A kind of micro-nano fiber yarn spinning device and its spinning process

A micro-nano fiber, yarn technology, applied in yarn, melt spinning, textile and papermaking, etc., can solve problems such as production reduction

Active Publication Date: 2017-07-07
奎屯雅达西纺织有限公司
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The finer the fiber, the better the quality of the melt blown cloth, but the output is relatively reduced

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of micro-nano fiber yarn spinning device and its spinning process
  • A kind of micro-nano fiber yarn spinning device and its spinning process
  • A kind of micro-nano fiber yarn spinning device and its spinning process

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0047] A single-hole melt-blown testing machine is used, the width of the air groove is 0.65mm; the angle of the air groove is 30°; the diameter of the spinneret hole is 0.42mm, and the spinneret process is: the temperature of the polymer melt is 260°C, and the temperature of the hot air is 280°C , the air pressure is 0.3MPa, the receiving distance is 10cm, the melt flow rate of the PP polymer used is 900g / 10min, and the diameter of the spinning fiber is between 0.6-1.1μm.

[0048] Spinning process parameters: polyester DTY 40D / 96f filament is used, the diameter of the upper and lower drums is 100mm, the rotational speed of the upper and lower drums is 3500mm / min, and the surfaces of the upper and lower drums are both "V" type groove structure, the width A of the groove top is 30mm, the angle B is 90°, the groove depth C is 10mm, the diameter of the microhole is 1mm, and the density of the hole is 25 / cm 2 , The negative pressure on the bottom surface of the lower drum groove is:...

Embodiment 2

[0050] A single-hole meltblown test machine is used, the air groove width is 0.65mm; the air groove angle is 30°; the spinneret hole diameter is 0.42mm. The spinning process is as follows: the polymer melt temperature is 240°C; the air pressure is 0.3 MPa; the receiving distance is 15cm, the hot air temperature is 280°C, the melt flow rate of the PP polymer used is 900g / 10min, and the average diameter of the spinning fiber is is 1.2 μm.

[0051] Spinning process parameters: the spandex yarn is 70D, the spandex yarn tension is 4.1 times, the diameter of the upper drum and the lower drum is 100mm, the rotation speed of the upper drum and the lower drum is 3000mm / min, the upper drum and the lower drum are The surface is a "V" groove structure, the width A of the groove top is 30mm, the angle B is 90°, the groove depth C is 10mm, the diameter of the micropore is 0.8mm, and the density of the hole is 36 / cm 2 , The negative pressure on the bottom surface of the lower drum groove is...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a micro-nano fiber yarn spinning device and its spinning process. The spinning device includes a spinneret, a yarn feeding system, a fiber polymerization mechanism and a twisting mechanism. The spinneret is composed of a hot air duct , a polymer melt pipeline and a cold air pipeline, the yarn feeding system is composed of bobbins, unwinding rollers and yarn guide rods, the fiber polymerization mechanism is composed of an upper roller and a lower roller that are meshed with each other, and the lower roller The groove bottom of the drum is provided with a number of micro-holes, and a special-shaped air duct is also provided inside the lower drum. The structure and process design of the present invention are reasonable, and the actual operation is convenient. The micro-nano fiber ejected from the melt-blown spinning head can be spun into a micro-nano fiber core-spun yarn, and the micro-nano fiber is coated on the surface of the core yarn, and the bonding rate is high and The work efficiency is high, so that the produced yarn has the functions of antibacterial, heat insulation, heat preservation, filtration and adsorption, and sound absorption.

Description

technical field [0001] The invention relates to a spinning device and a process thereof, in particular to a micro-nano fiber yarn spinning device and a spinning process thereof. Background technique [0002] Melt blown spinning technology is mainly used in the production of nonwovens. Flame-blown nonwoven technology originated in the early 1950s, when the U.S. Naval Laboratory, with government funding, researched and developed filter materials for collecting radioactive particles in the upper atmosphere after nuclear bomb explosions. Extruded into a concentrated hot air flow through the extruder, the ultra-fine fibers formed under the stretching effect of the air flow are blown to the condenser, thereby accumulating into an ultra-fine filter material. This process is the prototype of modern meltblown nonwoven technology. In the mid-1960s, the American Exxon company improved the method, and in the 1970s, it turned this technology into civilian use, and jointly established a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D01D5/08D02G3/36
Inventor 刘梅城洪杰
Owner 奎屯雅达西纺织有限公司