Bamboo charcoal plate and manufacturing method thereof

A production method and technology of bamboo charcoal, applied in the field of board materials, can solve the problems of secondary pollution, limited purification effect of harmful gas molecules, etc.

Inactive Publication Date: 2016-06-08
赵星安
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Based on the above existing technologies, the purification effect of carbon plates on harmful gas molecules is limited, and even secondary pollution occurs

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0056] The raw material that bamboo charcoal plate is made according to mass parts proportioning, namely 30 parts of adsorption matrix (bamboo fine fiber powder accounts for 5% of adsorption matrix quality) that charcoal powder and bamboo fine fiber powder (particle diameter is 10 orders) are mixed to form, 0.2 part Titanium dioxide, 3 parts of binding resin powder (composed of resin powder, binder) and 10 parts of recycled resin powder, 1 part of fixative, 1 part of lubricant, 0.1 part of expansion agent, 0.1 part of OA6 and 0.1 part of PE wax , 0.1 part of ZB-60, 0.1 part of ZB-175.

[0057] The prepared material was stirred at 30°C for 50min. Then use a high-speed mixer to mix the materials for 10-20 minutes at a rotating speed of 2500-4000 rpm to form a mixture.

[0058] The above-mentioned mixture is sent to the extrusion die, and extruded through the hot die head, and the thermoforming temperature of the die head is controlled between 120-180°C. Then it is cooled by ru...

Embodiment 2

[0061] The raw material that bamboo charcoal plate is made according to mass parts proportioning, namely 100 parts of adsorption matrix (bamboo fine fiber powder accounts for 95% of adsorption matrix quality) that is mixed by charcoal powder and bamboo fine fiber powder (particle diameter is 200 orders), 2.5 parts Titanium dioxide, 80 parts of bonding resin powder (composed of resin powder, binder) and 50 parts of recycled resin powder, 10 parts of fixative, 5 parts of lubricant, 0.5 parts of expansion agent, 3 parts of OA6 and 3 parts of PE wax , 1.5 parts of ZB-60, 1.5 parts of ZB-175.

[0062] The prepared material was stirred at 200°C for 1 min. Then use a high-speed mixer to mix the materials for 10-20 minutes at a rotating speed of 2500-4000 rpm to form a mixture.

[0063] The above-mentioned mixture is sent to the extrusion die, and extruded through the hot die head, and the thermoforming temperature of the die head is controlled between 120-180°C. Then it is cooled b...

Embodiment 3

[0066] The raw material that bamboo charcoal plate is made according to mass parts proportioning, namely 65 parts of adsorption matrix (bamboo fine fiber powder accounts for 50% of adsorption matrix quality) that is mixed by charcoal powder and bamboo fine fiber powder (particle diameter is 100 orders), 1 part Titanium dioxide, 3 parts of binding resin powder (composed of resin powder, binder) and 10 parts of recycled resin powder, 5.5 parts of fixative, 2.5 parts of lubricant, 0.3 parts of expansion agent, 1.5 parts of OA6 and 1.5 parts of PE wax , 0.8 parts of ZB-60, 0.8 parts of ZB-175.

[0067] The prepared material was stirred at 100°C for 25min. Then use a high-speed mixer to mix the materials for 10-20 minutes at a rotating speed of 2500-4000 rpm to form a mixture.

[0068] The above-mentioned mixture is sent to the extrusion die, and extruded through the hot die head, and the thermoforming temperature of the die head is controlled between 120-180°C. Then it is cooled...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention provides a bamboo charcoal plate and a manufacturing method thereof. The bamboo charcoal plate is prepared from the following raw materials in parts by weight: 0.2-2.5 parts of titanium dioxide, 30-100 parts of adsorptive substrate prepared by mixing powdered carbon with bamboo fine-fiber powder and 10-130 parts of a resin matrix. The raw materials of the bamboo charcoal plat include the bamboo fine-fiber powder. The bamboo charcoal not only has high formaldehyde adsorption capacity, but also has a certain degradation effect on formaldehyde, so that the harmful gas adsorption effect of the bamboo charcoal plate is improved; 50-100g bamboo charcoal is put in a space per cubic meter, so that the formaldehyde adsorption rate within 12 hours can be up to 33 percent; in addition, the bamboo charcoal can improve the nail-holding ability and the tenacity.

Description

technical field [0001] The invention relates to the technical field of plates, in particular to a bamboo charcoal plate and a manufacturing method thereof. Background technique [0002] With the rapid development of real estate, various building materials are widely used in interior decoration, causing indoor environmental pollution is becoming increasingly serious. Formaldehyde is one of the most widespread indoor air pollutants. In addition to causing irritant and chronic diseases, the harm of formaldehyde to the human body can also react with ionic chlorides in the air to generate carcinogens—dichloromethyl ether. Indoor furniture, floors, carpets, tobacco, deodorants, disinfectants, etc. can release formaldehyde. Among them, decorative panels are the main source of harmful substances such as formaldehyde and benzene. [0003] In response to harmful gases such as formaldehyde in the indoor environment, "carbon board" decoration materials have been introduced in the furn...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L97/02C08L101/00C08K13/02C08K3/04C08K3/22
CPCC08L97/02C08L101/00C08L2205/035C08L2205/16
Inventor 赵春雷
Owner 赵星安
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com