Method for measuring and representing microcosmic interface phases of asphalt concrete

A technology of asphalt concrete and interfacial phase, which is applied in the direction of testing material hardness and applying stable tension/pressure to test material strength, etc. It can solve the problems affecting the collection and calculation of load-displacement curves, test failures, and unreliable tests for the mechanical properties of interface phases Program and other issues

Inactive Publication Date: 2016-01-20
SOUTHEAST UNIV
View PDF3 Cites 20 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the nanoindentation test has extremely strict requirements on the production of samples, and it was rarely used in the field of asphalt in the past. Therefore, there is currently no feasible and standardized method for preparing test samples for asphalt concrete.
In addition, nanoindentation is theoretically only suitable for conventional hard materials, and asphalt concrete is a v

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for measuring and representing microcosmic interface phases of asphalt concrete
  • Method for measuring and representing microcosmic interface phases of asphalt concrete

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0033] The present invention will be further described below in conjunction with the accompanying drawings and specific embodiments.

[0034] A method for testing and characterizing asphalt concrete microscopic interfacial phases, comprising the following steps:

[0035] (1) Prepare the sample first

[0036] The nano-indentation test requires the surface of the sample to be flat and smooth, so as to reduce the variation of the data caused by the unevenness in the Z-axis direction, reduce the error, and ensure the reliability of the data. Therefore, the sample must be finely ground, but the asphalt concrete grinding process is easy It is peeled off and deformed, and it is not easy to fix. Therefore, in this test method, it is fixed in epoxy resin. The specific operation steps are as follows:

[0037] 1) Cut the asphalt concrete specimen into small pieces with a size of about 1.5 cm;

[0038] 2) if figure 1 As shown, mix epoxy resin AB glue 2 in proportion (volume ratio 2.5:1, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a method for measuring and representing microcosmic interface phases of asphalt concrete. According to the method, a small asphalt concrete piece is wrapped with epoxy resin AB glue and cured into a flat cylindrical test piece in a mold to prevent the small asphalt concrete piece from being stripped and deformed in the follow-up polishing process and improve the polishing flatness; the test piece is polished with metallographic abrasive paper, and then a final test piece meeting the requirements is obtained after ultrasonic cleaning is performed on the test piece when polishing is completed; the test piece enters a measuring step, all surface phases of the test piece are observed through amplification with a nanoindentation instrument, a measuring region containing all the phases is selected, equally-spaced dotting measuring is performed, and a load-displacement curve and a microscope image are recorded; after the test is finished, the Young modulus and hardness of all the points are computerized according to the load-displacement curve, and then the modulus and hardness indexes of all the phases are obtained by combining the phases where the measured points are located; finally, the size and the mechanical characteristics of a microcosmic interface transition area between asphalt and aggregates in the test piece can be analyzed and estimated according to the changing condition of the distance among the measured points and the mechanical indexes.

Description

technical field [0001] The invention belongs to the technical field of highway asphalt pavement, and specifically relates to a method for testing and characterizing the microscopic interface phase of asphalt concrete, which is used to characterize the multiphase behavior of asphalt mixture (aggregate phase, asphalt mortar phase, interface phase) from a microscopic perspective. Especially the mechanical properties of the interfacial phase, to help researchers connect with the macro from the micro to a deeper understanding of the macro performance of asphalt concrete, and to solve related controversies and practical engineering problems. Background technique [0002] 1. Microscopic properties of asphalt concrete [0003] Asphalt concrete is a composite material composed of asphalt, aggregate, mineral powder, etc. It has excellent road performance, so it is widely used in road paving. The road performance of asphalt concrete is mainly affected by its mechanical properties. How...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): G01N3/08G01N3/40
Inventor 杨军姚泽恒董夏鑫龚明辉
Owner SOUTHEAST UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap