A kind of concrete for C45 strength grade of steel-concrete composite structure

A combination structure and strength level technology, applied in the field of building materials, can solve the problems of poor natural bonding performance, material waste, uneconomical, etc., and achieve the effects of good compatibility, improved durability, and steel saving

Inactive Publication Date: 2018-02-27
XI'AN UNIVERSITY OF ARCHITECTURE AND TECHNOLOGY
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The above-mentioned strength grades of concrete can significantly improve the bonding performance between steel and high-strength or ultra-high-strength concrete, and improve the durability of the structure. High-strength high-performance or ultra-high-strength high-performance concrete will cause material waste and uneconomical problems
In addition, although there are some preparation technologies for high-performance low-strength concrete in the prior art, none of them involve or solve the problem of poor natural bonding between steel and low-strength high-performance concrete when used in SRC structures. question

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of concrete for C45 strength grade of steel-concrete composite structure
  • A kind of concrete for C45 strength grade of steel-concrete composite structure
  • A kind of concrete for C45 strength grade of steel-concrete composite structure

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0048] (1) Raw materials

[0049] 1. Cement

[0050] Select Qinling brand P·O 42.5R cement with stable quality and good performance, and conduct an adaptability test with polycarboxylate superplasticizer before use. The test method adopts the current building materials industry standard "Cement and Water Reducer". Agent Compatibility Test Method "JC / T 1083-2008 method, good compatibility with polycarboxylate superplasticizer. The performance indicators of the selected cement meet the requirements of the relevant current national standards, and its alkali content is low, its heat of hydration is low, and its water demand is also low.

[0051] 2. Aggregate

[0052] The fine aggregate adopts medium-to-coarse and Bahe sand with smooth particles, hard texture and good gradation. The quality of the sand conforms to the current building material industry standard "Sand and Stone Quality and Inspection Method Standard for Ordinary Concrete" JC / T 52-2006 and The high-quality sand st...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
specific surface areaaaaaaaaaaa
specific surface areaaaaaaaaaaa
Login to View More

Abstract

The invention discloses C45 strength level concrete for a steel section-concrete combined structure, which is prepared from cement, fine aggregate, coarse aggregate, water, an efficient water reducer, a defoaming agent, silica fume, fly ash, and a composite booster in a ratio of 310:698:1197:142:6:1:30:70:2.5 (kg / m<3>). A preparation method comprises the steps of: uniformly mixing polycarboxylic acidefficient water reducer and the composite booster with weighed water to obtain a mixture, adding 1 / 3 of the total amount of the fine aggregate and the coarse aggregate according to the weight ratio to a stirrer, stirring, adding 1 / 3 of the total amount of the coarse aggregate and the mixture, stirring, adding the cement,silica fume, and fly ash, stirring, adding the defoaming agent and the rest mixture, stirring, and discharging. According to the concrete, the adhesion property between the steel section and concrete is significantly improved in natural state, and the respective mechanical property and synergic working property of the steel and concrete materials are effectively exerted, so that the bearing capability and use performance of a structural element are greatly improved and the structure durability is improved.

Description

technical field [0001] The invention belongs to the technical field of building materials, and relates to a high-performance concrete with a strength grade of C45 for steel-concrete composite structures. Background technique [0002] The invention of Portland cement in 1824 led to the rapid development of concrete technology. Its consumption is large and its scope of application ranks the highest in the world. Although concrete is a traditional man-made building material, because of its irreplaceable advantages (abundant raw materials, simple production process, high cost performance, etc.) and the continuous progress of concrete material science and technology, concrete has become the main body of civil engineering materials. , It will also be one of the indispensable main materials in future civil engineering and national construction. At the same time, with the continuous expansion of the city, the continuous increase of the population, the continuous increase of the lan...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B28/04C04B24/24C04B18/14C04B18/08C04B22/14
CPCC04B28/04C04B2201/50C04B14/068C04B14/14C04B14/048C04B18/146C04B18/08C04B24/24C04B22/00C04B2103/50C04B22/143C04B22/08Y02W30/91
Inventor 郑山锁董方园杨威郑捷李磊曾磊王帆王斌关永莹
Owner XI'AN UNIVERSITY OF ARCHITECTURE AND TECHNOLOGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com