A kind of 15-needle nylon plus spandex yarn moon pattern nitrile foam glove and its preparation process

A preparation process, technology of spandex yarn, applied in gloves, clothing, protective clothing, etc., can solve the problems of slippage, low tear strength, poor wear resistance and anti-aging performance

Active Publication Date: 2017-10-27
SHANDONG XINGYU GLOVES
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, nitrile gloves are widely used in petrochemical, paint printing, agriculture and animal husbandry, automobile machinery maintenance and other industries. They are the most important labor protection tools for people's daily work to protect hands. They are light, sensitive, soft, oil-resistant, and acid-resistant. Alkali, anti-corrosion and other advantages, but the existing nitrile gloves have the disadvantages of slipping, low tear strength, poor wear resistance and anti-aging performance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of 15-needle nylon plus spandex yarn moon pattern nitrile foam glove and its preparation process

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] The preparation process of the 15-needle nylon plus spandex nitrile superfine foam gloves of the present invention, the steps include in turn:

[0033] Material preparation, foaming agent preparation, coagulant preparation, glue adjustment, impregnation, first drying, water washing, second drying.

[0034] The mass ratio of raw materials adopted in the described preparation is: nitrile latex: foaming agent: thickener: water-based PU resin: water-based epoxy resin=100:1:1:5:1.

[0035] The foaming agent is an aqueous solution of sodium dodecylbenzenesulfonate, wherein the mass ratio of sodium dodecylbenzenesulfonate to water is sodium dodecylbenzenesulfonate:water=1:20.

[0036] Described thickening agent is the aqueous solution of sodium carboxymethyl cellulose with a mass fraction of 2%.

[0037] The nitrile latex is imported Japanese nitrile latex, filled with a mass concentration of 45%; the water-based PU resin is imported German water-based PU resin, 100Kg / barrel,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a fifteen-stitch nylon and polyurethane filament moon-pattern butyronitrile foaming glove and a preparation process thereof. The preparation process of the fifteen-stitch nylon and polyurethane filament moon-pattern butyronitrile foaming glove, provided by the invention, sequentially comprises the following steps: preparing materials; preparing a foaming agent; preparing a coagulating agent; mixing glue; immersing; drying for the first time; washing with water; and drying for the second time. The prepared glove has the characteristics that an adhesive force, namely peeling strength is 40N; a uniform thickness: the thickness of a glue surface is 2mm; the tearing strength is more than or equal to 75N and reaches and exceeds grade four; an abrasion-resisting force is more than or equal to 8000rad and reaches the level of grade four; the anti-ageing performance reaches the requirements of grade-I products.

Description

technical field [0001] The invention relates to a glove and a preparation process thereof, in particular to a 15-needle nylon and spandex silk moon-pattern nitrile foam glove and a preparation process thereof. Background technique [0002] At present, nitrile gloves are widely used in petrochemical, paint printing, agriculture and animal husbandry, automobile machinery maintenance and other industries. They are the most important labor protection tools for people's daily work to protect hands. They are light, sensitive, soft, oil-resistant, and acid-resistant. Alkali, anti-corrosion and other advantages, but the existing nitrile gloves have the disadvantages of slipping, low tear strength, poor wear resistance and anti-aging performance. Contents of the invention [0003] The object of the present invention is to provide a 15-needle nylon plus spandex silk moon pattern nitrile foam glove, which is beautiful, soft and non-slip, high tear strength, excellent wear resistance ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): A41D19/015D06M15/693D06M15/564D06M15/55D06M15/09D06M13/265D06M101/34D06M101/30
CPCA41D19/015D06M13/265D06M15/09D06M15/55D06M15/564D06M15/693D06M2101/30D06M2101/34
Inventor 周星余
Owner SHANDONG XINGYU GLOVES