A kind of preparation method of nano layered composite hydroxide

A composite hydroxide, nano-layered technology, applied in chemical instruments and methods, nickel compounds, iron compounds, etc., can solve the problems of high energy consumption, high LDH preparation cost, long heating time, etc., and achieve easy industrial production, Abundant sources of raw materials and mild reaction conditions

Active Publication Date: 2017-04-05
BEIJING UNIV OF CHEM TECH
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Co-precipitation and nucleation / crystallization isolation methods both use NaOH as the alkali source, and about 0.8 tons of NaOH are needed to produce 1 ton of LDH. Applications in the field
The uniform precipitation method usually uses urea as a precipitating agent, and the urea is slowly decomposed by heating to release ammonia to precipitate metal cations to form LDH. However, this method takes a long time to heat, consumes high energy, and can only prepare micron-sized LDH, and it is difficult to synthesize nano-sized LDH.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of nano layered composite hydroxide
  • A kind of preparation method of nano layered composite hydroxide
  • A kind of preparation method of nano layered composite hydroxide

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] Step A: Weigh 5.88g of calcium oxide and add it into 110g of deionized water, grind it in a ball mill for 5 minutes, and prepare a calcium oxide slurry. Weigh 12.198g MgCl 2 . 6H 2 O and 7.2429g AlCl 3 . 6H 2 O was added to 100ml deionized water to prepare a salt solution.

[0027] Step B: Add the prepared salt solution dropwise to the calcium oxide slurry under magnetic stirring, and the dropwise addition is completed in 30 minutes, then heat the slurry to 60°C and continue to stir for 6 hours. After the reaction, filter and wash the slurry for 3 times A composite hydroxide filter cake is obtained.

[0028] C: Disperse the filter cake obtained in step B into 100ml of deionized water and grind it with a ball mill for 2 minutes to obtain a composite hydroxide slurry. Weigh 0.2g of disodium edetate into the slurry, stir evenly, and then weigh Take 1.9gNa 2 CO 3 Add it into the slurry, stir and react at 60°C for 1 hour, cool to room temperature after the reaction,...

Embodiment 2

[0030] Step A: Same as Example 1, the difference is to weigh calcium oxide and MgCl 2 . 6H 2 The masses of O are 7.56g and 18.297g, respectively.

[0031] Step B: Add the prepared salt solution dropwise to the calcium oxide slurry under magnetic stirring, and the dropwise addition is completed in 20 minutes, then heat the slurry to 80°C and continue stirring for 3 hours. After the reaction, filter and wash the slurry 4 times A composite hydroxide filter cake is obtained.

[0032] Step C: Disperse the filter cake obtained in Step B into 150ml of deionized water and grind it with a ball mill for 4 minutes to obtain a composite hydroxide slurry. Weigh 0.4g of disodium edetate into the slurry, stir evenly, and then Weigh 2.0gNa 2 CO 3 Add it into the slurry, stir and react at 60°C for 1 hour, cool to room temperature after the reaction, the precipitate is washed by centrifugation until the pH value is less than 8, and the sample is dried in an oven at 100°C for 10 hours to ob...

Embodiment 3

[0034] Step A: Weigh 5.88g of calcium oxide and add it into 100g of deionized water, grind it in a ball mill for 8 minutes, and prepare a calcium oxide slurry. Weigh 15.384gMg(NO 3 ) 2 . 6H 2 O and 11.253g Al(NO 3 ) 3 . 9H 2 O was added to 90ml deionized water to prepare a salt solution.

[0035] Step B: Add the prepared salt solution dropwise to the calcium oxide slurry under mechanical stirring, and the dropwise addition is completed in 40 minutes, then heat the slurry to 90°C and continue to stir for 2 hours. After the reaction, filter and wash the slurry 4 times A composite hydroxide filter cake is obtained.

[0036] C: Disperse the filter cake obtained in step B into 120ml of deionized water and grind it with a ball mill for 2 minutes to obtain a composite hydroxide slurry. Weigh 0.5g of disodium aminotriacetate and add it to the slurry. After stirring evenly, weigh 4.68g of NaH 2 PO 4 2H 2 O was added to the slurry, stirred and reacted at 70°C for 2 hours, coo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a low-cost preparation method of nano-layered composite hydroxide. The method adopts divalent and trivalent soluble metal nitrates or chlorides as raw materials for constructing LDH laminates, uses calcium oxide as an alkali source, and utilizes The chelating effect of the calcium ion chelating agent inhibits the formation of calcium precipitated impurities, and can prepare high-purity nano-layer composite hydroxide. The preparation method adopted in the present invention is simple, does not require high temperature and high pressure, does not require special equipment, has abundant sources of raw materials, and is low in cost. The nano layered composite hydroxide can be widely used in the fields of adsorption separation, catalysis, polymer materials and the like.

Description

[0001] Field [0002] The invention relates to the field of preparation of inorganic non-metallic functional materials, in particular to a preparation method of nano-layer composite hydroxide. Background technique [0003] Layered double hydroxides (LDH for short) is a kind of anionic layered clay, its chemical formula is [M 2+ 1-x m 3+ x (OH) 2 ] x+ (A n- x / n ) . mH 2 O, where M 2+ , M 3+ Represent divalent and trivalent metal cations respectively, x represents the change of metal element content, A n- Represents interlayer anions. LDHs have attracted extensive attention in recent years due to their unique two-dimensional layered structure and the exchangeability of interlayer anions. The unique properties of LDH make it widely used in the fields of catalysis, adsorption, ion exchange and polymer material additives (flame retardants, heat stabilizers and other functional additives). [0004] LDH is usually prepared by co-precipitation method, nucleation / crystall...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C01F7/00C01B25/26C01G53/00C01G49/00C07F19/00
CPCC01B25/26C01G49/009C01G53/006C07F13/005C07F15/045C01P2002/72C01P2002/82C01P2004/03C01P2004/64C01F7/78
Inventor 唐平贵李殿卿冯拥军陈廷伟
Owner BEIJING UNIV OF CHEM TECH