Color change indicating device and transparent printing ink

A technology of color change indication and transparent ink, which is applied in the direction of ink, material analysis by observing the influence of chemical indicators, and analysis by making materials undergo chemical reactions, etc., can solve the problems of inconsistent pH values, deviations in the indication effect of indicating devices, Non-neutral and other issues to achieve the effect of avoiding deviation and interference

Active Publication Date: 2016-06-01
SHENZHEN NINE STARS PRINTING & PACKAGING GRP
View PDF4 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In order to avoid the influence of the protective layer on the discoloration of the indicating part, a material with a neutral pH value is usually selected as the material of the protective layer, such as hot-stamping anodized aluminum. However, the pH value of hot-stamped anodized aluminum is not neutral, and due to The indicator part where the volatile base is located is alkaline, and the pH values ​​of the two are inconsistent. Therefore, the protective layer will have a negative impact on the pH value of the indicator part, resulting in deviations in the indication effect of the color change indicator device, and even failure.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Color change indicating device and transparent printing ink

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0058] The structure of the color change indicating device of embodiment 1 is as follows figure 1 As shown, it includes a base layer 10 , an indicator layer 20 , a protective layer 30 , an isolation layer 40 , a release layer 50 , a first adhesive layer 60 , a barrier layer 70 , a second adhesive layer 80 and a release layer 90 .

[0059] Wherein, the material of the base layer 10 is PET, and the thickness is 0.1mm; the material of the indicating layer 20, the protective layer 30, and the isolation layer 40 is polyvinyl butyral, and the thickness is 0.1mm; the material of the release layer 50 is silicone oil, The thickness is 0.005 mm; the material of the first adhesive layer 60 is acrylic resin, and the thickness is 0.05 mm; the material of the barrier layer 70 is PVC, and the thickness is 0.15 mm; the material of the second adhesive layer 80 is acrylic resin, and the thickness is 0.1 mm. mm; the material of the peeling layer 90 is cellophane with a thickness of 0.15 mm.

[...

Embodiment 2

[0065] The structure of the color change indicating device of embodiment 2 is as follows figure 1 As shown, it includes a base layer 10 , an indicator layer 20 , a protective layer 30 , an isolation layer 40 , a release layer 50 , a first adhesive layer 60 , a barrier layer 70 , a second adhesive layer 80 and a release layer 90 .

[0066] Among them, the material of the base layer 10 is PVC with a thickness of 0.15 mm; the material of the indicating layer 20, the protective layer 30 and the isolation layer 40 is hydroxyethyl cellulose with a thickness of 0.08 mm; the material of the release layer 50 is polyvinyl alcohol , with a thickness of 0.05mm; the material of the first adhesive layer 60 is polyurethane, with a thickness of 0.1mm; the material of the barrier layer 70 is PET, with a thickness of 0.1mm; the material of the second adhesive layer 80 is polyurethane, with a thickness of 0.08mm ; The material of the release layer 90 is release paper with a thickness of 0.10 mm....

Embodiment 3

[0072] The structure of the color change indicating device of embodiment 3 is as follows figure 1As shown, it includes a base layer 10 , an indicator layer 20 , a protective layer 30 , an isolation layer 40 , a release layer 50 , a first adhesive layer 60 , a barrier layer 70 , a second adhesive layer 80 and a release layer 90 .

[0073] Wherein, the material of the base layer 10 is PET, and the thickness is 0.2mm; the material of the indicating layer 20, the protective layer 30, and the isolation layer 40 is hydroxypropyl cellulose, and the thickness is 0.05mm; the material of the release layer 50 is emulsified paraffin, The thickness is 0.05mm; the material of the first adhesive layer 60 is acrylic resin, and the thickness is 0.05mm; the material of the barrier layer 70 is PET, and the thickness is 0.07mm; the material of the second adhesive layer 80 is polyurethane, and the thickness is 0.03mm ; The material of the release layer 90 is paper coated with silicone oil, with a ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention relates to a color change indicating device and transparent printing ink.The color change indicating device comprises a substrate layer and an indicating layer formed on the surface of the substrate layer, the indicating layer comprises an indicating portion, and the indicating portion is printed by indicating printing ink; the color change indicating device further comprises a protection layer covering the surface of the indicating portion, the protection layer is printed with the transparent printing ink, and the transparent printing ink comprises volatile alkali, binder and solvent; indicating printing ink comprises volatile alkali, binder, solvent and pH indicator; the volatile alkali is selected from one or more of ammonium hydroxide, ammonium hydroxide, propylamine, n-butylamine, normal hexyl amine and n-octylamine; the binder is selected from one or more of polyvinyl butyral, nitrocotton, polyving akohol, hydroxyethyl cellulose and hydroxy propyl cellulose; the pH value of the transparent printing ink is the same as that of the indicating printing ink, and the concentration of volatile alkali in the transparent printing ink is the same as that of volatile alkali in the indicating printing ink.The color change indicating device can effectively avoid deviation of the pH value of the indicating portion.

Description

technical field [0001] The invention relates to a color change indicating device and transparent ink. Background technique [0002] General products have a service life or shelf life, especially food, beverages and medicines that are prone to spoilage during storage. In order to reduce the oxygen in the packaging and avoid deterioration in an oxygen environment, vacuum packaging or air conditioning are usually used. Packaging, and print the date of manufacture and shelf life on the outer packaging for people to judge whether it is expired. However, if the product package is opened or used, how to effectively record the time of opening or use is particularly important. [0003] The existing color change indicating device comprises a base layer, an indicating layer and a protective layer formed on the surface of the base layer, the indicating layer includes an indicating part and a reference part, and the protective layer covers the surface of the indicating part to protect t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D11/03C09D11/106C09D11/14G01N21/80
CPCC09D11/03C09D11/106C09D11/14G01N21/80
Inventor 刘永生郭欣刘文恒曾海明覃玲
Owner SHENZHEN NINE STARS PRINTING & PACKAGING GRP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap