UV coating construction process of edge band veneer elastic matte finishing paint

A veneer and elastic technology, which is applied to the UV coating construction process of veneer elastic matte finish for edge banding, can solve the problems of unenvironmental protection and difficult grinding, and achieves solutions that are not environmentally friendly, improve utilization, and have obvious effects. Effect

Inactive Publication Date: 2016-04-13
惠州市摩彩装饰材料有限公司
View PDF1 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In order to solve the problems that the traditional process is not environmentally friendly and difficult to polish, etc., a UV coating construction process of veneer elastic matte finish paint for edge banding strips in the present invention comprises the following steps

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A kind of veneer elastic matt topcoat UV coating construction process for edge banding, comprising the following steps

[0023] S1. Sand the rolled natural veneer or technological veneer substrate with a veneer-specific sander;

[0024] S2. Roller coating of elastic UV putty for wood veneer, the coating amount is 30g / ㎡, and then UV drying is carried out with a double mercury lamp, the drying intensity is 200mJ, and the drying time is 3 seconds;

[0025] S3. Roller coating of special elastic UV elastic primer for wood veneer, the coating amount is 40g / ㎡, and then UV drying is carried out with a double mercury lamp, the drying intensity is 200mJ, and the drying time is 3 seconds;

[0026] S4. Elastic UV sanding primer for wood veneer by roller coating, the coating amount is 30g / ㎡, and then UV drying is carried out with a double mercury lamp, the drying intensity is 250mJ, and the drying time is 3 seconds;

[0027] S5. Use a veneer sander for sanding and dust removal;

...

Embodiment 2

[0032] A kind of veneer elastic matt topcoat UV coating construction process for edge banding, comprising the following steps

[0033] S1. Sand the rolled natural veneer or technological veneer substrate with a veneer-specific sander;

[0034] S2. Elastic UV putty for roller coating wood veneer, the coating amount is 25g / ㎡, and then use double mercury lamp for ultraviolet drying, the drying intensity is 200mJ, and the drying time is 1 second;

[0035] S3. Roller coating of special elastic UV elastic primer for wood veneer, the coating amount is 30g / ㎡, and then UV drying is carried out with a double mercury lamp, the drying intensity is 200mJ, and the drying time is 1 second;

[0036] S4. Elastic UV sanding primer for roller coating wood veneer, the coating amount is 25g / ㎡, and then UV drying is carried out with a double mercury lamp, the drying intensity is 250mJ, and the drying time is 1 second;

[0037] S5. Use a veneer sander for sanding and dust removal;

[0038] S6. Ela...

Embodiment 3

[0042] A kind of veneer elastic matt topcoat UV coating construction process for edge banding, comprising the following steps

[0043] S1. Sand the rolled natural veneer or technological veneer substrate with a veneer-specific sander;

[0044] S2. Elastic UV putty for roller coating wood veneer, the coating amount is 27g / ㎡, and then UV drying is carried out with a double mercury lamp, the drying intensity is 200mJ, and the drying time is 2 seconds;

[0045] S3. Roller coating of special elastic UV elastic primer for wood veneer, the coating amount is 35g / ㎡, and then UV drying is carried out with a double mercury lamp, the drying intensity is 200mJ, and the drying time is 2 seconds;

[0046] S4. Elastic UV sanding primer for wood veneer by roller coating, the coating amount is 27g / ㎡, and then UV drying is carried out with a double mercury lamp, the drying intensity is 250mJ, and the drying time is 2 seconds;

[0047] S5. Use a veneer sander for sanding and dust removal;

[00...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a half-open UV coating construction process of edge band veneer elastic matte finishing paint. The half-open UV coating construction process comprises the following steps: (S1) a coiled natural veneer or technical veneer base material is sanded by a special veneer sanding machine; (S2) the roll coating is performed for special veneer elastic UV putty; the coating quantity is 30 g / m2; double mercury lamps are used for ultraviolet drying; the drying strength is 200 mJ; and the drying time is 3 seconds; (S3) the roll coating is performed for special veneer elastic UV elastic primer; the coating quantity is 70 g / m2; then, double mercury lamps are used for ultraviolet drying; the drying strength is 200 mJ; and the drying time is 3 seconds; (S4) the roll coating is performed for special veneer elastic UV sanding primer; the coating quantity is 30 g / m2; then, double mercury lamps are used for ultraviolet drying; the drying strength is 250 mJ; and the drying time is 3 seconds; and the like. The construction process needs no spraying, is free of paint mist, and can be suitable for batch production; and as the roll coating is performed for UV paint on the surface of the base material, subsequent coating treatment is not needed after a wood line is coated by a veneer painted by the elastic primer and finishing paint.

Description

technical field [0001] The invention relates to the field of coating construction, and more specifically relates to a UV coating construction process of veneer elastic matt finish paint for edge banding strips. Background technique [0002] At present, the main process of producing wood moldings in the market is to directly cover the wood moldings with veneer without any coating treatment, and then polish and spray at least two primers (polishing is required after each layer of primer). Finally, the topcoat is sprayed. In this way, harmful substances volatilize during the production process, seriously affecting the health of the body, and the production cycle is long, prone to bursting, orange peel and other problems, and it is extremely difficult to polish. Contents of the invention [0003] In order to solve the problems that the traditional process is not environmentally friendly and difficult to polish, etc., a UV coating construction process of veneer elastic matte f...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More