High-CTI(Comparative Tracking Index), environment-friendly and flame-retardant reinforced PBT (Polybutylene Terephthalate) composite material and preparation method thereof

A composite material and environmental protection technology, applied in the field of composite materials, can solve the problems of non-environmental protection of flame retardants and low CTI, and achieve the effect of improving environmental protection performance, reducing addition amount and excellent mechanical properties.

Active Publication Date: 2016-06-01
江苏沃特新材料科技有限公司
View PDF6 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a high CTI environmentally friendly flame retardant reinforced PBT composite material with a high glow wire value, aiming to simultaneously solve the problems of the existing PBT materials that the flame retardant is not environmentally friendly and the CTI is low

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-CTI(Comparative Tracking Index), environment-friendly and flame-retardant reinforced PBT (Polybutylene Terephthalate) composite material and preparation method thereof
  • High-CTI(Comparative Tracking Index), environment-friendly and flame-retardant reinforced PBT (Polybutylene Terephthalate) composite material and preparation method thereof
  • High-CTI(Comparative Tracking Index), environment-friendly and flame-retardant reinforced PBT (Polybutylene Terephthalate) composite material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0033] Correspondingly, the embodiment of the present invention also provides a method for preparing a high CTI environmentally friendly flame-retardant reinforced PBT composite material, comprising the following steps:

[0034] S01. Weigh each component according to the formula of the above-mentioned high CTI environment-friendly flame-retardant reinforced PBT composite material;

[0035] S02. The above-mentioned components are mixed to obtain a mixed material;

[0036] S03. Using a twin-screw extruder to melt-extrude the mixed material, wherein the processing temperature of the twin-screw extruder is 220-250°C.

[0037] Specifically, in the above-mentioned step S01, the formulation components of the high-CTI environment-friendly flame-retardant reinforced PBT composite material and their preferred conditions are as described above, and will not be repeated here to save space.

[0038] In the above-mentioned step S02, the method of mixing the above-mentioned components is no...

Embodiment 1

[0043] A high CTI environment-friendly flame-retardant reinforced PBT composite material, based on the total weight of the high-CTI environment-friendly flame-retardant reinforced PBT composite material as 100%, including the components in weight percentage as shown in Example 1 of Table 1.

[0044] The preparation method of described high CTI environment-friendly fire-retardant reinforced PBT composite material, comprises the following steps:

[0045] S11. Weigh each component according to the formula of the above-mentioned high CTI environment-friendly flame-retardant reinforced PBT composite material;

[0046] S12. Mixing the above-mentioned components to obtain a mixed material;

[0047] S13. Using a twin-screw extruder to melt-extrude the mixed material, wherein the processing temperature of the twin-screw extruder is 220-250°C.

Embodiment 2

[0049] A high CTI environment-friendly flame-retardant reinforced PBT composite material, based on the total weight of the high-CTI environment-friendly flame-retardant reinforced PBT composite material as 100%, including the components in weight percentage as shown in Example 2 of Table 1.

[0050] The preparation method of the high CTI environment-friendly flame-retardant reinforced PBT composite material is the same as that of Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
impact strengthaaaaaaaaaa
Login to view more

Abstract

The invention is suitable for the field of composite materials, and provides a high-CTI (Comparative Tracking Index), environment-friendly and flame-retardant reinforced PBT (Polybutylene Terephthalate) composite material and a preparation method of the high-CTI, environment-friendly and flame-retardant reinforced PBT composite material. According to 100 percent total weight, the high-CTI, environment-friendly and flame-retardant reinforced PBT composite material is prepared from the following components in percentage by weight: 40 to 55 percent of PBT, 20 to 40 percent of fiberglass, 3 to 8 percent of bromine-containing flame retardant, 8 to 14 percent of phosphor-containing composite flame retardant, 0.1 to 2 percent of polysiloxane, 2 to 5 percent of toughening agent and 0.1 to 1 percent of anti-oxidant.

Description

technical field [0001] The invention belongs to the field of composite materials, and in particular relates to a high-CTI environment-friendly flame-retardant reinforced PBT composite material and a preparation method thereof. Background technique [0002] Polybutylene terephthalate (PBT) is a thermoplastic polyester with fast crystallization speed. It has the advantages of chemical corrosion resistance, excellent mechanical strength, and good processability. It is widely used in automobiles, electronic appliances, etc. industry. With the improvement of people's awareness of fire safety, the flame retardant modification of polymer materials used in automobile, electronic and electrical industries has become an inevitable demand. For a long time, flame retardant PBT modified engineering plastics usually use brominated flame retardants and antimony trioxide compounded. This system has high flame retardant efficiency and good flame retardant effect, but the relative tracking i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L67/02C08L83/04C08L63/00C08L25/06C08K13/04C08K7/14C08K5/5313C08K5/03
CPCC08L67/02C08L2201/02C08L2203/20C08L2205/03C08L83/04C08K13/04C08K7/14C08K5/5313C08K5/03C08L63/00C08L25/06
Inventor 林公澎刘则安李海涛张宝军李凤雪
Owner 江苏沃特新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap