Water-dilutability epoxy woodware transparent primer and preparing method thereof

A technology of epoxy woodware and transparent primer, which is applied in the field of paint, can solve the problems of affecting the health of the body, the quality of the coating film, the impact on the environment, and the number of construction passes, so as to meet the needs of assembly line production and solve the problem of water sensitivity , The effect of broadening the scope of application

Inactive Publication Date: 2016-04-20
CHENGDU YOUPIN CHEM CO LTD
View PDF4 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Traditional solvent-based primers are toxic, harmful solvents such as benzene and free TDI, etc., causing harm to users and affecting people's health; with the enhancement of people's awareness of environmental protection, water-based wood paints are non-toxic, environmentally friendly, Odor, very little volatile matter, high safety of non-flammable and non-explosive, non-yellowing, large painting area and other advantages are more and more popular in the market
However, the water-based wood paint sold on the market, whether it is one-component or two-component, due to the low solid content, leads to many constructions and long drying time. , high-efficiency coating requirements, can not be industrialized production line, resulting in poor coating effect, poor fullness, poor compactness of the coating film, poor anti-adhesion, low hardness, does not meet the aesthetic requirements of the Chinese people for the coating effect, It cannot meet the coating requirements of high-decorated furniture, and is not conducive to the promotion of water-based wood lacquers

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] Prepare the main paint; weigh 100kg according to the following mass percentages: 62% epoxy resin, 0.3% defoamer, 0.3% dispersant, 0.4% leveling agent, 2% anti-settling agent, 11% filler, and 24% cosolvent ; Weigh the raw materials in proportion, first put the epoxy resin and some co-solvents into the container, stir and mix evenly, then add defoamer, dispersant, anti-sedimentation agent, leveling agent, filler, mix evenly, and disperse evenly to fine The viscosity is less than or equal to 60um, then add the remaining co-solvent to adjust to the required viscosity, filter and package to obtain the main paint components.

[0026] Prepare a curing agent; weigh 25 kg in total according to the following mass percentages: 80% polyamide and 20% modifier; stir and mix the weighed polyamide and modifier evenly, filter and pack to obtain the curing agent component.

[0027] Coating: Mix the above main paint and curing agent thoroughly, then add water, mix according to the mass ra...

Embodiment 2

[0029] Prepare the main paint; weigh 100kg according to the following mass percentages: 46% epoxy resin, 0.2% defoamer, 0.3% dispersant, 0.3% leveling agent, 2% anti-settling agent, 30% filler, and 21.2% cosolvent ; Weigh the raw materials in proportion, first put the epoxy resin and some co-solvents into the container, stir and mix evenly, then add defoamer, dispersant, anti-sedimentation agent, leveling agent, filler, mix evenly, and disperse evenly to fine If the viscosity is less than or equal to 60um, add the remaining co-solvent to adjust to the required viscosity, filter and package to obtain the main paint components.

[0030] Prepare a curing agent; weigh 25 kg in total according to the following mass percentages: 80% polyamide and 20% modifier; stir and mix the weighed polyamide and modifier evenly, filter and pack to obtain the curing agent component.

[0031] Coating: Mix the above main paint and curing agent thoroughly, then add water, and mix according to the mas...

Embodiment 3

[0033] Prepare the main paint; weigh 100kg according to the following mass percentages: 54% epoxy resin, 0.3% defoamer, 0.3% dispersant, 0.4% leveling agent, 2% anti-settling agent, 20% filler, and 23% cosolvent ; Weigh the raw materials in proportion, first put the epoxy resin and some co-solvents into the container, stir and mix evenly, then add defoamer, dispersant, anti-sedimentation agent, leveling agent, filler, mix evenly, and disperse evenly to fine If the viscosity is less than or equal to 60um, add the remaining co-solvent to adjust to the required viscosity, filter and package to obtain the main paint components.

[0034] Prepare a curing agent; weigh 25 kg in total according to the following mass percentages: 80% polyamide and 20% modifier; stir and mix the weighed polyamide and modifier evenly, filter and pack to obtain the curing agent component.

[0035] Coating: Mix the above main paint and curing agent thoroughly, then add water, and mix according to the mass ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
epoxy valueaaaaaaaaaa
amine valueaaaaaaaaaa
Login to view more

Abstract

The invention discloses a water-dilutability epoxy woodware transparent primer. The water-dilutability epoxy woodware transparent primer is prepared from main paint and a curing agent. The main paint is prepared from, by mass, 45-65% of epoxy resin, 0.2-0.5% of a defoaming agent, 0.1-0.3% of a dispersing agent, 0.2-0.4% of a flatting agent, 1-2% of an anti-settling agent, 10-30% of filler and 20-25% of a cosolvent. The curing agent is prepared form, by mass, 80% of polyamide and 20% of a modifier. The main paint and the curing agent in the transparent primer exist in a solvent state and can be cured in a humid environment, so that high crosslinking density is achieved, and a formed coating is relatively dense and high in hardness. An emulsifying agent is not adopted in the primer, so that the problem of water sensitivity of waterborne paint is thoroughly solved, the performance of the primer is obviously better than that of common waterborne woodware transparent primers, and the primer can be diluted into solvent paint with a low-toxicity organic solvent under the low-temperature and high-humidity conditions.

Description

technical field [0001] The invention relates to a paint, in particular to an epoxy primer. Background technique [0002] Traditional solvent-based primers are toxic, and harmful solvents such as benzene and free TDI will cause harm to users and affect people's health; with the enhancement of people's awareness of environmental protection, water-based wood paints are non-toxic, environmentally friendly, and non-toxic. Odor, very little volatile matter, high safety of non-flammable and non-explosive, non-yellowing, large painting area and other advantages are more and more popular in the market. However, the water-based wood paint sold on the market, whether it is one-component or two-component, due to the low solid content, leads to a large number of constructions, a long drying time, and the quality of the coating film is greatly affected by manpower and the environment. , high-efficiency coating requirements, can not be industrialized production line, resulting in poor coa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D163/00C09D7/12
CPCC09D163/00C08L2205/035C09D7/61C09D7/62C09D7/63C09D7/65C08L83/12C08L77/00C08K13/06C08K9/04C08K5/098C08K3/34C08K3/346C08K5/06C08K5/05
Inventor 陈文斌李相权
Owner CHENGDU YOUPIN CHEM CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products