 4 parts of polyaluminum ferric chloride, 5 parts of talcum powder, 4 parts of triisopropanolamine, 1 part of sodium lignosulfonate, and 400 parts of water.
Embodiment 3
[0030] This embodiment discloses an inorganic penetrating waterproofing agent, which is made of the following components in proportion by weight: 550 parts of sodium silicate, 7 parts of aluminum potassium sulfate, 6 parts of copper sulfate, 8 parts of zinc stearate, hard 8 parts of calcium fatty acid, 25 parts of diatomaceous earth, 2 parts of aluminum powder, 2 parts of polyaluminum ferric chloride, 1 part of talcum powder, 2 parts of triisopropanolamine, 5 parts of sodium lignosulfonate, and 350 parts of water.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
PUM
Login to View More
Abstract
The invention discloses an inorganic capillary waterproofing agent. The waterproofing agent is prepared from, by weight, 450-550 parts of sodium silicate, 3-7 parts of potassium dichromate, 2-6 parts of copper sulfate, 2-8 parts of zinc stearate, 2-8 parts of calcium stearate, 25-30 parts of diatomite, 2-7 parts of aluminum powder, 2-4 parts of polyaluminum ferric chloride, 1-5 parts of talcum powder, 2-4 parts of triisopropanolamine, 1-5 parts of sodium lignosulfonate and 350-400 parts of water. The waterproofing agent disclosed in the invention has the advantages of large penetration depth and good durability, and can be used in waterproofing of roofs, basements and toilets.
Description
technical field [0001] The invention relates to an inorganic penetrating waterproofing agent, which belongs to the technical field of concrete building waterproofing materials. Background technique [0002] Concrete structure refers to the structure mainly made of concrete. It mainly includes plain concrete structure, reinforced concrete structure and prestressed concrete structure. Among them, the reinforced concrete structure has always been considered as the strongest and most durable concrete structure. Although steel bars and concrete are two materials with different physical and mechanical properties, there is a strong bond between them, which can make them work together effectively. In addition, concrete can also form a protective layer for steel bars, so that the steel bars are not corroded, thereby improving the performance of reinforced concrete. As a result, high expectations are placed on the use of reinforced concrete structures, while its durability issues a...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to View More 
Login to View More