A kind of phosphotungstic acid modified short-channel hpw-zr/sba-15 catalyst catalyzes the method for synthesizing bisphenol-F

A catalyst and short-channel technology, applied in the field of catalytic synthesis of bisphenol F, can solve the problems of unfavorable mass transfer and reaction, difficult separation and recovery, poor thermal stability, etc., and achieve improved mass transfer and reaction efficiency, high catalytic activity, and corrosion. small effect

Inactive Publication Date: 2018-04-03
XIANGTAN UNIV
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Since pure phosphotungstic acid (HPW) has problems such as low specific surface area, poor thermal stability, easy solubility in polar solvents to contaminate products, and difficulty in separation and recovery, immobilization of phosphotungstic acid can effectively increase its dispersion degree and improve catalytic efficiency, while the traditional SBA-15 molecular sieve has long pores, which is not conducive to mass transfer and reaction, so the modification makes its pores shorter to improve mass transfer and reaction efficiency

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of phosphotungstic acid modified short-channel hpw-zr/sba-15 catalyst catalyzes the method for synthesizing bisphenol-F
  • A kind of phosphotungstic acid modified short-channel hpw-zr/sba-15 catalyst catalyzes the method for synthesizing bisphenol-F
  • A kind of phosphotungstic acid modified short-channel hpw-zr/sba-15 catalyst catalyzes the method for synthesizing bisphenol-F

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] (1) Preparation of short-channel HPW-Zr / SBA-15 catalyst modified by phosphotungstic acid

[0028] Using phosphotungstic acid as the active component and zirconium oxychloride as the modifier, a short-channel HPW-Zr / SBA-15 catalyst was synthesized by one-step method: 2g polyethylene oxide-polypropylene oxide-polyethylene oxide three Add the block copolymer (P123) into a 250mL reactor, add 15g of deionized water and 60ml of 2mol / L dilute hydrochloric acid, control the reaction temperature at 40°C, stir evenly at 300rpm, slowly add 3.2g of zirconium oxychloride, stir and dissolve , then add 4.7g ethyl orthosilicate and 10mL aqueous solution dissolved with 0.7g phosphotungstic acid, keep stirring for 24h, then transfer the mixed solution into a polytetrafluoroethylene hydrothermal kettle to crystallize at 100°C for 24h, filter and wash , dried at 80°C for 8h, moved to a muffle furnace, and was calcined at 2°C / min to 550°C for 6h to prepare the short-channel HPW-Zr / SBA-15 ca...

Embodiment 2

[0037] The operation steps are the same as in Example 1, the difference is that the amount of formaldehyde is 3.24g, so that the molar ratio of phenol to formaldehyde is 25:1, the reaction time is 30min, and the yield of bisphenol F is 97.2%.

Embodiment 3

[0039] The operation steps are the same as in Example 1, the difference is that the reaction temperature is 70° C., the reaction time is 5 minutes, and the yield of bisphenol F is 41.66%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
pore sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a method for catalytically synthesizing bisphenol F by phosphotungstic acid modified short-channel HPW-Zr / SBA-15. The method uses phosphotungstic acid modified short-channel HPW-Zr / SBA-15 as a catalyst, and phenol and formaldehyde as raw materials to catalyze the synthesis of bisphenol F. The catalyst used is polyethylene oxide-polypropylene oxide-polyethylene oxide triblock copolymer (P123) as a template, tetraethyl orthosilicate as a silicon source, and phosphotungstic acid as a catalytic active component , zirconium oxychloride is used as a modifier, synthesized by one-step method, the preparation process is simple, the channel is short, it is beneficial to improve the mass transfer and reaction efficiency, the reaction activity is good, the reaction time is short, the catalytic efficiency is high, easy to separate, reusable, and the reaction There is no need to add any organic solvents during the process, which is green and environmentally friendly.

Description

technical field [0001] The invention relates to a method for catalytically synthesizing bisphenol F, belonging to the field of organic catalytic synthesis of fine chemicals. Background technique [0002] Bisphenol F is an important chemical intermediate, which is suitable for the preparation of low-viscosity epoxy resins. Compared with bisphenol A-based epoxy resins, it has the characteristics of low viscosity and excellent workability. Bisphenol F can also be used as a modification and stabilizer of phenolic resin. The modified phenolic resin produced by bisphenol F can significantly improve the processing and mechanical properties of phenolic resin, especially beneficial to the processing of epoxy resin for large wind turbine blades Forming reduces environmental pollution and improves the processing environment. [0003] Patents JP58177928US4400554 and CN200810072071 report methods for catalytically synthesizing bisphenol F with sulfuric acid, hydrochloric acid, and phosp...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C07C37/20C07C39/16B01J29/03B01J35/10
CPCY02P20/52
Inventor 刘跃进周健李勇飞谈瑛吴志民王艳聂真何晓建李蒙骆战涛
Owner XIANGTAN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap