A preparation method of alumina composite material enriched with ruthenium ions in tailings wastewater

A composite material and alumina technology, applied in the field of preparation of alumina composite materials, can solve problems such as affecting the effect of adsorption

Active Publication Date: 2017-11-28
TAICANG BIQI NEW MATERIAL RES & DEV
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In addition, the surface chemical properties, polarity and charge of the adsorbent activated alumina also affect the adsorption effect.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] Harvest the corn stalks, wash them with tap water, and dry them.

[0016] Dissolve ammonium acetate, ammonia water, 1,3-propylenediamine, and ethylenediamine in deionized water, the concentration of ammonium acetate is 5g / L, the concentration of ammonia water is 4g / L, and the concentration of 1,3-propylenediamine is 4g / L , the concentration of ethylenediamine is 3g / L, and the ammoniated solution is obtained.

[0017] Put 10 g of washed corn stalks in 500 mL of ammoniated solution, place at 60° C. for 240 minutes, rinse and dry to obtain ammoniated corn stalks.

[0018] Dissolve acrylic acid and trimethylhexadecyl ammonium bromide in deionized water, the mass concentration of acrylic acid is 28%, and the mass concentration of trimethylhexadecyl ammonium bromide is 0.3%, to obtain acrylic acid / trimethyl hexadecyl ammonium bromide Cetyl ammonium bromide mixed aqueous solution.

[0019] Put 100g of alumina in 1500mL of acrylic acid / trimethylhexadecylammonium bromide mixed...

Embodiment 2

[0024] Harvest the corn stalks, wash them with tap water, and dry them.

[0025] Dissolve ammonium acetate, ammonia water, 1,3-propylenediamine, and ethylenediamine in deionized water, the concentration of ammonium acetate is 6g / L, the concentration of ammonia water is 6g / L, and the concentration of 1,3-propylenediamine is 3g / L , the concentration of ethylenediamine is 3g / L, and the ammoniated solution is obtained.

[0026] Put 50 g of washed corn stalks in 500 mL of ammoniated solution, place at 60° C. for 240 minutes, rinse and dry to obtain ammoniated corn stalks.

[0027] Dissolve acrylic acid and trimethylhexadecylammonium bromide in deionized water, the mass concentration of acrylic acid is 30%, and the mass concentration of trimethylhexadecylammonium bromide is 0.1%, to obtain acrylic acid / trimethylhexadecylammonium bromide Cetyl ammonium bromide mixed aqueous solution.

[0028] Put 100g of alumina in 2000mL of acrylic acid / trimethylhexadecylammonium bromide mixed aqu...

Embodiment 3

[0033] Harvest the corn stalks, wash them with tap water, and dry them.

[0034]Dissolve ammonium acetate, ammonia water, 1,3-propylenediamine, and ethylenediamine in deionized water, the concentration of ammonium acetate is 4g / L, the concentration of ammonia water is 5g / L, and the concentration of 1,3-propylenediamine is 5g / L , the concentration of ethylenediamine is 2g / L, and the ammoniated solution is obtained.

[0035] Put 100 g of washed corn stalks in 500 mL of ammoniated solution, place at 60° C. for 240 minutes, rinse and dry to obtain ammoniated corn stalks.

[0036] Dissolve acrylic acid and trimethylhexadecyl ammonium bromide in deionized water, the mass concentration of acrylic acid is 25%, and the mass concentration of trimethylhexadecyl ammonium bromide is 0.2%, to obtain acrylic acid / trimethyl hexadecyl ammonium bromide Cetyl ammonium bromide mixed aqueous solution.

[0037] Put 100g of alumina in 1000mL of acrylic acid / trimethylhexadecylammonium bromide mixed...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to the field of water-processing materials, and relates to a preparation method of an aluminium oxide composite material for enriching ruthenium ion in mine-tailing wastewater. The provided preparation method comprises filling holes of ammoniated corn straws with modified aluminum oxide. The concrete technology comprises cleaning corn straws, ammoniating, modifying aluminium oxide, and preparing the composite material. Compared with corn straws, the composite material substantially improves in ruthenium ion saturation enrichment amount, and also overflow pollution of corn straw organic carbon during water processing is avoided. The prepared composite material improves the ruthenium ion enrichment amount to 144.1 mg / g, is applicable to mine-tailing ruthenium-containing wastewater, and possesses extensive market prospect.

Description

technical field [0001] The invention belongs to the technical field of water treatment materials, and in particular relates to a method for preparing an alumina composite material enriched with ruthenium ions in tailings wastewater. Background technique [0002] my country is in the stage of accelerated industrialization and urbanization, with a large consumption of mineral resources and a high degree of dependence on foreign countries. However, the global mineral product prices continue to rise, increasing the production costs of mineral product demand enterprises, and at the same time increasing the pressure on resource security. Under the tense situation of global mineral resources supply, developed countries around the world have discovered that there are business opportunities for secondary utilization in the residues and tailings left after the processing and utilization of mineral resources. As my country is a big mining country, the development and utilization of a ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B01J20/24B01J20/30C02F1/28C02F1/62
Inventor 蓝碧健
Owner TAICANG BIQI NEW MATERIAL RES & DEV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap